Special novel material for TPU leg guard plate, and preparation method thereof

A leg shield, a new type of technology, applied in the field of sports equipment, can solve the problems affecting the speed of athletes, the shield is bulky, easy to sweat, etc., and achieve the effects of impact resistance, prolonging the service life, and convenient coloring

Inactive Publication Date: 2018-12-18
江苏绿艳高分子材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In ball sports, especially in football, leg guards are essential protective gear. Football players sweat a lot, and their body temperature rises, so they need to cool down, and the collision of limbs, especially legs, during sports It is essential, so it is necessary to wear leg guards for protection, and most of the guards are bulky and affect the speed of athletes, so there is a need for a leg guard that is light in weight, high in hardness, and can reduce body temperature and quickly absorb sweat.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special novel material for TPU leg guard plate, and preparation method thereof
  • Special novel material for TPU leg guard plate, and preparation method thereof
  • Special novel material for TPU leg guard plate, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] 1. Weigh 20% by weight of PEA-1800; 3% by weight of 1,4-BDO; 1% by weight of 1,3-BDO; 24% by weight of MDI; Resin; 6% by weight of titanium oxide; 20% by weight of bamboo fiber; 0.2% by weight of antioxidant; 6% by weight of reinforcing agent.

[0045] 2. Put 1,4-BDO, 1,3-BDO and PEA-2000 in the No. 1 reaction kettle, stir and mix evenly at a constant speed, then add polymer water-absorbent resin, titanium oxide, bamboo fiber, antioxidant and reinforcement agent, the temperature is set at 80°C; MDI is placed in the No. 2 reactor, and the set temperature is 75°C;

[0046] 3. When the temperature is stable, it is mixed through the high-speed rotating mixing head with a perfusion metering system, so that the molecules of various raw materials are fully collided and mixed, and then flow into the conveyor belt equipped with a ripening plate, and then pass through the drying tunnel equipped with 10 sections of oven. The oven temperature is set The heating temperature is set ...

Embodiment 2

[0050] 1. Weigh 38% by weight of PEA-1800; 6% by weight of 1,4-BDO; 1% by weight of 1,3-BDO; 38% by weight of MDI; Resin; 8% by weight of titanium oxide; 30% by weight of bamboo fiber; 0.4% by weight of antioxidant; 8% by weight of reinforcing agent.

[0051] 2. Put 1,4-BDO, 1,3-BDO and PEA-2000 in the No. 1 reaction kettle, stir and mix evenly at a constant speed, then add polymer water-absorbent resin, titanium oxide, bamboo fiber, antioxidant and reinforcement agent, the temperature is set at 90°C; MDI is placed in the No. 2 reactor, and the set temperature is 85°C;

[0052] 3. When the temperature is stable, it is mixed through a high-speed rotating mixing head with a perfusion metering system, so that the molecules of various raw materials are fully collided and mixed, and then flow into the conveyor belt equipped with a ripening plate, and then pass through the drying tunnel equipped with 14 sections of ovens. The oven temperature is set The heating temperature is set at ...

Embodiment 3

[0056] 1. Weigh 30% by weight of PEA-1800; 5% by weight of 1,4-BDO; 1% by weight of 1,3-BDO; 28% by weight of MDI; Resin; 7% by weight of titanium oxide; 26% by weight of bamboo fiber; 0.3% by weight of antioxidant; 7% by weight of reinforcing agent.

[0057] 2. Put 1,4-BDO, 1,3-BDO and PEA-2000 in the No. 1 reaction kettle, stir and mix evenly at a constant speed, then add polymer water-absorbent resin, titanium oxide, bamboo fiber, antioxidant and reinforcement agent, the temperature is set at 85°C; MDI is placed in the No. 2 reactor, and the set temperature is 80°C;

[0058] 3. When the temperature is stable, it is mixed through the high-speed rotating mixing head with a perfusion metering system, so that the molecules of various raw materials are fully collided and mixed, and then flow into the conveyor belt equipped with a ripening plate, and then pass through the drying tunnel equipped with 12 sections of ovens. The temperature of the oven is set Set at 100°C, the heati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special novel material for a TPU leg guard plate, and a preparation method thereof. The material is prepared from 20-38 wt% of PEA-1800, 3-6 wt% of 1,4-BDO, 1 wt% of 1,3-BDO,24-38 wt% of MDI, 10-24 wt% of polymeric water-absorbent resin, 6-8 wt% of titanium oxide, 20-30 wt% of bamboo fibers, 0.2-0.4 wt% of an antioxidant and 6-8 wt% of a reinforcing agent. The material has the advantages of good transparency, convenience in coloring, rapidness in cooling and sweat absorption, antibacterial and self-cleaning functions, good wear resistance, high strength, high impactresistance, high toughness, suitableness for all kinds of bad weather, keeping of dryness, maintaining of the elegant appearance of the guard, improvement of the use effect of the product, and prolongation of the service life.

Description

technical field [0001] The invention relates to the field of sports equipment, more specifically, a new type of special material for TPU leg shields and a preparation method thereof. Background technique [0002] When the existing TPU production materials are applied to many fields, they often have strict requirements for their various performance indicators, especially high temperature resistance, wear resistance, hardness and toughness. [0003] In ball sports, especially in football, leg guards are essential protective gear. Football players sweat a lot, and their body temperature rises, so they need to cool down, and the collision of limbs, especially legs, during sports Therefore, it is necessary to wear leg guards for protection, and most of the guards are bulky and affect the speed of athletes. Therefore, there is a need for a leg guard that is light in weight, high in hardness, and can reduce body temperature and quickly absorb sweat. Contents of the invention [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/06C08L101/00C08L61/06C08L97/02C08K3/22C08K3/04C08K5/098C08G18/76C08G18/66C08G18/42C08G18/32
CPCC08G18/3206C08G18/4238C08G18/664C08G18/7671C08K2003/2241C08L75/06C08L2201/10C08L2205/035C08L2205/16C08L101/00C08L61/06C08L97/02C08K3/22C08K3/04C08K5/098
Inventor 方超
Owner 江苏绿艳高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com