Destructive effect testing method for detecting rigidity of ionic sandwich glass

A technology of laminated glass and testing methods, applied in the direction of elastic testing, testing of material strength using one-time impact force, testing of machine/structural components, etc., to achieve optimized product design, intuitive and clear testing results, and simple and clear testing process

Active Publication Date: 2019-03-19
东莞市群安塑胶实业有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the quality inspection of this kind of ionic laminated glass is only carried out by checking the qualification of the manufacturer and checking the appearance of the product. As for how to test the rigidity of this kind of laminated glass, there is no consistent testing method and standard at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Destructive effect testing method for detecting rigidity of ionic sandwich glass
  • Destructive effect testing method for detecting rigidity of ionic sandwich glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0021] see Figure 1-Figure 2 , the present invention provides a technical solution: a destructive test method for detecting the rigidity of ionic laminated glass, which is characterized in that the test adopts a unilateral support test device, and the unilateral support test device includes a base 1, and a pillar is arranged on the base 1 2. The pillar 2 is provided with a crossbar 3, and the crossbar 3 is provided with a fastening screw 4.

[0022] The spec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a destructive effect testing method for detecting rigidity of ionic sandwich glass. The method specifically includes the following steps of firstly, adjusting a testing device;secondly, recording before-test data; thirdly, damaging a test product; fourthly, recording after-test data; fifthly, obtaining a test result. By means of the detecting method, by completing damagingglass of the two sides of the ionic sandwich glass and directly comparing before-damage and after-damage visual data of the product, the rigidity grade corresponding to the test product can be obtained; the detecting process is simple and clear, the detecting result is visual and clear, the unified simple and feasible detecting method and judgment criteria are provided for detecting the rigidityof the product, and further technological support is provided for the optimized design of the product.

Description

technical field [0001] The invention relates to the technical field of laminated glass, more specifically, a destructive test method for detecting the rigidity of ionic laminated glass. Background technique [0002] Laminated glass is made of two or more pieces of glass sandwiched between one or more layers of organic polymer interlayer film. The integrated composite glass product, because it overcomes the disadvantages of ordinary glass being fragile and easily hurt by fragments, and at the same time retains the good permeability of the glass, and can add interlayer films with different characteristics to make the laminated glass have different characteristics. , has been more and more widely used in all aspects of production and life. At present, the common civilian laminated glass mainly includes ordinary glass curtain wall laminated glass (PVB laminated glass) and ionic laminated glass (SGP laminated glass). The ionic laminated glass has stronger tear resistance and is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G01M5/00G01N3/30G01N3/06
CPCG01M5/005G01N3/06G01N3/30G01N2203/001G01N2203/0282G01N2203/0682
Inventor 晏晓峰
Owner 东莞市群安塑胶实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com