Preparation method of plastic plated piece

A technology for plastic and plated parts, applied in the direction of coating, etc., can solve the problems of insufficient final brightness, warping of casting surface decoration, poor elasticity, etc., and achieve the effect of good product effect, good ductility, and strong deformation resistance

Active Publication Date: 2017-04-05
GUANGZHOU BAOLI TRADE
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even so, the film used is PET or PC, and the PET film can only be slightly stretched, so it cannot be used for large-area curved surface decoration, and it is easy to cause a high defect rate of the final product. The final brightness is not enough; and PC is easy to absorb moisture, which will affect the life of the product, and because the PC film is thick, only screen printing can be used, so the effect is rough
There are improvements to the film in the prior art, such as the Chinese patent "An Optical Polyester Film a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of plastic plated piece

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] A method for preparing plastic plating parts. The modified polyester film is used for vacuum sputtering, and then a thermal adhesive layer is compounded on the modified polyester film, and then the modified polyester film is positively pressure-formed into the desired plastic The plated part has the same shape, and finally the finished product is injection molded. The hot-bonding layer is a material that can be hot-bonded with plastic castings during injection molding. The plastic casting is 4 circular rings connected in sequence.

[0021] The modified polyester film is prepared by melting saturated polyester and polyurethane, adding curing agent and auxiliary agent, and then coating and curing the carrier film, and then tearing off the carrier film.

[0022] Further, when melting, the mass ratio of the saturated polyester, polyurethane, solvent, curing agent and auxiliary agent is 80:20:50:5:5; when melting, the saturated polyester, polyurethane, curing ...

Example Embodiment

[0026] Example 2

[0027] A method for preparing plastic plating parts. The modified polyester film is used for vacuum sputtering, and then a thermal adhesive layer is compounded on the modified polyester film, and then the modified polyester film is positively pressure-formed into the desired plastic The plated part has the same shape, and finally the finished product is injection molded. The hot-bonding layer is a material that can be hot-bonded with plastic castings during injection molding. The plastic casting is 4 circular rings connected in sequence.

[0028] The modified polyester film is prepared by dissolving saturated polyester and polyurethane, adding a curing agent and an anti-hydrolysis agent, and then coating and curing the carrier film and tearing off the carrier film.

[0029] Further, when melting, the mass ratio of the saturated polyester, polyurethane, solvent, curing agent and anti-hydrolysis agent is 60:5:45:3:3.

[0030] Wherein, the curing temperature is 25°C....

Example Embodiment

[0033] Example 3

[0034] A method for preparing plastic plating parts. After vacuum sputtering, a modified polyester film is used to print a hot-adhesive layer on the modified polyester film, and then the modified polyester film is positively pressure-formed into the desired plastic The plated part has the same shape, and finally the finished product is injection molded. The hot-bonding layer is a material that can be hot-bonded with plastic castings during injection molding. The plastic casting is 4 circular rings connected in sequence.

[0035] The modified polyester film is prepared by melting the saturated polyester and polyurethane, adding a curing agent and an anti-UV agent, and then coating and curing the carrier film and tearing off the carrier film.

[0036] Further, when melting, the mass ratio of the saturated polyester, polyurethane, curing agent and anti-UV agent is 95:40:8:8.

[0037] Wherein, the melting temperature is 230°C. The curing temperature is 80°C. The thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting temperatureaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a plastic plated piece. The preparation method comprises the following steps: a modified polyester film is adopted to carry out vacuum sputtering, then, hybrid printing is carried out on the modified polyester film, positive pressure suction plastic is carried out the modified polyester film to enable the modified polyester film to form the shape the same as that of the to-be-prepared plastic plated piece, and finally, injection molding is carried out to form a finished product. According to the invention, the non-stretched modified polyester film is taken as a composite film, so that the modified polyester film has better ductility compared with PET or PC, is suitable for large-area hook face decoration, and is high in dampproof and deformation resisting properties; and in addition, in combination with the advantages of vacuum sputtering and IMD (In-mold decoration), the plastic plated piece is excellent in effect and wear resistant, and the color and pattern can be changed at will.

Description

technical field [0001] The invention relates to film interior decoration, in particular to a preparation method of plastic plated parts. Background technique [0002] The decoration of plastic plated parts is to treat the surface of plastic parts. Since plastic products are required to be light, thin, short, and often have curved surfaces, this puts forward more requirements for technology. The existing technologies used for surface treatment are mainly divided into water plating, vacuum plating and chemical plating. Among them, water plating is to use electrolysis to deposit metal or alloy on the surface of the workpiece to form a uniform, dense, and well-bonded metal layer. Water plating can be used for the decoration of curved and flat surfaces, but the process is too long and the color is relatively monotonous. Generally, there are only sub-silver, gray silver, gun color, gold, black chrome, and the general coating material is "hexavalent chromium". ", this is a non-en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C45/14
CPCB29C45/14688B29C2045/14713
Inventor 李艳洵陈勇军
Owner GUANGZHOU BAOLI TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap