Wear-resistant and corrosion-resistant traffic marking material and preparation method thereof

A traffic marking and corrosion-resistant technology, applied in the traffic field, can solve the problems of easy wear and tear, poor corrosion resistance, etc., and achieve the effects of not easy to crack, good weather resistance, good wear resistance and corrosion resistance

Active Publication Date: 2020-02-14
长春市立元交通工程有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defects of the existing traffic marking materials that are easy to wear and fall off and have low corrosion resistance, provide a traffic marking material with high wear resistance and corrosion resistance, and improve the weather resistance of traffic markings sex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant and corrosion-resistant traffic marking material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A wear-resistant and corrosion-resistant traffic marking material, comprising the following components in parts by mass:

[0022] 10 parts of polyester resin, 10 parts of rosin glyceride, 8 parts of iron powder, 8 parts of limestone powder, 6 parts of silica gel, 4 parts of basic lead silicochromate, 1 part of dehydrated castor oil, 1 part of tung oil, ethylene glycol ether 20 servings.

[0023] The particle diameter of the iron powder is less than 0.5mm, and the particle diameter of the limestone powder is less than 1mm.

[0024] The silica gel is organic silica gel.

[0025] A method for preparing a wear-resistant and corrosion-resistant traffic marking material, comprising the steps of:

[0026] a. Weigh each component according to their respective mass parts, add ethylene glycol ether, polyester resin and rosin glyceride in sequence into the reaction kettle with stirring function, start the stirrer and stir slowly until the mixture is uniform in texture viscous, ...

Embodiment 2

[0032] A wear-resistant and corrosion-resistant traffic marking material, comprising the following components in parts by mass:

[0033] 18 parts of polyester resin, 18 parts of rosin glyceride, 12 parts of iron powder, 12 parts of limestone powder, 10 parts of silica gel, 5 parts of basic lead silicochromate, 3 parts of dehydrated castor oil, 3 parts of tung oil, ethylene glycol ether 30 servings.

[0034] The particle diameter of the iron powder is less than 0.5mm, and the particle diameter of the limestone powder is less than 1mm.

[0035] The silica gel is organic silica gel.

[0036] A method for preparing a wear-resistant and corrosion-resistant traffic marking material, comprising the steps of:

[0037] a. Weigh each component according to their respective mass parts, add ethylene glycol ether, polyester resin and rosin glyceride in sequence into the reaction kettle with stirring function, start the stirrer and stir slowly until the mixture is uniform in texture visc...

Embodiment 3

[0043] A wear-resistant and corrosion-resistant traffic marking material, comprising the following components in parts by mass:

[0044] 15 parts of polyester resin, 15 parts of rosin glyceride, 10 parts of iron powder, 10 parts of limestone powder, 8 parts of silica gel, 4 parts of basic lead silicochromate, 2 parts of dehydrated castor oil, 2 parts of tung oil, ethylene glycol ether 25 servings.

[0045] The particle diameter of the iron powder is less than 0.5mm, and the particle diameter of the limestone powder is less than 1mm.

[0046] The silica gel is organic silica gel.

[0047] A method for preparing a wear-resistant and corrosion-resistant traffic marking material, comprising the steps of:

[0048] a. Weigh each component according to their respective mass parts, add ethylene glycol ether, polyester resin and rosin glyceride in sequence into the reaction kettle with stirring function, start the stirrer and stir slowly until the mixture is uniform in texture visco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a wearproof and erosion resistant traffic marking material and a preparation method thereof. The traffic marking material comprises the following components by mass: 10-18 parts of polyester resin, 10-18 parts of rosin glycerin ester, 8-12 parts of iron powder, 8-12 parts of limestone powder, 6-10 parts of silica gel, 4-5 parts of basic lead silicochromate, 1-3 parts of dehydrated castor oil, 1-3 parts of tung oil, and 20-30 parts of ethylene glycol ether. The traffic marking material provided by the invention has very good wearproof, waterproof and alkali erosion resistant characteristics, also has good adhesion, does not fall off or crack easily, and is suitable for use on high grade traffic roads, like freeways and airport roads.

Description

technical field [0001] The invention relates to the technical field of traffic, in particular to a wear-resistant and corrosion-resistant traffic marking material and a preparation method thereof. Background technique [0002] Traffic markings are traffic safety facilities composed of various lines, arrows, characters, facade marks, raised road signs and contour marks marked on the road surface. Its function is to control and guide traffic. [0003] When traffic markings are applied on traffic roads, they are not only exposed to wind, sun, and rain, but also to the rolling and wear of wheels, and even in winter in the north, they often face the tearing of anti-skid chains, deicing agents, etc. erosion etc. When the traffic markings become blurred due to the above-mentioned erosion and wear, it will bring certain hidden dangers of traffic accidents. Therefore, the particularity of the environment in which traffic markings are used requires that their preparation materials s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/00C09D193/04C09D7/61
CPCC08K2003/0856C08K2003/265C08L2205/035C09D167/00C09D193/04C08L93/04C08L91/00C08L91/005C08K13/02C08K3/08C08K3/26C08K3/36C08K3/34C08L67/00
Inventor 郭绍卫
Owner 长春市立元交通工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com