Spray protection material usable for nondestructive color change and automobile body secondary creation

A technology for protecting materials and car bodies, which is applied in the field of spraying protective materials, which can solve the problems of easy foaming and opening, insufficient color, and low color brightness, and achieve the effects of helping society, excellent peelability, and improving spraying efficiency

Pending Publication Date: 2019-04-05
上海凯轮智能科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 2. Color-changing film: Advantages, the film is generally made of PVC material, and the adhesive is pasted on the surface of the car paint, which can provide a ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A spray protection material that can be used for non-destructive color change and secondary creation of the car body. It is made of the following raw materials in parts by weight: 75 parts by weight of TPU resin, 5 parts by weight of coloring pigment, 5 parts by weight of solvent, 4 parts by weight of curing agent, and fillers 3 parts by weight, 3 parts by weight of ultraviolet absorber, and 3 parts by weight of antioxidant, wherein the TPU resin is made by co-reacting and polymerizing melamine, macromolecular polyol and chain extender.

[0029] Its spraying method comprises the following steps:

[0030] (1) Spray the above-mentioned water-based TPU material on the surface of the car paint, with a film thickness of 100um, bake and dry for 1 hour with short-wave infrared rays to form a film;

[0031] (2) Spray the water-based TPU paint containing pigments, cover evenly, the thickness of the coating film is 50um, and bake and dry with short-wave infrared rays for 30 minut...

Embodiment 2

[0035] A spray protection material that can be used for non-destructive color change and secondary creation of the car body. It is made of the following raw materials in parts by weight: 78 parts by weight of TPU resin, 8 parts by weight of coloring pigment, 8 parts by weight of solvent, 7 parts by weight of curing agent, filler 5 parts by weight, 4 parts by weight of ultraviolet absorber, and 4 parts by weight of antioxidant, wherein the TPU resin is made by co-reacting and polymerizing melamine, macromolecular polyol and chain extender.

[0036] Its spraying method comprises the following steps:

[0037] (1) Spray the above-mentioned water-based TPU material on the surface of the car paint, the thickness of the coating film is 150um, and the short-wave infrared ray is baked and dried for 1.3 hours to form a film;

[0038] (2) Spray the water-based TPU paint containing pigments, cover evenly, the thickness of the coating film is 65um, and bake and dry with short-wave infrared...

Embodiment 3

[0042] A spray protection material that can be used for non-destructive color change and secondary creation of the car body. It is made of the following raw materials in parts by weight: 80 parts by weight of TPU resin, 10 parts by weight of coloring pigment, 10 parts by weight of solvent, 10 parts by weight of curing agent, and fillers 10 parts by weight, 5 parts by weight of ultraviolet absorber, and 5 parts by weight of antioxidant, wherein the TPU resin is made by co-reacting and polymerizing melamine, macromolecular polyol and chain extender.

[0043] Its spraying method comprises the following steps:

[0044] (1) Spray the above-mentioned water-based TPU material on the surface of the car paint, the thickness of the coating film is 200um, and the short-wave infrared ray is baked and dried for 1.5 hours to form a film;

[0045] (2) Spray the water-based TPU paint containing pigments, cover evenly, the thickness of the coating film is 80um, and bake and dry with short-wave...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a spray protection material usable for nondestructive color change and automobile body secondary creation. The spray protection material is made from raw materials including, by weight, 75-80 parts of TPU (thermoplastic polyurethane) resin, 5-10 parts of coloring pigment, 5-10 parts of solvents, 4-10 parts of curing agents, 3-10 parts of fillers, 3-5 parts of ultraviolet absorbents and 3-5 parts of antioxidants. A method for spraying the spray protection material on automobiles includes steps of spraying waterborne TPU materials on the surfaces of automobile paint underthe condition of the film thicknesses of 100-200 micrometers, and carrying out baking, drying and film forming by short-wave infrared rays for 1-1.5 hours; spraying waterborne TPU coating with pigment, carrying out uniform covering under the condition of the film thicknesses of 50-80 micrometers, and carrying out baking, drying and film forming by short-wave infrared rays for 30-50 minutes. The spray protection material has the advantages that the spray protection material is excellent in peeling property, waterborne coatings are free of optional damage on the original automobile paint, and accordingly nondestructive color change can be implemented; automobile body secondary creation can be carried out, and accordingly the spray protection material has great significance in maintaining the values of the automobiles; novel automobile life fashion can be led by nondestructive color change, and accordingly social harmony and splendidness and urban traffic cultural development can be assisted.

Description

technical field [0001] The invention relates to the technical field of automobile spraying, in particular to a spraying protection material which can be used for non-destructive color changing and secondary creation of car bodies. Background technique [0002] Existing car color changing mainly uses two categories of car spray paint and color changing sticking film. [0003] 1. Automobile painting: advantages, the paint is a permanent coating, and the original car paint needs to be destroyed before the construction operation can be carried out. The damage to the original car paint is relatively large, and the original car paint is permanently damaged and cannot be restored; the advantage is that the appearance is beautiful and beautiful, and the color variety is more Many, more mature industrial technology. [0004] 2. Color-changing film: Advantages, the film is generally made of PVC material, and the adhesive is pasted on the surface of the car paint, which can provide a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/12B05D3/02B05D5/06B05D7/00
CPCB05D3/0263B05D5/06B05D7/576B05D2503/00C09D175/12B05D2420/01B05D2420/02
Inventor 刘野
Owner 上海凯轮智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap