High temperature resistant water polystyrene material

A technology of high temperature resistance and hydraulic adhesive, applied in the field of building materials, can solve the problems such as the reduction of the strength of building materials and the destruction of the hardened slurry system, and achieve the effect of simplifying the composition

Active Publication Date: 2019-02-12
唐山易博达科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Building materials with cement as the main cementitious material usually cannot withstand high temperatures. This is because the hydration products based on ettringite decompose at 70 degrees, causing damage to the hardened slurry system and making the building materials Reduced strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature resistant water polystyrene material
  • High temperature resistant water polystyrene material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A mortar made of high-temperature-resistant hydraulic adhesive material is characterized in that it is obtained by uniformly mixing the following raw materials in weight proportions, including:

[0032] High temperature resistant hydraulic adhesive 400 parts

[0033] Quartz sand 350 parts

[0034] Mineral powder 100 parts

[0035] Dolomite powder 150 parts

[0036] Polycarboxylate high-performance water reducer 1 part

[0037] Sodium gluconate 0.5 parts

[0038] Among them, in the high-temperature-resistant hydraulic adhesive material, the content of tricalcium silicate is 40%, the content of dicalcium silicate is 10%, the content of amorphous silica is 50%, and the content of quartz sand is 20-100 mesh.

Embodiment 2

[0040] A mortar made of high-temperature-resistant hydraulic adhesive material is characterized in that it is obtained by uniformly mixing the following raw materials in weight proportions, including:

[0041] High temperature resistant hydraulic adhesive 400 parts

[0042] Quartz sand 350 parts

[0043] Metakaolin 100 parts

[0044] Dolomite powder 150 parts

[0045] Polycarboxylate high-performance water reducer 1 part

[0046] Sodium gluconate 0.5 parts

[0047] Among them, in the high-temperature-resistant hydraulic adhesive material, the content of tricalcium silicate is 40%, the content of dicalcium silicate is 10%, the content of amorphous silica is 50%, and the content of quartz sand is 20-100 mesh.

Embodiment 3

[0049] High temperature resistant hydraulic adhesive 400 parts

[0050] Quartz sand 350 parts

[0051] Mineral powder 100 parts

[0052] Talc powder 150 parts

[0053] Polycarboxylate high-performance water reducer 1 part

[0054] Sodium gluconate 0.5 parts

[0055] Among them, in the high-temperature-resistant hydraulic adhesive material, the content of tricalcium silicate is 40%, the content of dicalcium silicate is 10%, the content of amorphous silica is 50%, and the content of quartz sand is 20-100 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high temperature resistant water polystyrene material. A mineral composition of the high temperature resistant water polystyrene material comprises tricalcium silicate, dicalcium silicate, and amorphous silica powder, wherein the weight content of the tricalcium silicate is 25 to 50 percent, the weight content of the dicalcium silicate is 25 to 40 percent, the weight content of the amorphous silica powder is 25 to 50 percent, and a ratio of calcium to silicon is less than 2. The invention also discloses mortar made of the high temperature resistant water polystyrene material, which is obtained by uniformly mixing the following raw materials in parts by weight, comprising: 350 to 650 parts of high temperature resistant water polystyrene material, 200 to 500 parts of mortar, 50 to 200 parts of active mineral admixture, 100 to 200 parts of refractory filler, and 0.5 to 5 parts of dispersant. The mortar thus prepared has excellent high temperature resistance and can be used for construction in contact with high temperature building parts.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a high-temperature-resistant hydraulic adhesive material and mortar made from the high-temperature-resistant hydraulic adhesive material. Background technique [0002] At present, the main representative of hydraulic cementitious materials is Portland cement, and the main clinker minerals of cement are tricalcium silicate, dicalcium silicate, C 3 A,C 4 AF and gypsum, the hydration products of cement are mainly ettringite, hydrated calcium silicate gel. Building materials with cement as the main cementitious material usually cannot withstand high temperatures. This is because the hydration products based on ettringite decompose at 70 degrees, causing damage to the hardened slurry system and making the building materials Reduced strength. Therefore, the technology of high-temperature-resistant building materials based on high-temperature-resistant hydraulic adhesive materials s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02
CPCC04B28/02C04B2201/50C04B14/06C04B18/141C04B14/28C04B24/10C04B2103/302C04B14/106C04B14/042
Inventor 李莉张夕夕李小林
Owner 唐山易博达科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com