Hot-dip galvanized steel sheet for large-size liquid crystal display backplane and manufacturing method thereof

A technology of hot-dip galvanized steel sheet and liquid crystal display, applied in hot-dip galvanizing process, coating, metal material coating process, etc. Yield strength can not meet the requirements of material transverse and longitudinal properties to improve stamping and drum twisting, so as to reduce energy consumption and cooling water usage, reduce the amount of addition, and achieve the effect of easy production line

Active Publication Date: 2019-12-17
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a hot-dip galvanized steel sheet for a large-size liquid crystal display backplane and its manufacturing method, which mainly solves the technology of drumming and twisting in the stamping process of a 32-55-inch liquid crystal display backplane with an existing hot-dip galvanized steel sheet Problem, the hot-dip galvanized steel sheet of the present invention meets the manufacturing requirements of large-size liquid crystal display backplanes, and no drumming and distortion will occur after stamping
[0007] The present invention focuses on the realization of the ultra-low yield strength of the galvanized sheet, the uniformity of the yield strength in the width direction of the sheet, and the difference in the transverse and longitudinal yield strength of the steel sheet
[0008] In order to solve the technical problem of drumming and twisting after stamping, it is necessary to solve the problem that the yield strength of the hot-dip galvanized steel sheet cannot meet the requirements for improving the stamping and drumming distortion and the uniformity of the material's transverse and longitudinal properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-dip galvanized steel sheet for large-size liquid crystal display backplane and manufacturing method thereof
  • Hot-dip galvanized steel sheet for large-size liquid crystal display backplane and manufacturing method thereof
  • Hot-dip galvanized steel sheet for large-size liquid crystal display backplane and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 4

[0062] Example 4 shows that the sample with a yield strength of 151 MPa, a transverse yield strength difference of 5 MPa, and a transverse and longitudinal yield difference of 5 MPa has no drumming distortion after stamping, indicating that the range of yield strength, the uniformity of the transverse microstructure of the steel plate, and the poor transverse and longitudinal properties are important for improving drumming Distortion has a noticeable effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hot-dip-galvanized steel plate for large-size liquid crystal display back plates and a manufacturing method of the hot-dip-galvanized steel plate and mainly solves the technical problems of bulging and warping in the processes that 32-55-inch liquid crystal display back plates are formed through stamping machining of existing hot-dip-galvanized steel plates. A base plateof the hot-dip-galvanized steel plate for the large-size liquid crystal display back plates is prepared from chemical components in percentage by weight as follows: 0.0005%-0.0009% of C, 0-0.03% of Si, 0.05%-0.12% of Mn, 0.02%-0.04% of Ti, 0.0005%-0.0009% of Nb, less than or equal to 0.0030% of N, less than or equal to 0.015% of P, less than or equal to 0.010% of S, 0.0002%-0.0004% of B and the balance of Fe and inevitable inclusion elements. The hot-dip-galvanized steel plate meets the stamping machining requirements of the 32-55-inch liquid crystal display back plates.

Description

technical field [0001] The invention relates to a hot-dip galvanized steel sheet, in particular to a hot-dip galvanized steel sheet for a large-size liquid crystal display backplane and a manufacturing method thereof, in particular to a hot-dip galvanized steel sheet for manufacturing a 32-55 inch liquid crystal display backplane A steel plate belongs to the technical field of iron-based alloys. Background technique [0002] With the development of science and technology and the improvement of family living standards, LCD screen technology is gradually scaled up. Since 2009, liquid crystal displays have experienced explosive growth, accounting for more than 70% of the global display market. The original CRT displays have gradually withdrawn from the market, and the demand for steel for liquid crystal modules has increased significantly. [0003] In 2013, with the development of large-size LCD screen technology, more and more steel for LCD modules turned to galvanized produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/14C22C38/12C22C38/32B21C37/02C23C2/06C23C2/40
CPCB21C37/02C22C38/02C22C38/04C22C38/12C22C38/14C22C38/32C23C2/06C23C2/40
Inventor 丁志龙
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products