A kind of regenerated cellulose pellet containing flower-shaped nano zno and its preparation method

A technology for regenerated cellulose and cellulose fibers, applied in chemical instruments and methods, physical/chemical process catalysts, organic compounds/hydrides/coordination complex catalysts, etc. Poor friendliness and other issues, to achieve clean and environmentally friendly preparation process, improve high-value utilization, and improve the effects of difficult recycling

Active Publication Date: 2020-08-18
NANJING FORESTRY UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, commonly used inorganic carriers include silica, diatomaceous earth, alumina, carbon materials, etc. Inorganic carriers have the characteristics of high density (generally only suitable for fixed bed reactors), which limits their application in photocatalytic engineering; Organic polymer carriers include polyethylene, etc., which have low density and are not only suitable for fixed-bed reactors, but also for suspended-bed reactors, but petroleum-based polymers are not easy to degrade and regenerate, and have poor environmental friendliness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of regenerated cellulose pellet containing flower-shaped nano zno and its preparation method
  • A kind of regenerated cellulose pellet containing flower-shaped nano zno and its preparation method
  • A kind of regenerated cellulose pellet containing flower-shaped nano zno and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 2g of wood pulp cellulose fibers were added to 100g of 70% (wt%) ZnCl 2 In aqueous solution, pretreatment in a low-temperature bath at 0°C for 3 hours. The above liquid-solid material was placed in a water bath at 70° C. and heated and stirred to obtain a transparent and uniform cellulose solution. Use a syringe to dissolve the ZnCl of cellulose 2 The aqueous solution was injected into a 50% NaOH aqueous solution in the form of pellets, and allowed to stand for 12 hours. Filter the pellet and wash the pellet with distilled water until Cl-free - , put it into an ultra-low temperature refrigerator, and put the sample in a freeze dryer after freezing. After drying, a new material of regenerated cellulose pellets containing flower-like nano-ZnO was obtained. The characterization results are as follows Figure 1-6 shown. Depend on figure 1 It can be seen that the diameter of the pellets is 2-4 mm. Depend on figure 2 It can be seen that the surface of the pellet is ne...

Embodiment 2

[0029] 2g of wood pulp cellulose fibers were added to 60g of 65% (wt%) ZnCl 2 In aqueous solution, pretreatment in a low-temperature bath at -10°C for 4 hours. The above liquid-solid material was placed in a water bath at 70° C. and heated and stirred to obtain a transparent and uniform cellulose solution. Use a syringe to dissolve the ZnCl of cellulose 2 The aqueous solution was injected into a 50% NaOH aqueous solution in the form of pellets, and allowed to stand for 14 hours. Filter the pellet and wash the pellet with distilled water until Cl-free - , put it in an ultra-low temperature refrigerator, and place the sample in a freeze dryer after freezing. After drying, a new material of regenerated cellulose pellets containing flower-shaped nano ZnO is obtained. The diameter of the ball is 2-4mm, and the thickness of the petal is about 100-200nm.

Embodiment 3

[0031] 2g of cotton pulp cellulose fibers were added to 120g of 65% (wt%) ZnCl 2 In aqueous solution, pretreatment in a low-temperature bath at -10°C for 4 hours. The above liquid-solid material was placed in a water bath at 80° C. and heated and stirred to obtain a transparent and uniform cellulose solution. Use a syringe to dissolve the ZnCl of cellulose 2 The aqueous solution was injected into a 50% NaOH aqueous solution in the form of pellets and allowed to stand for 16 hours. Filter the pellet and wash the pellet with distilled water until Cl-free - , put it in an ultra-low temperature refrigerator, and place the sample in a freeze dryer after freezing. After drying, a new material of regenerated cellulose pellets containing flower-shaped nano ZnO is obtained. The diameter of the ball is 2-4mm, and the thickness of the petal is about 100-200nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a regenerated cellulose microsphere containing flower-like nanometer ZnO and a preparation method thereof. According to the novel regenerated cellulose microsphere, the thickness of petaline nanometer ZnO is 100-200 nm, and the diameter of the regenerated cellulose microsphere is 2-4 mm. According to the preparation method, a ZnCl2 water solution is adopted as a solvent forcellulose and a zinc source of nanometer ZnO, and dissolving pulp cellulose fibers are adopted as the raw materials of cellulose and subjected to low-temperature pretreatment, dissolution, injectioninto a ball shape, in-situ synthesis and freeze drying to prepare the regenerated cellulose microsphere containing flower-like nanometer ZnO. A preparation process is clean, environmentally friendly and capable of saving energy; through in-situ synthesis, the regenerated cellulose microsphere containing flower-like nanometer ZnO is prepared without a hydrothermal reaction or heating, flower-like nanometer ZnO is mainly distributed in the regenerated cellulose microsphere and cannot shed, and the regenerated cellulose microsphere has wide application in light-catalyzed reactions.

Description

technical field [0001] The invention belongs to the technical field of new cellulose materials, and in particular relates to a new material of regenerated cellulose pellets containing flower-shaped nano ZnO and a preparation method thereof. Background technique [0002] Compared with traditional sewage treatment technology, photocatalytic technology has the advantages of high efficiency, energy saving, easy operation, simplified process, clean and non-toxic, and no secondary pollution. Some commonly used photocatalytic materials are mainly semiconductor materials, and nano-ZnO is one of the materials with broad application prospects. However, it is difficult to recycle in application, so it needs to be compounded with a certain carrier to improve its utilization efficiency. [0003] At present, commonly used inorganic carriers include silica, diatomaceous earth, alumina, carbon materials, etc. Inorganic carriers have the characteristics of high density (generally only suita...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/26B01J35/08C02F1/32
CPCB01J31/26B01J35/004B01J35/08C02F1/32C02F2305/10
Inventor 李小保高亚年周小龙张雪李力成叶菊娣
Owner NANJING FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com