Sarcandra glabra facial mask base fabric, preparation method and preparation system

A grass coral fiber and coral technology, which is applied in the field of mask base fabric manufacturing, can solve the problems of lack of functionality of mask base fabric, incomplete degradation, low production speed, etc. Effect

Inactive Publication Date: 2016-03-30
SHANDONG PROVINCE WINSON NON WOVEN MATERIALS
View PDF8 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the above-mentioned problems existing in the prior art, to provide a grass-coral facial mask base cloth with good skin-adhesiveness, good antibacterial properties, good shape retention, good liquid-locking property and complete degradability, which overcomes the existing problems. The mask base fabric made by existing technology has defects such as lack of functionality, inability to completely degrade after being discarded, low production speed, and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sarcandra glabra facial mask base fabric, preparation method and preparation system
  • Sarcandra glabra facial mask base fabric, preparation method and preparation system
  • Sarcandra glabra facial mask base fabric, preparation method and preparation system

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation system of grass coral facial mask base cloth, such as figure 2 As shown, it includes a protective layer unwinder 1 connected in sequence, a carding machine 4 with agglomeration rollers, a carding machine 6 that directly strips the doffer into a web, a spunlace system 8, a dryer 9, and a winder 10. The lactic acid spunbonded nonwoven fabric is unrolled by the protective layer unwinder, adjusted by the tension adjustment structure 3, and then laminated with the liquid storage layer fiber web formed by the random carding of the carding machine with coagulation rollers to form a two-layer laminate. The two-layer laminate and The functional layer fiber web formed by the carding machine that is directly peeled off by the doffer is superimposed to form a three-layer laminate. The three-layer laminate is fed into the spunlace system for spunlace entanglement and compounding to obtain the wet grass coral mask base fabric. The wet state The grass coral mask base ...

Embodiment 1

[0046] A grass coral facial mask base cloth, which is a three-layer fiber web of functional layer web 7, liquid storage layer web 5 and protective layer web 2 from top to bottom, and the functional layer web 7 is made of 100% grass Coral fiber is made of, and its surface density is 12 grams / square meter; Described liquid storage layer web 5 is made of 100% viscose fiber, and its surface density is 11 grams / square meter; Described protective layer fiber web 2 is vertical and horizontal The polylactic acid spunbonded nonwoven fabric with a strength ratio of 1.2:1 has an areal density of 12 grams per square meter. The grass coral fiber fiber of the functional layer web 7 has a length of 45 mm and a linear density of 1.56 dtex; the viscose fiber of the liquid storage layer web 5 has a length of 45 mm and a linear density of 1.56 dtex; The fiber fineness of the protective layer web 2 is 1.1 decitex. The preparation steps refer to the above, and the functional layer web 7, the liqu...

Embodiment 2

[0048]A kind of grass coral facial mask base cloth, it is successively three layers of fiber webs of functional layer fiber web 7, liquid storage layer fiber web 5 and protective layer fiber web 2 from top to bottom, and described function layer fiber web 7 is added by weight ratio It is composed of 85% grass coral fiber and 15% bamboo pulp fiber, and its surface density is 15 grams per square meter; the liquid storage layer fiber web 5 is made of 100% viscose fiber, and its surface density is 15 grams per square meter m; the protective layer fiber web 2 is a polylactic acid spunbonded nonwoven fabric with a vertical and horizontal strength ratio of 1.1:1, and its surface density is 15 grams per square meter. The grass coral fiber fiber of the functional layer web 7 has a length of 42 mm and a linear density of 1.65 dtex; the viscose fiber of the liquid storage layer web 5 has a length of 42 mm and a linear density of 1.65 dtex; The fiber fineness of the protective layer web 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sarcandra glabra facial mask base fabric, a preparation method and a preparation system. The sarcandra glabra facial mask base fabric comprises three layers of fiber webs including a functional layer fiber web, a liquid storage layer fiber web and a protection layer fiber web, wherein the functional layer fiber web, the liquid storage layer fiber web and the protection layer fiber web are twisted and fixedly connected to a whole after being twisted and reinforced by spunlace; the functional layer fiber web is a parallel fiber web; the liquid storage layer fiber web is a fiber web formed by random carding by a condensing roller; the protection layer fiber web adopts non-woven cloth; the functional layer fiber web, the liquid storage layer fiber web and the protection layer fiber web are superposed from top to bottom, then are twisted and compounded by spunlace according to a working procedure of front prewet spunlace, one front spunlace, one back spunlace and two front spunlace, and are dried and wound to form the sarcandra glabra facial mask base fabric. The sarcandra glabra facial mask base fabric disclosed by the invention is high in skin-friendliness, antibacterial property, shape retention and liquid lock performance, can be completely degraded, is high in production efficiency and low in cost, and can meet the requirements on greening, ecology, environment protection and health.

Description

technical field [0001] The invention relates to the technical field of manufacturing facial mask base cloth, in particular to a grass coral facial mask base cloth which has antibacterial effect and can be completely degraded under natural conditions, a preparation method and a preparation system. Background technique [0002] The facial masks in the prior art are divided into carrier-free and carrier-based facial masks according to the way of use. The latter is based on the film-forming material as the facial mask base cloth, supplemented by functional nutrients. Non-woven material mask is a new type of carrier mask product, which must meet the requirements of "one-time use, practical and convenient, safe and hygienic, and low cost". Conventional facial mask base fabrics are usually made of polyester staple fibers and viscose staple fibers that are loosened and mixed, and then formed by cross-lapping, and then strengthened by hydroentangling, drying, and winding. However, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/02B32B9/04
CPCB32B9/02B32B9/04B32B2262/06B32B2262/14
Inventor 刘双营陈鑫王远富徐艳峰商延航朱磊杜婷婷贾亚楠
Owner SHANDONG PROVINCE WINSON NON WOVEN MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap