Pre-hydrated mineral powder nanocrystalline nucleus early strengthening agent for steam-curing concrete and preparation method thereof

A prehydration and nanocrystalline technology, applied in the field of concrete admixtures, can solve problems such as failure to meet early strength requirements, slow cement hydration speed, and low activity, so as to improve production efficiency, early strength, and process simple effect

Active Publication Date: 2018-12-14
WUHAN UNIV OF TECH
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the activity of slag is too low, it takes a long time from its activity being stimulated to participating in hydration and forming a strong hydration product, so the hydration r

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pre-hydrated mineral powder nanocrystalline nucleus early strengthening agent for steam-curing concrete and preparation method thereof
  • Pre-hydrated mineral powder nanocrystalline nucleus early strengthening agent for steam-curing concrete and preparation method thereof
  • Pre-hydrated mineral powder nanocrystalline nucleus early strengthening agent for steam-curing concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] In order to enable those skilled in the art to better understand the technical solution of the present invention, the present invention will be further described in detail below in conjunction with examples.

[0016] Example 1-5

[0017] Prepare the prehydrated mineral powder nano crystal nucleus early strength agent for steam-cured concrete, the specific steps are as follows:

[0018] Mineral powder (particle size ≤ 20μm, mainly containing CaO, SiO 2 、Al 2 o 3 , MgO, Fe 2 o 3 ), the surface modifier and water are put into the ball mill tank in proportion, and the zirconia grinding body is added. Ball milling for 30 minutes, stop for 10 minutes, recorded as one cycle, use laser particle size analyzer to test particle size distribution, repeat ball milling for 3-5 cycles, until the median particle size of the ball milled powder is 200-400nm, obtained for steam curing Prehydrated mineral powder nano crystal nucleus early strength agent for concrete.

[0019] The pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a pre-hydrated mineral powder nanocrystalline nucleus early strengthening agent for steam-curing concrete and a preparation method thereof. The early strengthening agent comprises, by mass, 20-30% of mineral powder, 2-3% of a surface modifier and 67-78% of deionized water. The surface modifier is a mixed solution containing a carboxylic acid-sulfonic acid polymer, a polycarboxylic acid water reducing agent and white sugar dissolved in water at a mass ratio of 1-3: 1-3: 1. The pre-hydrated mineral powder nanocrystalline nucleus early strengthening agent for steam-curingconcrete has strong induction effects on cement under steam-curing conditions. The early strengthening agent in a use ratio of 0.5-1.0% can improve the strength of ordinary Portland cement mortar by55-68% through steam-curing at 60 DEG C for 8h so that the early strength of steam-cured prefabricated components is significantly improved and the mold turnaround efficiency is improved. The early strengthening agent can be widely used in the steam-cured prefabricated component industry, greatly improve production efficiency and reduce energy consumption of the unit product.

Description

technical field [0001] The invention belongs to the technical field of concrete admixtures, and in particular relates to a prehydrated mineral powder nano crystal nucleus early strength agent for steam-cured concrete and a preparation method thereof. Background technique [0002] my country's slag is the highest output of all industrial by-products, about 30 million tons per year. The slag finely ground slag is a polymer composed of glass phase and crystal phase. The crystal phase wraps the glass phase. The former is an inert component. Chemically very inactive, the latter is potentially reactive and hydraulically hard. Adding mineral powder to concrete as a concrete mineral admixture can reduce the cost of concrete and improve the durability and impermeability of concrete. [0003] During the hydration process of general mineral powder cement, because mineral powder replaces a part of cement clinker, the relative content of clinker that can participate in hydration in the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/16
CPCC04B40/0039C04B24/163C04B24/10C04B18/12C04B2103/302C04B28/04
Inventor 谭洪波邓秀峰张迅贺行洋苏英
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap