Polyamide-6 filament production technology

A production process and technology of nylon, which is applied in the field of nylon, can solve the problems of poor elasticity and poor comfort, and achieve the effect of improving performance, comfort and tightness

Inactive Publication Date: 2015-11-25
TAICANG HONGYI CHEM FIBER
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The common disadvantages of nylon filaments in the prior

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Prepare raw materials, by weight, take by weight 60 parts of nylon 6, 4 parts of modified antibacterial and anti-ultraviolet functional masterbatches, 8 parts of sulfite, 8 parts of polycaprolactone, 7 parts of sodium fluoride, Among them, the modified antibacterial and anti-ultraviolet functional masterbatch, in parts by weight, includes 40 parts of nylon 6 slices, 0.3 parts of polycaprolactone, and 3 parts of zirconium sodium silver phosphate. , slice the raw materials separately;

[0022] (2) Use a nitrogen flow to continuously dry the slices of nylon 6, and the drying temperature is 160°C;

[0023] (3) Put the dried polyamide 6 slices, modified antibacterial and anti-ultraviolet functional masterbatch, antioxidant, dispersant, and catalyst into the screw extruder to melt, and the melt is transported to the metering pump for metering after passing through the static mixer , after being extruded by the spinning machine, it is cooled to form filaments, and the fil...

Embodiment 2

[0026] (1) Prepare raw materials, by weight, take by weight 65 parts of nylon 6, 5 parts of modified antibacterial and anti-ultraviolet functional masterbatches, 6 parts of sulfite, 5 parts of polycaprolactone, 8 parts of sodium silicate, Among them, the modified antibacterial and anti-ultraviolet functional masterbatch, in parts by weight, includes 35 parts of nylon 6 slices, 0.4 parts of polycaprolactone, and 5 parts of sodium zirconium phosphate. , slice the raw materials separately;

[0027] (2) Use a nitrogen flow to continuously dry the slices of nylon 6, and the drying temperature is 170°C;

[0028] (3) Put the dried polyamide 6 slices, modified antibacterial and anti-ultraviolet functional masterbatch, antioxidant, dispersant, and catalyst into the screw extruder to melt, and the melt is transported to the metering pump for metering after passing through the static mixer , after being extruded by a spinning machine, it is cooled to form filaments, and the filaments ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyamide-6 filament production technology. The Polyamide-6 filament production technology comprises the steps of preparation and drying of raw materials, preparation of POY yarns, preparation of DTY yarns and preparation of polyamide-6 filaments. As a modified antibacterial uvioresistant functional master batch is added into the raw materials to improve the performance of the finished polyamide-6 filaments, the produced polyamide-6 filaments has the antibacterial and uvioresistant functions. As the POY-DTY production process is adopted, the fluffiness and favorable elasticity of the polyamide-6 filaments are maintained, the compactness of the filaments is improved and the comfort degree of the end product is effectively improved.

Description

technical field [0001] The invention relates to the technical field of nylon, in particular to a production process of nylon 6 filament. Background technique [0002] Nylon, scientific name polyamide fiber, commonly known as nylon (Nylon), English name Polyamide (referred to as PA), nylon is the trade name of polyamide fiber, density 1.15g / cm 3 , is the general term for thermoplastic resins containing repeating amide groups (-NHCO-) ​​in the main molecular chain. The main varieties are nylon 6 and nylon 66. Nylon yarn is a fiber made of polyamide, divided into nylon filament and nylon short yarn. Nylon filament can be made into elastic yarn, and short yarn can be blended with cotton and acrylic fiber to improve its strength and elasticity. The common disadvantages of the nylon filaments in the prior art are that they are relatively hard, have poor elasticity, and have a bad sense of comfort. Contents of the invention [0003] In view of the deficiencies in the prior art...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/90D01F1/10D02G1/02D01D5/096
Inventor 陆国强
Owner TAICANG HONGYI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap