A kind of regenerated cellulose pellet containing flaky nano ZNO and its preparation method

A technology for regenerating cellulose and cellulose fibers, used in chemical instruments and methods, physical/chemical process catalysts, organic compound/hydride/coordination complex catalysts, etc. problems such as poor friendliness, to achieve the effect of clean and environmentally friendly preparation process, improving high-value utilization, and improving difficult recycling

Active Publication Date: 2020-08-18
NANJING FORESTRY UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, commonly used inorganic carriers include silica, diatomaceous earth, alumina, carbon materials, etc. Inorganic carriers have the characteristics of high density (generally only suitable for fixed bed reactors), which limits their application in photocatalytic engineering; Organic polymer carriers include polyethylene, etc., which have a low density and are not only suitable for fixed-bed reactors, but also for suspended-bed reactors. However, petroleum-based polymers are not easy to degrade and regenerate, and have poor environmental friendliness. Usage requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of regenerated cellulose pellet containing flaky nano ZNO and its preparation method
  • A kind of regenerated cellulose pellet containing flaky nano ZNO and its preparation method
  • A kind of regenerated cellulose pellet containing flaky nano ZNO and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 2g of wood pulp cellulose fibers were added to 100g of 65% (wt%) ZnCl 2 In aqueous solution, pretreatment in a low-temperature bath at 0°C for 3 hours. The above liquid-solid material was placed in a water bath at 60° C. and heated and stirred to obtain a transparent and uniform cellulose solution. Use a syringe to dissolve the ZnCl of cellulose 2 The aqueous solution was injected into a 50% NaOH aqueous solution in the form of pellets, and left to stand for 24 hours. Filter the pellet and wash the pellet with distilled water to be free of C1 - , put it in an ultra-low temperature refrigerator, and put the sample in a freeze dryer after freezing. After drying, a new material of regenerated cellulose pellets containing flaky nano-ZnO was obtained. The characterization results are as follows Figure 1~5 shown. Depend on figure 1 It can be seen that the diameter of the pellets is 2-4 mm. Depend on figure 2 It can be seen that the surface of the pellet is network-li...

Embodiment 2

[0029] 2g of wood pulp cellulose fibers were added to 80g of 65% (wt%) ZnCl 2 In aqueous solution, pretreatment in a low-temperature bath at -10°C for 4 hours. The above liquid-solid material was placed in a water bath at 70° C. and heated and stirred to obtain a transparent and uniform cellulose solution. Use a syringe to dissolve the ZnCl of cellulose 2 The aqueous solution was injected into a 50% NaOH aqueous solution in the form of pellets, and left to stand for 26 hours. Filter the pellet and wash the pellet with distilled water until Cl-free - , put it in an ultra-low temperature refrigerator, and place the sample in a freeze dryer after freezing. After drying, a new material of regenerated cellulose pellets containing flaky nano ZnO is obtained. The diameter of the small ball is 2-4mm, and the thickness of the ZnO nanosheet is about 20-50nm.

Embodiment 3

[0031] 2g bamboo pulp cellulose fiber is added to the ZnCl of 60g 70% (wt%) 2 In aqueous solution, pretreatment in a low-temperature bath at 20°C for 4 hours. The above liquid-solid material was placed in a water bath at 60° C. and heated and stirred to obtain a transparent and uniform cellulose solution. Use a syringe to dissolve the ZnCl of cellulose 2 The aqueous solution was injected into a 50% NaOH aqueous solution in the form of pellets, and allowed to stand for 18 hours. Filter the pellet and wash the pellet with distilled water until Cl-free - , put it in an ultra-low temperature refrigerator, and place the sample in a freeze dryer after freezing. After drying, a new material of regenerated cellulose pellets containing flaky nano ZnO is obtained. The diameter of the small ball is 2-4mm, and the thickness of the ZnO nanosheet is about 20-50nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A regenerated cellulose pellet containing sheet nanometer ZnO inside and a preparing method thereof are disclosed. In the regenerated cellulose pellet that is a novel material, the thickness of ZnO nanosheets is 20-50 nm, and the diameter of the regenerated cellulose pellet is 2-4 mm. The method includes subjecting dissolved cellulose fibers, as a raw material, to low-temperature pretreatment, dissolving, injection for pellet formation, in-situ synthesis and freeze-drying to prepare the regenerated cellulose pellet containing sheet nanometer ZnO inside, with an aqueous ZnCl2 solution being adopted as a solvent for the cellulose and a zinc source of nanometer ZnO. The material is easy to recover and high in practicability.

Description

technical field [0001] The invention belongs to the technical field of new cellulose materials, and in particular relates to a new material of regenerated cellulose pellets containing flaky nano ZnO and a preparation method thereof. Background technique [0002] Compared with traditional sewage treatment technology, photocatalytic technology has the advantages of high efficiency, energy saving, easy operation, simplified process, clean and non-toxic, and no secondary pollution. Some commonly used photocatalytic materials are mainly semiconductor materials, and nano-ZnO is one of the materials with broad application prospects. However, it is difficult to recycle in application, so it needs to be compounded with a certain carrier to improve its utilization efficiency. [0003] At present, commonly used inorganic carriers include silica, diatomaceous earth, alumina, carbon materials, etc. Inorganic carriers have the characteristics of high density (generally only suitable for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/26B01J35/08C02F1/32
CPCB01J31/26B01J35/004B01J35/08C02F1/32C02F2305/10
Inventor 李小保周小龙高亚年张雪李力成叶菊娣
Owner NANJING FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com