A kind of low-carbon cold-rolled steel plate for LED lead frame and production method thereof

A technology of lead frame and cold-rolled steel plate, which is applied in the field of low-carbon cold-rolled steel plate for LED lead frame and its production field, can solve the problems of high surface roughness, uneven hardness, poor aging resistance, etc., and achieve high surface quality, crystal The degree of grain "cake shape" is increased, and the processing and aging resistance are good

Active Publication Date: 2017-10-27
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a low-carbon cold-rolled steel plate for LED lead frame and its production method, which mainly solves the technical problems of uneven hardness, high surface roughness and poor aging resistance of the existing low-carbon cold-rolled steel plate for LED lead frame

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low-carbon cold-rolled steel plate for LED lead frame and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] This implementation selects product specification to be 0.5mm*836mm, below in conjunction with embodiment 1 ~ 3 and comparative example---Chinese patent application number is disclosed in the patent application of CN200580032921.5, the present invention is further described, as table 1 ~ table 4 shown.

[0040] Table 1 The chemical composition of the present invention (% by weight), the balance is Fe and unavoidable impurities.

[0041] element

C%

Si%

Mn%

P%

S%

Alt%

B%

N%

this invention

0.025-0.05

≤0.03

0.15-0.25

≤0.020

≤0.010

0.025-0.048

0.001-0.0014

≤0.0035

Example 1

0.0268

0.0119

0.2215

0.0135

0.0086

0.0426

0.0013

0.002

Example 2

0.0392

0.0117

0.1857

0.0134

0.0085

0.0308

0.0010

0.00198

Example 3

0.0485

0.0116

0.1951

0.0130

0.0088

0.0375

0.0011

0.0028

comparative example

0.02-0.055

≤0.04

0.2-0.3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a low carbon cold-rolled steel sheet for a LED lead frame and a production method thereof, and mainly solves the technical problems that the low carbon cold-rolled steel sheet for the LED lead frame in prior art has nonuniform hardness, high surface roughness and bad aging-resistance. The production method comprises the following steps: smelting according to components, molten iron desulphurization, complex top-bottom blowing converter smelting, argon blowing from bottom of a ladle, protective casting with argon blowing in whole course, heating in a slab heating furnace, rough rolling, finish rolling, reeling for obtaining a hot-rolled steel coil, uncoiling, pickling, cold rolling, annealing in a vertical type continuous annealing furnace, flattening, and reeling for obtaining a finished product with a thickness of 0.4-0.5mm; the finishing temperature of the finish rolling is 860-900 DEG C, the reeling temperature of the hot rolling is 620-660 DEG C, the cold rolling reduction is 75-85%, the temperature scope of a soaking zone of the vertical type continuous annealing furnace for a band steel in hard rolled state after cold rolling is 710-730 DEG C, the soaking time for the band steel in the vertical type continuous annealing furnace is 105-120 s, and temper elongation is 1.0-1.4%. The low carbon cold-rolled steel sheet is mainly used for the LED lead frame.

Description

technical field [0001] The invention relates to a low-carbon cold-rolled steel plate and a production method thereof, in particular to a low-carbon cold-rolled steel plate for an LED lead frame and a production method thereof. Background technique [0002] Light emitting diode (LED) is known as the fourth generation of light source in human history. It has many advantages such as high luminous efficiency, small size, safety, and long life. It is also energy-saving and environmentally friendly. It is widely used in agriculture, fishery, medical treatment, communication and other fields have broad prospects for development. [0003] The lead frame of the LED bracket is the basic component of the LED product. In order to reduce the cost, the industry has begun to use low-carbon steel instead of the original copper material; in order to ensure corrosion resistance, the surface of the low-carbon steel is first plated with copper and then silver-plated. The main difficulty of ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/06C21D8/02
Inventor 赵楠刘学伟周丽萍王海军曹博蕊李丹曹孝平申庆波
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products