Resourceful treatment method for recycled waste powder from asphalt concrete mixing station

A technology for asphalt concrete and a treatment method, which is applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problem of not suitable for the treatment of recycled waste powder in an asphalt concrete mixing station, with many formula components and high treatment costs. problems, to minimize economic costs, increase economic benefits, improve elastic modulus and overall flexibility

Active Publication Date: 2018-09-25
武汉市江夏路桥工程有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this solution has many ingredients and high processing costs, so it is not suitable for ordinary road construction companies to process waste powder recovered from asphalt concrete mixing plants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for recycling waste powder from asphalt concrete mixing plants, which is carried out according to the following steps: by mass percentage, weigh 4.5% of PCSB curing agent, 20% of asphalt waste powder, 45.5% of fine aggregate, and 30% of coarse aggregate , add water to stir and mix. During the mixing process, the water content is controlled to account for 8.0% of the weight of the mixture. The time from mixing and discharging to the end of molding is ≤4h. Paving or pouring to preset specifications, wet water curing for 7 days, its compressive strength ≥5.5MPa, which meets the requirements of 5.0MPa~7.0MPa for the strength of the base layer of the super-heavy and extremely heavy traffic standard road surface of high-grade highways.

[0029] Wherein, the fine aggregate is stone chips with a particle size of ≤5 mm, and the coarse aggregate is gravel with a particle size of 5-10 mm.

[0030] The asphalt waste powder used is waste powder produced by Lingshan Asphalt ...

Embodiment 2

[0032] A method for recycling waste powder from asphalt concrete mixing plants, which is carried out according to the following steps: by mass percentage, weigh 3.5% of PCSB curing agent, 20% of asphalt waste powder, 46.5% of fine aggregate, and 30% of coarse aggregate , add water to stir and mix. During the mixing process, the water content is controlled to account for 9% of the weight of the mixture. The time from mixing and mixing to the end of molding is ≤4h. Paving or pouring to preset specifications, wet water curing for 7 days, its compressive strength ≥4.0MPa, which meets the requirement of 3.0MPa~5.0MPa for the strength of the sub-base layer of the super-heavy and extremely heavy traffic standard road surface of high-grade highways.

[0033] Wherein, the fine aggregate is stone chips with a particle size of ≤5 mm, and the coarse aggregate is gravel with a particle size of 5-10 mm.

[0034] The waste powder produced by the Wuhan Jiangxia Road and Bridge Engineering Cor...

Embodiment 3

[0036] A method for recycling waste powder from asphalt concrete mixing plants, which is carried out according to the following steps: by mass percentage, weigh 2.5% of PCSB curing agent, 17.5% of asphalt waste powder, 48.5% of fine aggregate, and 31.5% of coarse aggregate , add water to stir and mix. During the mixing process, the moisture content is controlled to account for 5% of the weight of the mixture. The time from mixing and discharging to the end of molding is ≤4h. Paving or pouring to preset specifications, wet water curing for 7 days, its compressive strength ≥4.5MPa, which meets the requirements of 3.0MPa~5.0MPa for the strength of the subbase layer of the super-heavy and extremely heavy traffic standard road surface of high-grade highways.

[0037] Wherein, the fine aggregate is stone chips with a particle size of ≤5 mm, and the coarse aggregate is gravel with a particle size of 5-10 mm.

[0038] The gray waste powder produced by the Lingshan Asphalt Concrete Mixin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
hydration enthalpyaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a resourceful treatment method for recycled waste powder from an asphalt concrete mixing station. The resourceful treatment method is characterized by comprising the following steps: 1) weighing, by mass, 2 to 8% of a PCSB curing agent, 15 to 25% of waste asphalt powder, 35 to 50% of fine aggregate and 25 to 35% of coarse aggregate, summing to 100%; 2) adding water into theweighed components, carrying out mixing to form a mixture, and controlling water content to be 5 to 10%; and 3) subjecting the mixture to rolling or compaction molding to form a preset specification and carrying out wet water maintenance for 5 to 10 d. The method provided by the invention can treat recycled waste powder from the asphalt concrete mixing station to form a base material for a road pavement, so environmental pollution is reduced, economic benefits are increased, and construction cost for a pavement base is lowered.

Description

technical field [0001] The invention belongs to the field of waste recycling, and in particular relates to a resource treatment method for recycling waste powder in an asphalt concrete mixing plant. Background technique [0002] During the asphalt concrete mixing process, 8-10 tons of waste powder will be produced for every 100 tons of asphalt concrete produced, which is the waste powder recovered from the asphalt concrete mixing plant (referred to as asphalt waste powder) in the present invention. This kind of asphalt waste powder is some very fine powder, most of which have a particle size of ≤0.075mm and have no direct use value. According to an incomplete survey, there are more than 20 asphalt mixing plants in Wuhan and its surrounding areas, which generate 800,000 to 1,000,000 tons of asphalt waste every year. There are more than 1,000 asphalt concrete mixing plants in the country, and tens of millions of tons of asphalt waste powder are produced every year. Over the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B18/16
CPCC04B18/16C04B28/10C04B2201/50C04B14/06C04B14/303C04B22/06C04B22/066C04B14/308C04B24/24C04B22/00C04B18/12Y02W30/91
Inventor 彭锦红徐世红周翔周晓华陈洁刘军文强周恒胡德富覃青林文丕珍
Owner 武汉市江夏路桥工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com