Blended yarn multifunctional fabric and making method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A blended yarn, multifunctional technology, applied in the field of blended yarn multifunctional fabric and its preparation, can solve the problems of insufficient completeness and single function, and achieve improved compression resistance, excellent mechanical properties, good strength and light weight. Effect
Inactive Publication Date: 2016-06-08
NINGBO MH IND CO LTD
View PDF6 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But the function of existing blended yarn multifunctional fabric is comparatively single, not complete enough
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0020] Warping yarn: bobbin, warping, coiling, warp head, sizing, coiling, doubling, weaving weaving; in the doubling process, stainless steel fiber, copper fiber and carbon fiber are gradually wrapped around the spandex yarn core Spun into warp blended yarn; the contents of stainless steel fiber, copper fiber, carbon fiber and spandex are 8%, 3%, 4% and 85% respectively;
[0021] Whole weft yarn: bobbin, warping, coiling, warp yarn head, sizing, coiling, warp doubling, weaving pan head; in the doubling process, stainless steel fiber, bamboo fiber, ramie fiber is gradually wrapped in spandex yarn core Outwardly spun into weft blended yarn; the content of stainless steel fiber, bamboo fiber, ramie fiber and spandex is 5%, 6%, 5% and 84% respectively;
[0022] Weaving: weaving warp yarn blended yarn and weft yarn blended yarn into fabric, the fabric weave adopts plain weave; finishing: after dyeing, softening and shaping, the blended yarn multifunctional fabric of the present in...
Embodiment 2
[0024] In the present embodiment, the contents of stainless steel fiber, copper fiber, carbon fiber and spandex in the warp yarn are 6%, 4%, 4% and 86% respectively; the contents of stainless steel fiber, bamboo fiber, ramie fiber and spandex are respectively 8%, 4%, 4% and 84%; other processes are as described in Example 1, and will not be repeated here.
Embodiment 3
[0026] In the present embodiment, the contents of stainless steel fiber, copper fiber, carbon fiber and spandex in the warp yarn are respectively 9%, 3%, 3% and 85%; the contents of stainless steel fiber, bamboo fiber, ramie fiber and spandex are respectively 6%, 7%, 5% and 82%; other processes are as described in Example 1, and will not be repeated here.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a blended yarn multifunctional fabric and a making method thereof, and belongs to the technical field of spinning engineering. Warp of the fabric is blended yarn spun by adopting spandex silk as a yarn core and wrapping the yarn core by stainless steel fibers, copper fibers and carbon fibers. Weft of the fabric is blended yarn spun by adopting spandex silk as a yarn core and wrapping the yarn core by stainless steel fibers, natural bamboo fibers and ramie. The content of the stainless steel fibers in the warp ranges from 5% to 10%, the content of the copper fibers in the warp ranges from 2% to 5%, the content of the carbon fibers in the warp ranges from 2% to 5%, and the content of the spandex silk in the warp ranges from 80% to 91%. The content of the stainless steel fibers in the weft ranges from 3% to 10%, the content of the natural bamboo fibers in the weft ranges from 3% to 8%, the content of the ramie in the weft ranges from 3% to 8%, and the content of the spandex silk in the weft ranges from 74% to 91%. The fabric has the environmental protection property and functionality on the aspects of bacteria resistance and bacteriostasis, moisture absorption and quick drying, biodegradation and the like, and has good strength, elasticity, tear resistance and tenacity, and a good radiation protection and shielding effect is further achieved. The cloth face is flat, soft and smooth, the radiation protection efficiency reaches 92% or above, the moisture regain ranges from 8% to 10%, and the fiber bacteriostasis rate is larger than or equal to 91%.
Description
technical field [0001] The invention relates to a blended yarn multifunctional fabric and a preparation method thereof, belonging to the technical field of spinning engineering. Background technique [0002] Blended yarn is a yarn spun from two or more fibers, such as linen / cotton, wool / cotton, wool / linen / silk, polyester / cotton, polyester / wool, etc., breaking the original cotton, linen , wool, silk, and chemical fiber can make up for the deficiency of a single textile material, reflect the superiority of each component fiber, improve the wearing function of the fabric, and expand the scope of application. But existing blended yarn multifunctional fabric function is relatively single, not complete enough. Contents of the invention [0003] Aiming at the defects in the prior art, the invention provides a blended yarn multifunctional fabric with good radiation protection performance, antibacterial and antibacterial effects and excellent elasticity. [0004] The above object...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more