Aloe natural environmental-protection wall coating

A natural and environmentally friendly coating technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve problems such as adverse effects on the human body, achieve super moisture retention and pH adjustment capabilities, reduce viscosity, and high whiteness Effect

Inactive Publication Date: 2016-06-01
JIANGSU CHAMPION TECHNOLOGY GROUP CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are domestic patent reports about aloe paint, such as CN102140282A, which provides a preparation method of wild aloe paint, using aloe powder as raw material, but using antifungal agents and preservatives with chemical functional components, these Chemical antifungal agents and preservatives will gradually volatilize into the indoor air after painting, and become the main components of VOC like chemical humectants, causing adverse effects on the human body. This is not the development trend of shell powder wall coatings in the future

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aloe natural environmental-protection wall coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044]Add 200.5kg of water, 1.0kg of ephedra alkaloids, 2.5kg of SN5040 dispersant, 1.0kg of CF-10 wetting agent, and 1.0kg of NXZ defoamer into the reactor, and disperse at a speed of (500~800) r / min (10~ 25) min; then add 120.0kg aloe vera gel, 160.5kg R-902 titanium dioxide, 40.0kg talcum powder, stir at a speed of (800~1500) r / min for (10~40) min, and grind to the fineness of the material ≤50μm; then add 190.5kg ELASTENE (Yi Renda?) 3131NG pure acrylic emulsion, 30.5kg plant glue, 1.0kgNXZ defoamer to the reactor, stir at the speed of (300~900) r / min (10~30 ) min; finally, adjust the viscosity with 25.5kg water and 7.5kg vegetable glue, so that the viscosity is (100±5) KU at (25±1)°C, pass through a 200-mesh sieve, and obtain a white flowing liquid after passing the test, which is Invent products.

Embodiment 2

[0046] Add 230.5kg of water, 1.5kg of ephedra alkaloids, 4.5kg of SN5040 dispersant, 1.5kg of CF-10 wetting agent, and 1.5kg of NXZ defoamer into the reactor, and disperse at a speed of (500~800) r / min (10~ 25) min; then add 150.0kg aloe vera gel, 190.5kg R-902 titanium dioxide, 50.0kg talcum powder, stir (10~40)min at a speed of (800~1500)r / min, and sand grind to the fineness of the material ≤50μm; then add 220.5kg ELASTENE (Yi Renda?) 3131NG pure acrylic emulsion, 40.5kg vegetable glue, 1.5kgNXZ defoamer to the reactor, stir at the speed of (300~900) r / min (10~30 ) min; finally, adjust the viscosity with 30.5kg water and 10.5kg vegetable glue, so that the viscosity is (100±5) KU at (25±1)°C, pass through a 200 mesh sieve, and obtain a white flowing liquid after passing the test, which is Invent products.

Embodiment 3

[0048] Add 260.0kg of water, 2.5kg of ephedra alkaloids, 5.0kg of SN5040 dispersant, 2.8kg of CF-10 wetting agent, and 2.5kg of NXZ defoamer into the reactor, and disperse at a speed of (500~800) r / min (10~ 25) min; then add 170.0kg of aloe vera gel, 210.5kg of R-902 titanium dioxide, 60.0kg of talcum powder, stir at a speed of (800~1500)r / min for (10~40)min, and sand-mill to the fineness of the material ≤50μm; then add 260.5kg ELASTENE (Yi Renda?) 3131NG pure acrylic emulsion, 45.5kg plant glue, 2.5kgNXZ defoamer to the reactor, stir at the speed of (300~900) r / min (10~30 ) min; finally adjust the viscosity with 35.5kg water and 12.5kg vegetable glue, so that the viscosity is (100±5) KU at (25±1)°C, pass through a 200-mesh sieve, and obtain a white flowing liquid, which is Invent products.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aloe natural environmental-protection wall coating, which is characterized by being mainly prepared from the following ingredients (by weight): 200-340 parts of water, 130-250 parts of titanium dioxide, 20-80 parts of talcum powder, 1-4 parts of alkaloid, 2-8 parts of a dispersant, 1-4 parts of a wetting agent, 1-8 parts of an antifoaming agent, 100-240 parts of aloe-gel, 150-320 parts of an acrylic emulsion and 20-80 parts of vegetable glue. The coating has full film, has excellent effects in aspects of smell, environmental protection and performance, has good decorative function and environmental protection function, and is an aloe natural environmental-protection wall coating with excellent comprehensive properties.

Description

technical field [0001] The invention belongs to the field of wall paint for interior decoration, in particular to an aloe vera natural environmental protection wall paint Background technique [0002] With the increasing development of urban and rural areas, the harm of indoor air pollution to human health has become the most concerned hot issue in today's society. People's awareness of indoor environmental protection is also rising rapidly. In interior decoration, people generally pay attention to the pollution of benzene substances in paints. In fact, formaldehyde is the number one killer in home decoration. It exists in large quantities in paints and adhesives, and harmful substances such as formaldehyde and benzene in decoration materials The release period is 3 to 15 years, and it is difficult to remove by traditional methods. At present, biological scientists have found that natural aloe vera has excellent antiseptic and antibacterial functions, super moisturizing pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D105/00C09D7/12C09D5/08C09D5/14
Inventor 谢海
Owner JIANGSU CHAMPION TECHNOLOGY GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap