A special water-based tempered glass ink for touch screen and preparation method thereof

A tempered glass ink, touch screen technology, applied in ink, application, home appliances and other directions, can solve problems such as signal attenuation, and achieve the effect of dense structure, good weather resistance and low melting point

Active Publication Date: 2020-07-21
郑州市亚美凯新材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a special water-based tempered glass ink for touch screen and its preparation method, which mainly improves the ability of surface acoustic wave signal transmission of touch screen glass, and solves the problem of signal attenuation after surface acoustic wave passes through touch screen glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A special water-based tempered glass ink for touch screen and preparation method thereof
  • A special water-based tempered glass ink for touch screen and preparation method thereof
  • A special water-based tempered glass ink for touch screen and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A special water-based tempered glass ink for a touch screen, made of the following raw materials in parts by weight: 12 parts of inorganic pigments, 40 parts of the first glass frit, 10 parts of the second glass frit, 37 parts of water-based varnish, Wetting and dispersing agent 0.5 part, defoamer 0.5 part.

[0032] The first glass powder frit is made up of the composition of following percentage by weight: SiO 2 30%, B 2 o 3 6.8%, Al 2 o 3 2%, Na 2 O 4.5%, K 2 O 2.5%, CaO 3.8%, Li 2 O 6%, TiO 2 3.8%, F 1.5%, Sb 2 o 3 0.5%, the balance is ZnO.

[0033] The second glass powder frit is made up of the composition of following percentage by weight: SiO 2 12%, B 2 o 3 13%, Al 2 o 3 1.5% balance is Bi 2 o 3 .

[0034] The water-based varnish is made up of the following components by weight percentage: 25% water-based modified acrylic polymer HOMAAC TM 5224D (Jintuan Chemicals), 1% water-based hydroxyethyl cellulose HBR250 (Ashlane), 14.6% ethanol, 8...

Embodiment 2

[0044] A special water-based tempered glass ink for a touch screen, made of the following raw materials in parts by weight: 12 parts of inorganic pigments, 32 parts of first glass powder frit, 16 parts of second glass frit, 38.2 parts of water-based varnish, 0.5 parts of wetting and dispersing agent, 0.5 parts of defoaming agent, and 0.8 parts of leveling agent.

[0045] The first glass powder frit is made up of the composition of following percentage by weight: SiO 2 35%, B 2 o 3 12%, Al 2 o 3 1.5%, Na 2 O 8.2%, K 2 O 0.3%, CaO 3.8%, BaO 3.7%, Li 2 O 12%, TiO 2 0.5%, F 1.8%, and the balance is ZnO.

[0046] The second glass powder frit is made up of the composition of following percentage by weight: SiO 2 6%, B 2 o 3 14%, Al 2 o 3 1.5% balance is Bi 2 o 3 .

[0047] The water-based varnish is made up of the following components by weight percentage: 32% water-based modified acrylic polymer HOMAAC TM 5224D (Jintuan Chemicals), 1.5% water-based hydroxye...

Embodiment 3

[0057] A special water-based tempered glass ink for a touch screen, made of the following raw materials in parts by weight: 12 parts of inorganic pigments, 38 parts of the first glass frit, 12 parts of the second glass frit, 37 parts of water-based varnish, Wetting and dispersing agent 0.5 part, defoamer 0.5 part.

[0058] The first glass powder frit is made up of the composition of following percentage by weight: SiO 2 28.2%, B 2 o 3 8.2%, Al 2 o 3 4%, Na 2 O 6.5%, K 2 O 2.1%, CaO 0.8%, BaO 7.2%, Li 2 O 9%, TiO 2 1.2%, F 3%, and the balance is ZnO.

[0059] The second glass powder frit is made up of the composition of following percentage by weight: SiO 2 12%, B 2 o 3 13%, Al 2 o 3 1.5% balance is Bi 2 o 3 .

[0060] The water-based varnish is composed of the following components by weight percentage: 35% water-based modified acrylic polymer HOMAAC TM 5224D (Jintuan Chemicals), 0.8% water-based hydroxyethyl cellulose HBR250 (Ashlan), 15% ethanol, 10% ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of chemical printing ink, and specifically relates to an aqueous toughened glass printing ink dedicated for touch screen and a preparation method thereof. The aqueous toughened glass printing ink is prepared from the following raw materials in parts by weight: 6 to 28 parts of inorganic pigment, 20 to 50 parts of first glass powder frit, 10 to 40 parts of second glass powder frit, 10 to 60 parts of aqueous varnish, 0 to 2 parts of wetting dispersant, 0 to 1 part of antifoaming agent, and 0 to 2 parts of leveling agent. The printing ink can improve the surface acoustic wave signal transduction performance of touch screen glass, solves the problem that after surface acoustic waves go through tough screen glass, the signal attenuates, and has the advantages that the covering performance of the printing ink is good, the surface acoustic wave propagation speed is quick, the energy attenuation is little, no phase change happens, and the corrosion of the printing ink is weak.

Description

technical field [0001] The invention belongs to the technical field of chemical inks, and in particular relates to a special water-based tempered glass ink for touch screens and a preparation method thereof. Background technique [0002] Touch screen, also known as touch screen, is a new computer input device, and is currently the simplest, most convenient and fastest way of human-computer interaction. It is widely used in military electrical appliances, aerospace electrical appliances, high-speed rail, aircraft carrier ships, ships and automobiles, Industry 4.0 Internet of Things, financial banks, commercial retail, industrial control, interactive digital signage and game entertainment. Current touch screens mainly include surface acoustic wave, infrared, resistive, capacitive and other types. The surface acoustic wave touch screen has the characteristics of high resolution, good stability, and good light transmission, which makes it win in other types of touch screen appl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/03C09D11/107C09D11/033
CPCC09D11/03C09D11/033C09D11/107
Inventor 杨中民周岩何宜刚
Owner 郑州市亚美凯新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com