High temperature-resistant Ba-Re-Te zinc alloy applied to cold chamber die casting

A ba-re-te, cold chamber die-casting technology, applied in the field of alloys, can solve the problems of complex equipment, high cost, low output, etc., and achieve the effect of excellent flame retardancy

Inactive Publication Date: 2018-06-19
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has the disadvantages of high cost to varying degrees, flux inclusions in castings, and complicated equipment.
Therefore, the research, development and application of zinc-barium alloys are limited.
Therefore, in the indu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high temperature resistant Ba-Re-Te zinc alloy smelted at 450°C suitable for cold chamber die-casting. In terms of weight percentage, the chemical composition of the alloy is: Ba: 0.8wt.%, Re: 0.5wt.%; Te: 0.7wt.%, Ge: 2.5wt.%, V: 0.6wt.%, Pr: 0.3wt.% .%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 450 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 450°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 18m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare zinc-barium alloy castings with complex shapes; the final hea...

Embodiment 2

[0021]A high-temperature-resistant Ba-Re-Te zinc alloy smelted at 470°C suitable for cold chamber die-casting. In terms of weight percentage, the chemical composition of the alloy is: Ba: 0.9wt.%, Re: 0.5wt.%; Te: 0.7wt.%, Ge: 2.5wt.%, V: 0.6wt.%, Pr: 0.3wt.% .%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 470 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 470°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots, with the ingot moving down at a speed of 16m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare zinc-barium alloy castings with complex shapes; the fina...

Embodiment 3

[0024] A high-temperature-resistant Ba-Re-Te zinc alloy smelted at 490°C suitable for cold chamber die-casting. In terms of weight percentage, the chemical composition of the alloy is: Ba: 0.6wt.%, Re: 0.5wt.%; Te: 0.6wt.%, Ge: 2.8wt.%, V: 0.6wt.%, Pr: 0.3wt.% .%, the balance is zinc. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 490 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 490 degrees for 10 minutes, it is cast into the same level equipment as the hot top for semi-continuous casting into the required square and round ingots. The ingot moving speed is 18m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare zinc-barium alloy castings with complex shapes; the final heat treatmen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high temperature-resistant Ba-Re-Te zinc alloy applied to cold chamber die casting and a processing process thereof. The alloy is prepared from the following components in percentage by weight: 0.4-1.2wt% of Ba, 0.4-0.8wt% of Re, 0.6-0.8wt% of Te, 2.0-4.0wt% of Ge, 0.5-0.8wt% of V, 0.2-0.4wt% of Pr and the balance of zinc. The zinc-barium alloy has excellent die-casting performance and can be used for producing long thin-walled parts; meanwhile, in the die casting process, the zinc-barium alloy can be casted by using cold chamber; the production efficiency is greatlyimproved; the energy consumption is reduced; the obtained products can be widely used in electric appliance manufacturing industry and radio industry.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a zinc-barium alloy. Background technique [0002] In our country, zinc is one of the main metals that are focused on the development of non-ferrous metal industry. my country's zinc resource reserves are very rich, and it can also be exported in large quantities while meeting domestic demand. And replacing copper alloy and aluminum alloy with zinc alloy is of great significance in terms of saving energy, reducing material costs and rationally allocating domestic resources. With the continuous emergence of new die-casting technology, die-casting parts are no longer limited to the automobile industry and instrument industry, but gradually expanded to industries such as electronics industry and daily hardware. The main uses of zinc alloy castings in my country are toys (car models), daily hardware (handles, locks, sanitary ware), zippers, instrument parts and wear-resistant parts ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C18/00C22C1/02C22F1/16C22F1/02
CPCC22C18/00C22C1/02C22F1/02C22F1/165
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products