ABS/POK alloy spraying-free material and preparation method thereof

A spray-free and alloy technology, applied in the field of ABS/POK alloy spray-free materials and their preparation, can solve the problems of poor product weight, non-spray materials are not resistant to scratches, and the application range is narrow, and achieves low motion resistance and high toughness. , the effect of improving gloss

Active Publication Date: 2019-05-31
威海联桥新材料科技股份有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the technical problems that the existing spray-free materials are not scratch-resistant, the product weight is poor and the application range is narrow, and provides an ABS / POK alloy spray-free material with scratch resistance, good product weight and wide application range and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS/POK alloy spraying-free material and preparation method thereof
  • ABS/POK alloy spraying-free material and preparation method thereof
  • ABS/POK alloy spraying-free material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5

[0041] The preparation method of embodiment 1~5 is as follows:

[0042] (1) The raw materials ABS and POK are first placed in an oven to dry, and the moisture content of the raw materials is determined to be below 0.01%;

[0043] (2) After mixing the aluminum strip mixture corresponding to the weight portion with the lubricating dispersant, place it in a constant temperature box for use;

[0044] (3) Put the dry base materials in step (1) into the mixer together, stir at low speed (400-600r / min) for 1min, add compatibilizer while stirring, and stir at high speed (1300-1500r / min) for 1 minute Stir at low speed (400-600r / min) for 1 minute, then stir at low speed (400-600r / min) for 1 minute, add all the baked processing aids and acid absorbents, and add white oil; Stir at high speed (1300~1500r / min) for 1 minute, then turn to low speed (400~600r / min) and stir for 2 minutes;

[0045] (4) Within 5 minutes after the end of stirring, add the mixed raw materials into the twin-screw ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an ABS/POK alloy spraying-free material and a preparation method thereof, and solves the technical problems that an existing spraying-free material is not scratch-resistant, poor in product weight and narrow in application range. Every 100 parts by weight of the ABS/POK alloy spraying-free material comprises the following components: 49.5-65 parts of ABS, 30-44 parts of POK, 2-5 parts of a compatilizer, 0.2-1 part of a processing aid, 1-2 parts of an aluminum strip mixture, 0.3-0.6 part of an acid absorbent, 0.1-0.5 part of a lubricating dispersant and 0.1 part of whiteoil. The invention also provides a preparation method of the ABS/POK alloy spraying-free material.

Description

technical field [0001] The invention relates to a spray-free material and a preparation method thereof, in particular to an ABS / POK alloy spray-free material and a preparation method thereof. Background technique [0002] With the continuous improvement of living standards, engineering plastics occupy an increasingly important position in people's lives; and with the development of the economy, people are no longer satisfied with the single use value of products, the performance, design, and Requirements such as aesthetics and color are becoming more and more stringent. The color of most products on the market is made by spraying on the surface of the material. This post-processing seriously affects the production efficiency, cost and environmental protection; spray-free products have various advantages such as environmental protection and low cost. , has been increasingly applied and promoted in this field. [0003] At present, the surface hardness of spray-free ABS produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L73/00C08L91/06C08L51/06C08K3/08C08K5/098
Inventor 李宏杰王玉良薛刚耿建家刘福平
Owner 威海联桥新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap