Preparation method of multifunctional sanitary-fitting hardware

A hardware and multi-functional technology, applied in the field of hardware, can solve the problems of not being able to adapt to the high requirements of elongation at break and flexural modulus, and achieve the effects of preventing moisture inflow, efficient control, and enhanced cooling effect

Inactive Publication Date: 2018-09-14
南京思甲宁新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0023] In order to solve the above problems, the present invention provides a method for preparing multi-functional sanitary hardware, which effectively avoids the failure of sanitary hardware with an elongation at break of less than 4.1% and a flexural modulus of less than 5900 MPa in the prior art. Defects that are suitable for occasions that require high elongation at break and flexural modulus

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of multifunctional sanitary-fitting hardware
  • Preparation method of multifunctional sanitary-fitting hardware
  • Preparation method of multifunctional sanitary-fitting hardware

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] like Figure 1-Figure 5 As shown, the preparation method of multifunctional sanitary ware hardware includes the following steps:

[0051] Step a, the wollastonite that is 12 parts by weight, the aluminum hydroxide that is 4 parts by weight, the 3-glycidyl etheroxypropyl trimethoxysilane that is 0.02 part by weight, the parts by weight 0.08 parts of N-aminoethyl-γ-aminopropyltriethoxysilane and 0.02 parts by weight of N-(β-aminoethyl)-γ-aminopropyltrimethyl(ethyl)oxysilane Pour into the 3-glycidyloxypropyltrimethoxysilane, N-aminoethyl-γ-aminopropyltriethoxysilane and N-(β-aminoethyl)-γ-aminopropyl In the acetone of 6 times of the total mass of trimethyl (ethyl) oxysilane, then the mica powder that is 10 parts by weight is also put into the acetone, the acetone is removed through the heater, and then the wollastonite and hydroxide after the acetone removal are removed Aluminum, 3-glycidyloxypropyltrimethoxysilane, N-aminoethyl-γ-aminopropyltriethoxysilane, N-(β-aminoet...

Embodiment 2

[0075] The preparation method of multifunctional sanitary ware hardware includes the following steps:

[0076] Step a, the wollastonite that is 18 parts by weight, the aluminum hydroxide that is 4-6 parts by weight, the 3-glycidyl etheroxypropyl trimethoxysilane that is 0.09 part by weight, weight Parts are 0.16 parts of N-aminoethyl-γ-aminopropyltriethoxysilane and 0.09 parts by weight of N-(β-aminoethyl)-γ-aminopropyltrimethyl (ethyl)oxy The 3-glycidyloxypropyltrimethoxysilane, N-aminoethyl-γ-aminopropyltriethoxysilane and N-(β-aminoethyl)-γ-ammonia Propyl trimethyl (ethyl) oxysilane in acetone with 6 times the total mass, then put mica powder that is 13 parts by weight into the acetone, remove the acetone through the heater, then remove the wollastonite, Aluminum hydroxide, 3-glycidyloxypropyltrimethoxysilane, N-aminoethyl-γ-aminopropyltriethoxysilane, N-(β-aminoethyl)-γ-aminopropyl Trimethyl(ethyl)oxysilane and mica powder are crushed by a closed crusher to obtain crushe...

Embodiment 3

[0100] The preparation method of multifunctional sanitary ware hardware includes the following steps:

[0101] Step a, the wollastonite that is 24 parts by weight, the aluminum hydroxide that is 6 parts by weight, the 3-glycidyl etheroxypropyl trimethoxysilane that is 0.16 part by weight, the parts by weight 0.24 parts of N-aminoethyl-γ-aminopropyltriethoxysilane and 0.16 parts by weight of N-(β-aminoethyl)-γ-aminopropyltrimethyl(ethyl)oxysilane Pour into the 3-glycidyloxypropyltrimethoxysilane, N-aminoethyl-γ-aminopropyltriethoxysilane and N-(β-aminoethyl)-γ-aminopropyl In the acetone of 6 times of the total mass of trimethyl(ethyl)oxysilane, then the mica powder that is 10-16 parts by weight is also put into the acetone, the acetone is removed through the heater, and then the wollastonite, Aluminum hydroxide, 3-glycidyloxypropyltrimethoxysilane, N-aminoethyl-γ-aminopropyltriethoxysilane, N-(β-aminoethyl)-γ-aminopropyl Trimethyl(ethyl)oxysilane and mica powder are crushed b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of multifunctional sanitary-fitting hardware. The preparation method includes checking the soaking state of dehumidifying sponge on a surface layer, and removing liquid in the dehumidifying sponge by dehumidifying agents to obtain smashed particles, wherein the dehumidifying sponge is kept in a water-free state during continuous operation of the dehumidifying agents; step b, evenly blending, by weight, 6-12 parts of unsaturated polyester resin, 4-6 parts of polyester-type anti-shrinkage agents, 8-22 parts of reinforced fibers and the smashed particles in a blending machine for 0.03-0.06 hour to obtain a blended material. The preparation method has the advantages that the defects that sanitary-fitting hardware in the prior art cannot adapt to sites with high requirements on elongation-at-break and flexural modulus since its elongation-at-break is lower than 4.1% and its flexural modulus is lower than 5900MPa, and components of server cases are damaged ceaselessly due to high humidity therein are avoided effectively.

Description

technical field [0001] The invention relates to the technical field of hardware, in particular to a method for preparing multifunctional sanitary ware hardware. Background technique [0002] The shells of various kitchen and bathroom faucets that were commonly used in the past were made of copper-zinc alloy materials, which were sand-cast and formed, then polished and polished, and then electroplated. There were cumbersome procedures and low production efficiency. , the cost is high; finally, the current production of sanitary ware hardware needs to melt the metal and then cast it, which belongs to the field of high energy consumption and high carbon emission, especially for the energy saving and emission reduction required by today's society. [0003] So there is the currently commonly used sanitary ware hardware with the application number 201410585760.3, the application date is 2014.10.28, and the patent name is "a resin-based composite sanitary ware hardware and its prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/06C08L77/00C08L67/00C08K13/04C08K7/14C08K3/34C08K3/22C08J5/04
CPCC08J5/043C08J5/046C08J2367/06C08J2467/00C08J2477/00C08K3/34C08K2003/2227
Inventor 时伟
Owner 南京思甲宁新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com