Polymer semi-permeable material

A technology of semi-permeable materials and polymers, applied in the field of polymer semi-permeable materials, can solve the problems of easy damage, short service period and high cost of use, and achieve the effects of preventing collapse, long service period and improving durability

Inactive Publication Date: 2019-03-01
CHONGQING RUNZE PHARM CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the relationship between structure and performance has not been thoroughly studied at present, such as the contradiction between capture rate, interception rate and permeability treatment speed; polymer separation materials have a precise microstructure, are easy to be damaged, have a short service life, and are expensive to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer semi-permeable material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A PTFE material with a three-dimensional penetrating pore structure. There are stem holes on the stems surrounding the pores. The pore diameter is 100-1000nm; the stem diameter is 50-600nm, and the stem pore diameter is 30-200nm; the porosity of the pores is 50%- 90%, the porosity of the stem hole is 15-65%; the total surface area of ​​the stem, stem area:stem hole area=1-30:1.

[0028] Stem surface area image analysis: Photographs of the material were taken with a scanning electron microscope (SEM photographs, 10,000-50,000x magnification). Scan this photo with image processing equipment (the television image processor TVIP-4100II produced by Avionics Corporation of Japan, the television image processor provided by Latock System Engineering Company) separate the stem from the stem hole to obtain the stem and stem hole image, and process the image through software , to obtain the respective areas, the ratio of the stem area to the total area of ​​the stem hole area imag...

Embodiment 2

[0040] The PTFE material of this embodiment has a three-dimensional penetrating pore structure. There are stem holes on the stems surrounding the pores. The pore diameter is 200±100 nm, the stem diameter is 125±75 nm, and the stem hole diameter is 50±20 nm.

[0041] The preparation method of described PTFE material, comprises the following steps:

[0042] (1) Preparation of spinning solution: dissolve polyvinyl alcohol in water to obtain a uniform solution with a concentration of 14-15%, add polytetrafluoroethylene (PTFE) emulsion (55-60%), so that the mass ratio of PTFE to polyvinyl alcohol is 2 -3:1; the preparation of the emulsion is to prepare high molecular polymer particles by emulsion polymerization, and the average particle diameter of the high molecular polymer particles is 15-40nm;

[0043] (2) Spinning: use high-voltage electrospinning equipment for electrospinning to obtain a uniform nanofiber precursor film; spinning voltage 15~20kV, distance 12~30cm;

[0044] (3) ...

Embodiment 3

[0051] The PTFE material of this embodiment has a three-dimensional penetrating pore structure, and there are stem holes on the stems surrounding the pores, 300nm

[0052] Wherein (I) the porosity of the pores is 60±10%, the porosity of the stem pores is 55±10%; the total surface area of ​​the stems, stem area:stem hole area=1-15:1.

[0053] Or (II) the porosity of the pores is 60±10%, and the porosity of the stem pores is 55±10%; the total surface area of ​​the stem, stem area:stem hole area=16-30:1.

[0054] Or (Ⅲ) the porosity of the pores is 80±10%, and the porosity of the stem pores is 30±15%; the total surface area of ​​the stem, stem area:stem hole area=1-15:1.

[0055] Or (IV) The porosity of the pores is 80±10%, and the porosity of the stem pores is 30±15%; the total surface area of ​​the stem, stem area:stem hole area=16-30:1.

[0056] The preparation method of described PTFE material, co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a polymer semi-permeable material. The material has a three-dimensional linkage porous structure and is characterized in that pedicle openings are formed in the part surroundinga clearance, the diameter of the clearance is 100-1000 nm, the pedicle diameter is 50-600 nm, and the diameter of the pedicle hole is 30-200 nm. The polymer semi-permeable material has the advantagesthat a polymer semi-permeable material structure is improved, the durability of performance is improved, the selecting efficiency and the selection effect of the material are higher, and the servicelife is long.

Description

technical field [0001] The invention relates to a polymer semipermeable material. Background technique [0002] Macromolecular material is a material based on polymer compounds. Polymer materials are materials composed of compounds with relatively high molecular weights, including rubber, plastics, fibers, coatings, adhesives, and polymer-based composite materials. The unique structure of polymer materials and the characteristics of being able to be modified and processed make them have incomparable and irreplaceable excellent properties of other materials, so they are widely used in various fields of science and technology, national defense construction and national economy, and have become a modern society. Indispensable materials in all aspects of daily necessities of life. [0003] Polymer separation material is a separation material made of polymer material with selective permeation function. Using such a semi-permeable material, it is driven by pressure difference, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/728D01D5/00B01D69/12B01D71/36
CPCB01D69/125B01D71/36D01D5/0007D01D5/003D01D5/0076D04H1/728
Inventor 周涛孙琦叶雷
Owner CHONGQING RUNZE PHARM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com