HMX-based boraxal-containing explosive

A technology of explosives and boron-aluminum, which is applied in the field of HMX-based boron-containing aluminum explosives, can solve the problems of large increase in mechanical sensitivity, failure to meet the safety requirements of metallized explosives, increase in mechanical sensitivity, etc., and achieve the effect of reducing shape defects

Inactive Publication Date: 2018-10-19
INST OF CHEM MATERIAL CHINA ACADEMY OF ENG PHYSICS
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, when metal powder is added to the energetic material, its mechanical sensitivity increases, especially when aluminum powder, boron powder and B-Al composite powder are added to the system composed of HMX, AP and binder, the mechanical sensitivity increases more than Large, unable to meet the safety requirements of metallized explosives in the process of preparation and processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HMX-based boraxal-containing explosive
  • HMX-based boraxal-containing explosive
  • HMX-based boraxal-containing explosive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The HMX-based boron-containing aluminum explosive of the present invention is composed of 60% to 68% of HMX content, 15% to 25% of B-Al composite powder content, and 14% to 18% of binder content. The mass ratio of B powder and Al powder in B-Al composite powder is 1:1.

[0014] B powder uses a diameter of 1μm~5μm; B powder is prepared by boric acid thermal decomposition method; Al powder uses spherical particles with a diameter of 1μm~5μm, which are prepared by melting, spraying, cooling and airflow classification; Boron aluminum composite powder, prepared by ball milling , Coating boron powder on the surface of spherical Al powder, the diameter of the B-Al composite powder particles is 1µm~10µm.

[0015] The scanning electron microscope morphology of the B-Al composite powder of the explosive of the present invention is shown figure 1 . The particle size of B-Al composite powder is 1µm~10µm, the aluminum powder is spherical, and the surface is covered with many small-sized...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to HMX-based boraxal-containing explosive. The explosive is prepared from the following various ingredients in percentage by patent: 60-68% of HMX, 15-25% of B-A1 composite powder and 14-18% of bonding agent, wherein the mass ratio of powder B to powder Al in the B-A1 composite powder is 1:1. The explosive can be used as the main charge of high-strength and high-security ammunition.

Description

Technical field [0001] The invention relates to the field of energetic materials, in particular to an HMX-based boron-containing aluminum explosive with enhanced aftereffect function. Background technique [0002] The application of active metals in energetic materials can quickly and effectively improve its functional power and explosive power. In the past, the most researched was aluminum powder. The results of the study show that aluminum powder can effectively increase the energy of explosives and enhance the thermal effect of explosives. Many elements in the periodic table are combustible. Aluminum powder is not the material with the highest calorific value among metal combustibles. Boron powder has higher mass and volumetric heat of combustion than aluminum powder, but boron powder has a higher calorific value than aluminum powder. With high combustion temperature, the energy released by the oxidation of aluminum powder can increase the oxidation efficiency of boron powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C06B27/00C06D5/06
CPCC06B27/00C06D5/06
Inventor 高大元郑保辉宋清官李兴隆肖春路中华
Owner INST OF CHEM MATERIAL CHINA ACADEMY OF ENG PHYSICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com