A kind of environment-friendly fluorine-modified styrene-acrylic emulsion coating used in winter and preparation method thereof

A technology of styrene-acrylic emulsion and fluorine modification, which is applied in coating and other directions

Active Publication Date: 2021-02-26
福州盛世凌云环保科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the temperature is low, especially in winter, the stability and film-forming properties of these coatings will have greater problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly fluorine-modified styrene-acrylic emulsion coating used in winter and preparation method thereof
  • A kind of environment-friendly fluorine-modified styrene-acrylic emulsion coating used in winter and preparation method thereof
  • A kind of environment-friendly fluorine-modified styrene-acrylic emulsion coating used in winter and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0031] The fluorine-modified styrene-acrylic coatings of Examples 1-4 were prepared according to the following steps.

[0032] (1) Under the stirring condition of 1000 rpm, add emulsifier, leveling agent, drier, dispersant, defoamer, stabilizer to the water, stir for 20-30 minutes and then reduce the stirring speed to obtain a slurry, spare;

[0033] (2) Add fluorine-modified styrene-acrylic emulsion to the slurry obtained in step (1) successively under the stirring condition of 1000 rpm, film-forming resin, cyclodextrin, sodium bicarbonate, hydroxyethyl cellulose, and pH adjustment agent to adjust the pH value to 8-9 to obtain a slurry;

[0034] The fluorine-modified styrene-acrylic emulsion is obtained by emulsion copolymerization of styrene, acrylate and perfluorooctyl ethyl acrylate in a weight ratio of (1-3):(2-5):(0.5-2);

[0035] (3) Add diatomaceous earth, talcum powder, and heavy calcium carbonate to the slurry obtained in step (2) under stirring conditions of 500 r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environmental-friendly fluorine-modified styrene-acrylic emulsion coating used in winter and a preparation method of the styrene-acrylic emulsion coating. The coating contains fluorine-modified styrene-acrylic emulsion, film-forming resins, cyclodextrin, sodium bicarbonate, hydroxyethyl cellulose, diatomite, talcum powder, ground limestone, an emulsifier, a flatting agent, a drier, a dispersing agent, an antifoaming agent, a stabilizer and water. The coating has the lowest film forming temperature, is high in stability, and is applicable to use in winter construction.

Description

technical field [0001] The invention relates to the technical field of coatings and preparation, in particular to an environment-friendly fluorine-modified styrene-acrylic emulsion coating used in winter and a preparation method thereof. Background technique [0002] Styrene-acrylic emulsion (styrene-acrylate emulsion) is obtained by emulsion copolymerization of styrene and acrylate monomers. After decades of development in my country, it has excellent adhesion, oxidation resistance and oil resistance. It has been widely used in construction, coatings and adhesives and other fields. However, its water resistance and weather resistance are poor, and it is easy to deform, which limits its application. [0003] At present, silicone or organic fluorine is used to modify styrene-acrylic emulsion. Organosilicon has excellent properties such as high and low temperature resistance, ultraviolet and infrared radiation resistance, and oxidative degradation resistance. Modification of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D133/00C09D7/61C09D7/65
CPCC08K2003/265C08L2205/035C09D133/16C09D7/61C09D7/65C08L33/00C08L5/16C08L1/284C08K7/26C08K3/34C08K3/26
Inventor 郭思源
Owner 福州盛世凌云环保科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com