High magnetic flux density non-oriented electrical steel sheet and motor

An electromagnetic steel sheet, orientation technology, applied in the direction of magnetic circuit characterized by magnetic materials, magnetic properties of inorganic materials, etc., can solve the problems of increased manufacturing cost and inability to obtain sufficient magnetic flux density.

Active Publication Date: 2017-09-29
JFE STEEL CORP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since this method uses a single cold rolling method at room temperature, the effect of improving the magnetic flux density cannot be sufficiently obtained
In this regard, the magnetic flux density can be improved when the above-mentioned cold rolling is performed by heating the sheet temperature to about 200°C, but there are problems such as the need for equipment for warm rolling and strict process management.
Moreover, although two or more cold rolling methods with intermediate annealing in between can be used, there is a problem that the manufacturing cost increases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High magnetic flux density non-oriented electrical steel sheet and motor
  • High magnetic flux density non-oriented electrical steel sheet and motor
  • High magnetic flux density non-oriented electrical steel sheet and motor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0087] Steels a to r having various compositions shown in Table 1 were melted and continuously cast to produce billets. At this time, in order to facilitate the comparison of iron loss, the component composition of the slab was adjusted so that the value of (Si+Al+Mn / 2) obtained from the contents (mass %) of Si, Al, and Mn was to the same extent. Next, the above-mentioned billet was reheated to a temperature of 1020-1120° C., and then hot-rolled to form a hot-rolled sheet with a thickness of 2.0 mm. The hot-rolled sheet was annealed at 1,000° C.×30 seconds by continuous annealing, and then Cold-rolled to produce a cold-rolled sheet (cold-rolled coil) with a plate thickness of 0.15 mm. In addition, samples of the size of iron loss test pieces were cut out from the above-mentioned cold-rolled coils in the rolling direction (L) and the rolling direction (C) perpendicular to the rolling direction.

[0088] Table 1

[0089]

[0090] Next, the above-mentioned cold-rolled sheet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a non-oriented electrical steel sheet and a motor using the non-oriented electrical steel sheet as an iron core. The non-oriented electrical steel sheet contains C: 0.010% or less, Si: 1.0-7.0%, Mn: 0.001-3.0%, acid-soluble Al: 0.0001-3.5%, P: 0.01-0.2%, S: 0.010% or less, N: 0.010% or less, the peak-peak height P120 of P near the electron energy 120eV of the Auger differential spectrum obtained by analyzing the intergranular fracture surface of the non-oriented electrical steel sheet by Auger electron spectroscopy The peak-peak height Fe700 ratio (P120 / Fe700) of Fe near electron energy 700eV is 0.1 or more, and the sheet thickness is 0.10-0.50mm.

Description

technical field [0001] The present invention relates to a high-flux-density non-oriented electrical steel sheet excellent in iron loss characteristics in a high-frequency region, which is mainly used in electric vehicles, Iron core materials for drive motors and generator motors of hybrid vehicles, etc. Background technique [0002] In recent years, the practical use of hybrid vehicles and electric vehicles is rapidly developing. For the drive motors and generator motors used in these vehicles, they need to be installed in a limited space in the vehicle and reduce the weight of the vehicle. Therefore, it is desirable to have a small size. change. Therefore, in order to reduce the size of the electric motor, variable speed driving by frequency control of the drive power supply of the electric motor, and electric motors rotating at a high frequency in a high-frequency range higher than the commercial frequency are increasing. As a result, drive motors and generator motors ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C22C38/06C22C38/60H01F1/16C21D8/12
CPCC21D8/12C21D8/1233C21D8/1272C22C38/00C22C38/001C22C38/002C22C38/004C22C38/005C22C38/008C22C38/02C22C38/04C22C38/06C22C38/08C22C38/16C22C38/34C22C38/60H01F1/16H02K1/02
Inventor 中西匡小关新司尾田善彦户田广朗
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More