Preparation method of phosphorus-doped cadmium sulfide supported nickel carbide quantum dot nanorod photocatalyst

A photocatalyst and nanorod technology, used in physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes, etc., can solve the problems of poor stability and visible light catalytic activity, affecting the application of photocatalysts, etc., and achieve strong visible light. Responsiveness, good development potential, excellent performance

Active Publication Date: 2020-11-10
XI AN JIAOTONG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, semiconductor photocatalysis technology is considered to be one of the ideal ways to use solar energy to realize energy conversion and environmental governance. However, the stability and visible light catalytic activity of existing photocatalysts are poor, which seriously affects the application of photocatalysts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of phosphorus-doped cadmium sulfide supported nickel carbide quantum dot nanorod photocatalyst
  • Preparation method of phosphorus-doped cadmium sulfide supported nickel carbide quantum dot nanorod photocatalyst
  • Preparation method of phosphorus-doped cadmium sulfide supported nickel carbide quantum dot nanorod photocatalyst

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation process of CdS nanorods is as follows:

[0029] Add 3.0-5.0g of trioctylphosphine oxide, 0.60-1.0g of n-octadecyl phosphate and 0.10-0.5g of cadmium oxide into the three-necked flask, heat it to 300-350°C under vacuum, and keep it for 1 hour , to dissolve CdO, then inject 3.3g of monomeric tri-n-octylphosphine (TOP) and 0.1g of sulfur powder, react under a nitrogen atmosphere, then cool to 70°C, and finally add 3-6mL of toluene to initially remove the surface Active agent, and finally ultrasonically washed with a mixture of toluene and acetone to remove the surfactant, and then dried in an oven at 60°C for 5 hours to obtain CdS nanorods, wherein the volume ratio of toluene to acetone is 1:1, and the molar ratio of CdO to sulfur powder The ratio is 1 to 3-10.

[0030] The preparation method of phosphorus-doped cadmium sulfide loaded nickel carbide quantum dot nanorod photocatalyst of the present invention comprises the following steps:

[0031] 1) Take ...

Embodiment 1

[0036] The preparation method of phosphorus-doped cadmium sulfide loaded nickel carbide quantum dot nanorod photocatalyst of the present invention comprises the following steps:

[0037] 1) Take CdS nanorods and NaH 2 PO 2 , and then CdS nanorods and NaH 2 PO 2 mixed and then in N 2 Heating to 500°C in the atmosphere for 10 hours to obtain phosphorus-doped CdS nanorods;

[0038] 2) Dissolve phosphorus-doped CdS nanorods in N,N-dimethylformamide, and then add Ni(NO 3 ) 2 ·6H 2 O and 2-methylimidazole, and then stirred at room temperature for 4h to obtain the precursor material;

[0039] 3) Place the precursor material obtained in step 2) in a polytetrafluoroethylene-lined stainless steel autoclave, heat it to 160°C, and keep it for 24 hours, then cool it to room temperature, and then wash it with deionized water and ethanol , to obtain a black-green product, and place the black-green product in an oven at 60° C. to dry for 12 hours to obtain phosphorus-doped cadmium sul...

Embodiment 2

[0042] The preparation method of phosphorus-doped cadmium sulfide loaded nickel carbide quantum dot nanorod photocatalyst of the present invention comprises the following steps:

[0043] 1) Take CdS nanorods and NaH 2 PO 2 , and then CdS nanorods and NaH 2 PO 2 mixed and then in N 2 Heating to 500°C in the atmosphere for 10 hours to obtain phosphorus-doped CdS nanorods;

[0044] 2) Dissolve phosphorus-doped CdS nanorods in N,N-dimethylformamide, and then add Ni(NO 3 ) 2 ·6H 2 O and 2-methylimidazole, and then stirred at room temperature for 4h to obtain the precursor material;

[0045] 3) Place the precursor material obtained in step 2) in a polytetrafluoroethylene-lined stainless steel autoclave, heat it to 160°C, and keep it for 24 hours, then cool it to room temperature, and then wash it with deionized water and ethanol , to obtain a black-green product, and place the black-green product in an oven at 60° C. to dry for 12 hours to obtain phosphorus-doped cadmium sul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of phosphorus-doped cadmium sulfide loaded nickel carbide quantum dot nanorod photocatalyst, which comprises the following steps: 1) taking CdS nanorods and NaH 2 PO 2 , And then combine CdS nanorods with NaH 2 PO 2 Mix and then again in N 2 Heat in the atmosphere to obtain phosphorus-doped CdS nanorods; 2) Dissolve the phosphorus-doped CdS nanorods in N,N-dimethylformamide, and then add Ni(NO 3 ) 2 ·6H 2 O and 2-methylimidazole, then stir at room temperature to obtain precursor materials; 3) Heat and maintain the precursor materials obtained in step 2), then cool to room temperature, and then wash with deionized water and ethanol , The black and green products are obtained, and finally the black and green products are dried to obtain phosphorus-doped cadmium sulfide supported nickel carbide quantum dot nanorod photocatalyst. The photocatalyst prepared by this method has good stability and high visible light catalytic activity, and the preparation method simple.

Description

technical field [0001] The invention relates to a method for preparing a photocatalyst, in particular to a method for preparing a phosphorus-doped cadmium sulfide-loaded nickel carbide quantum dot nanorod photocatalyst. Background technique [0002] The limited reserves of fossil fuels, and with their massive consumption, make human beings face a severe energy crisis, and at the same time face a severe challenge: how to seek renewable and clean energy to ensure a safe and stable supply of global energy. As a clean and abundant energy source, solar energy has great application potential. Therefore, how to realize efficient utilization of solar energy has attracted much attention. [0003] In recent years, semiconductor photocatalysis technology is considered to be one of the ideal ways to use solar energy to realize energy conversion and environmental governance. However, the stability and visible light catalytic activity of existing photocatalysts are poor, which seriously ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/185B01J35/02B01J35/00
Inventor 杨贵东李贺陈子浩
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com