Indoor stone laying processing method

A treatment method and stone technology, applied in cement coating, coating, construction, etc., can solve the problems of anti-skid and anti-alkali treatment, achieve the effect of preventing efflorescence, improving water resistance, and simple and easy construction

Inactive Publication Date: 2019-05-24
SUZHOU KELIDA BUILDING & DECORATION CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, the technical problem to be solved by the present invention is to overcome the defects of difficult anti-skid and anti-alkali treatment of stone paving and facing in the prior art, thereby providing a simple and easy construction, convenient operation, easy to master process, economical and practical, low cost, A pavement treatment method that can effectively prevent the phenomenon of efflorescence on the stone surface and can echo the rough surface stone outdoors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A treatment method for indoor stone pavement, comprising the following steps:

[0035] S1. Clean the stone with normal temperature water, and then build a drying room to dry the stone. The drying temperature is 60-80°C, and the drying time is not less than 50 minutes, or the stone is soaked in hot water above 80°C 1 hour, and then the natural drying time is not less than 24 hours, so that the water in the stone voids can be analyzed;

[0036] S2, carry out sand blasting treatment to dry stone material, in this embodiment of the present invention, the sand blasting machine that adopts comprises workbench, pressure tank and spray gun, and wherein spray gun is connected with pressure tank through pipeline and is arranged on the top of workbench, The nozzle faces the workbench. When sandblasting, first place the stone on the workbench, adjust the position of the stone so that its center is aligned with the center of the circular workbench, and then drive the workbench to ro...

Embodiment 2

[0041] A treatment method for indoor stone pavement, comprising the following steps:

[0042] S1. Clean the stone with normal temperature water, and then build a drying room to dry the stone. The drying temperature is 60-80°C, and the drying time is not less than 50 minutes, or the stone is soaked in hot water above 80°C 1 hour, and then the natural drying time is not less than 24 hours, so that the water in the stone voids can be analyzed;

[0043] S2. Sandblasting the dried stone. In this embodiment of the present invention, use low-alkali cement to seal the six sides of the stone. When the sandblasting layer is thin or thick, use a grinder to perform positioning grinding and grind while grinding While spraying water, then carry out air-drying or drying treatment, so that the thickness of the sandblasting layer is 0.2-0.5cm;

[0044] S3. Configure a curing agent for waterproofing, and apply the curing agent evenly to infiltrate and seal the surface of the stone, and transmit ...

Embodiment 3

[0049] A treatment method for indoor stone pavement, comprising the following steps:

[0050] S1. Clean the stone with normal temperature water, and then build a drying room to dry the stone. The drying temperature is 60-80°C, and the drying time is not less than 50 minutes, or the stone is soaked in hot water above 80°C 1 hour, and then the natural drying time is not less than 24 hours, so that the water in the stone voids can be analyzed;

[0051] S2, sandblasting the dried stone;

[0052] S3. Configure a curing agent for waterproofing, and apply the curing agent evenly to infiltrate and seal the surface of the stone, and transmit it in the micropore capillary of the stone to achieve the purpose of overall blockage of the internal pores of the stone;

[0053] S31. Prepare 35 parts by weight of Portland cement, 30 parts by weight of quartz sand, 0.4 parts by weight of polycarboxylate superplasticizer, 4.5 parts by weight of osmotic crystalline waterproofing agent, 0.25 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of stone construction process, in particular to an indoor stone laying processing method, and aims to solve the problem that existing stone laying is hardin facing antiskid and anti-alkali processing. According to the technical scheme, the method includes the steps of S1, cleaning stone, and subjecting the stone to natural air drying or drying; S2, performing sand blasting on the dried stone; S3, preparing a waterproof curing agent, and evenly coating the surface of the stone with the curing agent to achieve a permeation sealing effect, wherein thecuring agent is conveyed in the micropore capillary of the stone to reach the internal pores of the stone so as to achieve the purpose of overall blocking; S4, performing base layer processing beforelaying, and arranging an under-layer aluminum veneer and a honeycombed aluminum plate on the to-be-laid base layer, wherein the honeycombed aluminum plate is horizontally laid right above the under-layer aluminum veneer; S5, preparing a stone laying adhesive, and using the adhesive to lay the corresponding stone onto the corresponding honeycombed aluminum plate. By the method, stone facing saltpetering can be avoided, and cooperation with outdoor rough-surface stone can be achieved.

Description

technical field [0001] The invention relates to the technical field of stone construction technology, in particular to an indoor stone pavement treatment method. Background technique [0002] During the installation of wet-laid natural stone walls, there will be plaques like watermarks on the stone plates. As the inlaid mortar hardens and dries, the watermarks will shrink slightly or even disappear. They appear isolated and scattered in the plates, but , with the passage of time, especially in wet weather, water vapor invades from the cracks of the board or the surface of the stone, and the water spots on the natural stone gradually become larger and connect into pieces at the cracks of the board. The white crystals often persist for many years and seriously affect the appearance. This phenomenon is called pan-alkaline phenomenon. The reasons are as follows: 1. The crystallization of natural stone is relatively thick, and there are many capillaries invisible to the naked ey...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04F21/18E04F21/165C09D1/08C09D7/61
Inventor 顾星凯钱宇川张洁
Owner SUZHOU KELIDA BUILDING & DECORATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap