A kind of tobacco humectant, its preparation method and application

A moisturizing agent, tobacco technology, applied in the direction of tobacco, tobacco processing, tobacco preparation, etc., to achieve the effects of improving moisturizing quality and stability, reducing irritation, and improving aftertaste

Active Publication Date: 2021-01-29
CHINA TOBACCO YUNNAN IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Metal-organic frameworks or MOFs (the abbreviation of the English name Metal organic Framework) materials have a large adsorption capacity, and there is no report on the use of MOFs materials in tobacco

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of tobacco humectant, its preparation method and application
  • A kind of tobacco humectant, its preparation method and application
  • A kind of tobacco humectant, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Preparation of tobacco humectant Uio-66 by solvothermal method:

[0036] 15mmol anhydrous ZrCl 4 Put it into a beaker, add 30ml of N,N'-dimethylamide, and then perform ultrasonic treatment for 30 minutes until it is completely dissolved. Add 15mmol terephthalic acid and 60ml N,N'-dimethylamide into the above solution, and continue to sonicate for 30 minutes until completely dissolved. The above mixed solution was transferred into a polytetrafluoroethylene reactor and reacted at 120°C for 24h. Filter out the solid product, wash it with 20ml of 60°C ethanol, dry it, transfer it to a conical flask, add 30ml N,N'-dimethylamide and stir to remove unreacted ligand. The above-mentioned product was filtered out, washed with 20ml of ethanol, dried and transferred to a reaction kettle, and then dried in an oven at 90°C for 12 hours. The solid product was obtained by centrifugation, and was centrifugally washed twice with 20 ml of ethanol and twice with 20 ml of acetone, and th...

Embodiment 2

[0037] Embodiment 2: Preparation of tobacco humectant Uio-66-NH by solvothermal method 2

[0038] 18mmol anhydrous ZrCl 4Put it into a beaker, add 30ml of N,N'-dimethylamide, and then perform ultrasonic treatment for 30 minutes until it is completely dissolved. Add 14mmol of 2-amino-terephthalic acid and 50ml of N,N'-dimethylamide into the above solution, and continue ultrasonic treatment for 30 minutes. The above mixed solution was transferred into a polytetrafluoroethylene reactor and reacted at 120°C for 24h. Filter out the solid product, wash it with 20ml of 60°C ethanol, dry it, transfer it to a conical flask, add 30ml N,N'-dimethylamide and stir to remove unreacted ligand. The above-mentioned product was filtered out, washed with 20ml of ethanol, dried and transferred to a reaction kettle, and then dried in an oven at 90°C for 12 hours. The solid product was obtained by centrifugation, and was centrifugally washed twice with 20 ml of ethanol and twice with acetone, a...

Embodiment 3

[0040] Embodiment 3: the mensuration of the dynamic content of moisture added in tobacco by tobacco humectant Uio-66

[0041] Dissolve the tobacco humectant Uio-66 prepared in Example 1 in a mixed solvent of 1,2-propanediol and glycerin, and add it to shredded tobacco according to the amount of humectant at 0.2%, so as to add an equal amount of alcohol mixed solvent but not Cut tobacco samples containing humectant Uio-66 were used as blank control. Then the shredded tobacco sample was placed in a DVS dynamic moisture adsorption instrument with a temperature of 22° C. and a relative humidity of RH46%, to measure the dynamic moisture content. The results are shown in Table 1 and Figure 4 shown. from Figure 4 It can be seen that the adsorption-desorption curve of Uio-66 has a large adsorption hysteresis. Under a certain pressure, it has a certain degree of adsorption and retention of water, and the maximum adsorption capacity can reach 14%, which has a good water adsorption ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tobacco humectant, which is Zr 4+ A metal-organic framework material with a three-dimensional structure obtained by self-assembly with terephthalic acid or 2-aminoterephthalic acid; Zr 4+ The three-dimensional metal-organic framework material self-assembled with terephthalic acid is Uio‑66, Zr 4+ The three-dimensional metal-organic framework material self-assembled with 2-aminoterephthalic acid is Uio-66-NH 2 . The invention also discloses the preparation method of the tobacco humectant and its application in tobacco.

Description

technical field [0001] The invention belongs to the field of tobacco additives, and in particular relates to a tobacco humectant, its preparation method and application. Background technique [0002] Tobacco leaf is a loose and porous material, and from a thermodynamic point of view, it has a high potential for absorbing moisture. Just because it is a porous material, free moisture, capillary moisture, etc. will be lost faster at higher temperature and lower humidity, so that cigarettes are also easy to dry. In the production process of cigarette products, the addition of humectant can maintain the moisture of cut tobacco and improve its physical moisturizing performance. [0003] At present, commonly used humectants are polyols such as propylene glycol, glycerin, diethylene glycol, and sorbitol. However, these humectants are unsatisfactory in improving the sensory quality of cigarettes. Therefore, a new type of humectant is needed to replace the traditional humectant, re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A24B15/30
CPCA24B15/30B01J20/226C07F7/003B01J20/3085B01J20/3071A24B9/00A24B3/02A24B3/04C07F7/00
Inventor 韩敬美郑绪东李航星尚善斋王汝雷萍李志强王程娅孙志勇汤建国陈永宽
Owner CHINA TOBACCO YUNNAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap