Rubber used for solid tyres and a preparing method thereof

A solid tire and rubber technology, applied in special tires, tire parts, transportation and packaging, etc., can solve problems such as car crashes and fatalities, and achieve improved mechanical properties, improved bonding uniformity, good antistatic and wear resistance Scratch-resistant effect

Inactive Publication Date: 2017-08-29
明光速耐德实心轮胎有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As the main parts of automobiles, tires are inevitably worn out and punctured during use, and air leakage is inevitable. Especially in the case of tire blowouts in high-speed automobiles, it is very easy to cause serious accidents such as car crashes and fatalities.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of rubber for solid tire according to the preferred embodiment of the present invention and its preparation method;

[0027] The rubber for the solid tire is prepared from the following raw materials in parts by weight:

[0028] 46 parts of natural rubber, 8 parts of nitrile rubber, 15 parts of polybutadiene, 17 parts of hydroxyethyl acrylate, 5 parts of graphene, 6 parts of nano-titanium dioxide, 10 parts of stearic acid, 6 parts of anti-aging agent, 8 parts of vulcanizing agent , 7 parts of coupling agent, 18 parts of filler.

[0029] The filler is a mixture of talc powder and high-viscosity attapulgite clay, wherein the weight ratio of the two is 1:0.9.

[0030] The high-viscosity attapulgite is a product obtained by purifying and thermally activating natural attapulgite clay.

[0031] The coupling agent is a silane coupling agent.

[0032] The present invention prepares the method for solid tire rubber, comprises the steps:

[0033] (1) Weigh natural rubb...

Embodiment 2

[0041] A kind of rubber for solid tire according to the preferred embodiment of the present invention and its preparation method;

[0042] The rubber for the solid tire is prepared from the following raw materials in parts by weight:

[0043] 35 parts of natural rubber, 5 parts of nitrile rubber, 10 parts of polybutadiene, 9 parts of hydroxyethyl acrylate, 2 parts of graphene, 5 parts of nano-titanium dioxide, 6 parts of stearic acid, 3 parts of anti-aging agent, 5 parts of vulcanizing agent , 6 parts of coupling agent, 15 parts of filler.

[0044] The filler is a mixture of talcum powder and high-viscosity attapulgite clay, wherein the weight ratio of the two is 1:0.8.

[0045] The high-viscosity attapulgite is a product obtained by purifying and thermally activating natural attapulgite clay.

[0046] The coupling agent is a silane coupling agent.

[0047] The present invention prepares the method for solid tire rubber, comprises the steps:

[0048] (1) Weigh natural rubb...

Embodiment 3

[0056] A kind of rubber for solid tire according to the preferred embodiment of the present invention and its preparation method;

[0057] The rubber for the solid tire is prepared from the following raw materials in parts by weight:

[0058] 50 parts of natural rubber, 12 parts of nitrile rubber, 20 parts of polybutadiene, 18 parts of hydroxyethyl acrylate, 7 parts of graphene, 8 parts of nano titanium dioxide, 13 parts of stearic acid, 9 parts of anti-aging agent, 10 parts of vulcanizing agent , 10 parts of coupling agent, 23 parts of filler.

[0059] The filler is a mixture of talcum powder and high-viscosity attapulgite clay, wherein the weight ratio of the two is 1:1.2.

[0060] The high-viscosity attapulgite is a product obtained by purifying and thermally activating natural attapulgite clay.

[0061] The coupling agent is a silane coupling agent.

[0062] The present invention prepares the method for solid tire rubber, comprises the steps:

[0063] (1) Weigh natural...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Rubber used for solid tyres and a preparing method thereof are disclosed. The rubber includes natural rubber, butadiene-acrylonitrile rubber, polybutadiene, 2-hydroxyethyl acrylate, graphene, nanometer titanium dioxide, stearic acid, an antioxidant, a vulcanizing agent, a coupling agent and a filler. The method includes adding polymer into an internal mixer, plastifying the polymer, then adding the graphene, the 2-hydroxyethyl acrylate and the silane coupling agent, blending the mixture, then adding the rest components in order, and discharging the rubber after blending is finished to obtain the rubber used for solid tyres. The rubber has good shaping effects, and has good using properties such as wear resistance, corrosion resistance and weatherability. The rubber is used for preparing the solid tyres and provides a guarantee for automobile using safety.

Description

technical field [0001] The invention relates to the technical field of solid tires, in particular to a rubber for solid tires and a preparation method. Background technique [0002] As the main accessories of automobiles, tires are unavoidable to be worn and punctured during use, especially when a tire blows out in a high-speed automobile, it is very easy to cause serious accidents such as car crashes and fatalities. Therefore, various manufacturers are constantly improving the safety, environmental protection, and energy-saving requirements of tires. In order to prevent tires from exploding, existing automobiles generally use the tubeless vehicle wheel, and the country for heavy-duty vehicles requires progressively promoting the use of the tubeless vehicle wheel. Solid tires are generally used under high loads, and the rubber compound is required to have sufficient pressure resistance and wear resistance, high enough modulus stress, high hardness, low permanent deformation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L9/02C08L47/00C08K13/02C08K5/101C08K3/04C08K3/22C08K5/09C08K3/34C08K5/54B60C1/00
CPCC08L7/00B60C1/00B60C2001/0091C08K2003/2241C08L2201/08C08L2205/03C08L9/02C08L47/00C08K13/02C08K5/101C08K3/04C08K3/22C08K5/09C08K3/34C08K3/346C08K5/54
Inventor 卞泽根
Owner 明光速耐德实心轮胎有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com