A 150mm thick low compression ratio z-direction performance steel plate and its production method

A production method and technology of compression ratio, applied in the field of metallurgy, can solve the problems of long waiting time and reduce production rhythm, and achieve the effects of improving production rhythm, improving production efficiency and lowering production cost

Active Publication Date: 2019-09-10
TANGSHAN HEAVY PLATE CO LTD +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And due to the thickness of the plate, it takes a long time to wait for the temperature during rolling, which reduces the production rhythm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A 150mm thick low compression ratio z-direction performance steel plate and its production method
  • A 150mm thick low compression ratio z-direction performance steel plate and its production method
  • A 150mm thick low compression ratio z-direction performance steel plate and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Table 1 shows the chemical composition and mass percentage of the 150 mm thick low compression ratio Z-direction performance steel plate Q420C-Z35 in this example.

[0027] The production method of the 150mm thick low compression ratio Z-direction performance steel plate Q420C-Z35 in this embodiment includes smelting, continuous casting, heating, controlled rolling and controlled cooling processes, and the specific process steps are as follows:

[0028] (1) Smelting process: After RH vacuum degassing treatment, [H] in molten steel is 0.0001%;

[0029] (2) Continuous casting process: the casting speed of the continuous casting machine is 0.85m / min, the superheat of molten steel in the tundish is 23°C, and the technology of continuous casting dynamic light reduction and casting slab solidification end heavy reduction technology is adopted, and the solid phase ratio is distributed according to the solid phase ratio. Segment reduction, the total reduction of the slab is 21m...

Embodiment 2

[0036] Table 1 shows the chemical composition and mass percentage of the 150 mm thick low compression ratio Z-direction performance steel plate in this example.

[0037] The production method of the 150mm thick low compression ratio Z-direction performance steel plate Q420C-Z35 in this embodiment includes smelting, continuous casting, heating, controlled rolling and controlled cooling processes, and the specific process steps are as follows:

[0038] (1) Smelting process: After RH vacuum degassing treatment, [H] in molten steel is 0.0001%;

[0039] (2) Continuous casting process: The casting speed of the continuous casting machine is 0.89m / min, the superheat of molten steel in the tundish is 17°C, and the technology of continuous casting dynamic light reduction and casting slab solidification end heavy reduction technology is adopted, and the solid phase ratio is distributed according to the solid phase ratio. Segment reduction, the total reduction of the slab is 19mm, the red...

Embodiment 3

[0046] Table 1 shows the chemical composition and mass percentage of the 150 mm thick low compression ratio Z-direction performance steel plate Q345B-Z15 in this example.

[0047] The production method of the 150mm thick low compression ratio Z-direction performance steel plate Q345B-Z15 in this embodiment includes smelting, continuous casting, heating, controlled rolling and controlled cooling processes, and the specific process steps are as follows:

[0048] (1) Smelting process: After RH vacuum degassing treatment, [H] in molten steel is 0.0002%;

[0049] (2) Continuous casting process: the casting speed of the continuous casting machine is 0.85m / min, the superheat of molten steel in the tundish is 15°C, the technology of continuous casting dynamic light reduction and casting slab solidification end heavy reduction technology is adopted, and the solid phase ratio is distributed according to the solid phase ratio. Segment reduction, the total reduction of the slab is 19mm, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a steel plate having a thickness of 150 mm, a low compression ratio and a low Z-direction performance, and a production method thereof. The steel plate comprises, by mass, 0.12-0.17% of C, 1.25-1.70% of Mn, 0.002-0.009% of S, 0.008-0.020% of P, 0.30-0.41% of Si, 0.032-0.042% of Als, 0.038-0.045% of Nb, 0.015-0.030% of Ti, 0.0030-0.0050% of N, and the balance of Fe and otherinevitable impurities. The production method comprises the following steps: smelting, continuous casting, heating, controlled rolling and controlled cooling. The rolling compression ratio of the produced steel plate is 1.77-1.80, the production method has the advantages of low production cost and fast production pace, and the steel plate has the characteristics of high flaw detection qualified rate, excellent mechanical properties and high performance uniformity of the microstructure in a thickness direction.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a 150mm thick low compression ratio Z-direction performance steel plate and a production method thereof. Background technique [0002] With the rapid development of my country's national economy, the demand for thick-gauge steel plates in the fields of machinery manufacturing, building structures, marine engineering, energy and power is increasing, and thick-gauge steel plates are generally used in key components. Therefore, the mechanical properties and welding properties of steel plates There are extremely strict requirements. The difficulty in the production of thick gauge steel plates lies in the flaw detection performance of the steel plate, the quality of the core of the steel plate, and the uniformity of the microstructure and properties of the steel plate in the thickness direction. At present, the annual output of my country's thick plates over 60mm is onl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/06C22C38/12C22C38/14C21D8/02B22D11/12
Inventor 刘伟建王强臧淼郑治秀王丽霞尹绍江杨小龙侯蕾王重君李行
Owner TANGSHAN HEAVY PLATE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap