Water-based high-corrosion-resistance coating with excellent stamping performance and preparing method and application of water-based high-corrosion-resistance coating

A punching and corrosion-resistant technology, applied in the field of water-based high corrosion-resistant coatings and their preparation, can solve the problems of unreported salt spray properties of coatings, unfavorable industrial application of coatings, affecting coating forming and punching, etc. Avoid creating weak points, good punchability, and improve the effect of corrosion resistance

Active Publication Date: 2015-11-11
GUANGZHOU HUMAN CHEM
View PDF11 Cites 49 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The salt spray of this patented technology reaches 1500 hours, but it has the following disadvantages: it is realized by two components, and the service life is short; the inorganic filler is added in the formula, which affects the forming and punching of the coating; and the key raw material used is mussel sticky Attachin is a biological agent, which is not conducive to the industrial application of coatings, and the cost is also high
However, the addition of inorganic fillers in the formula, including zinc phosphochromate, titanium dioxide, fillers, etc., is detrimental to the punchability of the coating, and the salt spray performance of the coating has not been stated in detail

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based high-corrosion-resistance coating with excellent stamping performance and preparing method and application of water-based high-corrosion-resistance coating
  • Water-based high-corrosion-resistance coating with excellent stamping performance and preparing method and application of water-based high-corrosion-resistance coating
  • Water-based high-corrosion-resistance coating with excellent stamping performance and preparing method and application of water-based high-corrosion-resistance coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] 1. Preparation of water-based high corrosion-resistant coatings with excellent flushability

[0043] (1) Weigh the raw materials of the following components in proportion

[0044]

[0045] (2) Mix the above-mentioned raw materials and disperse them evenly to prepare a water-based super corrosion-resistant coating with a solid content of 20%. The viscosity of the coating is 22 ± 2s when coated with 4 cups.

[0046] 2. Coating the prepared water-based super corrosion-resistant coating on the aluminum foil to form a corrosion-resistant coating. First, the aluminum foil was degreased and dried, and then the above-mentioned coating was applied to the aluminum foil, and baked in an oven at 200°C for 60s to obtain a coating with a dry film thickness of 5 μm.

[0047] The corrosion-resistant coating prepared above has excellent alkali resistance, cooking resistance, and salt spray resistance after testing, and the salt spray resistance of the coating after stamping and bend...

Embodiment 2

[0049] 1. Preparation of water-based high corrosion-resistant coatings with excellent flushability

[0050] (1) Weigh the raw materials of the following components in proportion

[0051]

[0052] (2) Mix the above raw materials and disperse them evenly to prepare a water-based super corrosion-resistant coating with a solid content of 36.5%. The viscosity of the coating is 53 ± 5s when coated with 4 cups.

[0053] 2. Coating the prepared single-coated water-based super corrosion-resistant coating on the aluminum foil to form a corrosion-resistant coating. First, the aluminum foil was degreased and dried, and then the paint was applied to the aluminum foil, and baked in a 300°C oven for 25s to obtain a coating with a dry film thickness of 3 μm.

[0054] The corrosion-resistant coating prepared above has excellent alkali resistance, cooking resistance, and salt spray resistance after testing, and the salt spray resistance of the coating after stamping and bending is still con...

Embodiment 3

[0056] 1. Preparation of water-based high corrosion-resistant coatings with excellent flushability

[0057] (1) Weigh the raw materials of the following components in proportion

[0058]

[0059] (2) Mix the above raw materials and disperse them evenly to prepare a water-based super corrosion-resistant coating with a solid content of 40%. The viscosity of the coating measured by coating -4 cups is 110 ± 10s.

[0060] 2. Coating the prepared single-coated water-based super corrosion-resistant coating on the aluminum foil to form a corrosion-resistant coating. Firstly, the aluminum foil was degreased and dried, then the coating was applied to the aluminum foil, and baked in an oven at 300°C for 50s to obtain a coating with a dry film thickness of 5 μm.

[0061] The corrosion-resistant coating prepared above has excellent alkali resistance, cooking resistance, and salt spray resistance after testing, and the salt spray resistance of the coating after stamping and bending is s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of surface corrosion prevention and discloses a water-based high-corrosion-resistance coating with excellent stamping performance and a preparing method and application of the water-based high-corrosion-resistance coating. The coating comprises, by mass, 25-60 parts of water-based resin, 2-8 parts of water-based cross-linking agent, 0.1-0.5 part of catalyst, 4-10 parts of cosolvent, 0.1-1 part of flatting agent, 0.1-10 parts of lubricating agent, 2-10 parts of water-based toughening resin, 0.1-0.5 part of defoaming agent, 0.5-3 parts of thickening agent and the balance water, and the total mass parts of the components are 100 parts. According to the water-based high-corrosion-resistance coating, the water-base resin serves as film forming matter, so that good construction performance is achieved, curing is quick, super corrosion resistance can be obtained when the thickness of the coating is 2-5 micrometers, the performance of resisting neutral salt mist is longer than 2,000 hours, resistance to acid salt mist is longer than 500 h, the corrosion grade can reach 9.8 or higher, and the salt mist resisting performance of the coating is maintained unchanged after stamping or bending is carried out.

Description

technical field [0001] The invention belongs to the technical field of surface anticorrosion, and in particular relates to a water-based high corrosion-resistant coating with excellent flushability, a preparation method and application thereof. Background technique [0002] In the field of surface anticorrosion, especially the common technology in the field of metal surface anticorrosion, solvent-based systems are mostly used, and oily resin is used as the film-forming material. The high content of solvents brings a burden to the environment, or contains some harmful substances such as heavy metals, which is not environmentally friendly. It is good, and it is mostly designed as a two-component system, which has special requirements for the service life of the coating, and the service life of the coating is short; moreover, the method of adding inorganic fillers is often used to make up for coating defects and improve coating corrosion resistance. However, due to the high har...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D125/14C09D163/00C09D167/00C09D5/08C09D7/12B05D7/24B05D3/02
Inventor 陈兴耀黄艳轶李月峰金兴菊魏小飞
Owner GUANGZHOU HUMAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap