Preparation method of non-homogeneous layered-structure commercial pure titanium

A technology of industrial pure titanium and heterogeneous layer, which is applied in the field of preparation of industrial pure titanium with heterogeneous layered structure, can solve problems such as not being able to meet industrial production, and achieve improved comprehensive mechanical properties, simple process conditions, and easy operation Effect

Active Publication Date: 2019-05-31
NANJING UNIV OF SCI & TECH +1
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the existing method, Wu et al. used a combination of asynchronous rolling and heat treatment to prepare industrially pure titanium with a heterogeneous layered structure. The highest strength can be cl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of non-homogeneous layered-structure commercial pure titanium
  • Preparation method of non-homogeneous layered-structure commercial pure titanium
  • Preparation method of non-homogeneous layered-structure commercial pure titanium

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Embodiment one

[0027] First of all, the present embodiment adopts the following equipment: Hot-rolling and cold-rolling multi-purpose rolling mill, tubular vacuum annealing furnace. The specific operation of preparing a kind of industrial pure titanium with heterogeneous layered structure in this embodiment is as follows:

[0028] (1) The commercially pure titanium plate used in this example has a thickness of 15mm, and its composition (wt.%) is as follows: 0.15O, 0.01N, 0.01C, 0.03Fe, and the rest is Ti and unavoidable impurities.

[0029] (2) The above-mentioned commercially pure titanium plate was kept in a tube-type vacuum annealing furnace at 750° C. for 2 hours to obtain a homogenized structure with an average grain size of 70 μm.

[0030] (3) The industrial pure titanium plate after homogenization annealing is cold-rolled at room temperature, the initial thickness is 15mm, the rolling reduction per pass is 0.3-0.5mm, and the plate thickness is finally rolled...

Example Embodiment

[0033] Embodiment two

[0034] First of all, the present embodiment adopts the following equipment: Hot-rolling and cold-rolling multi-purpose rolling mill, tubular vacuum annealing furnace. The specific operation of preparing a kind of industrial pure titanium with heterogeneous layered structure in this embodiment is as follows:

[0035] (1) The commercially pure titanium plate used in this example has a thickness of 15mm, and its composition (wt.%) is as follows: 0.15O, 0.01N, 0.01C, 0.03Fe, and the rest is Ti and unavoidable impurities.

[0036] (2) The above-mentioned commercially pure titanium plate was kept in a tube-type vacuum annealing furnace at 750° C. for 2 hours to obtain a homogenized structure with an average grain size of 70 μm.

[0037] (3) The industrial pure titanium plate after homogenization annealing is cold-rolled at room temperature, the initial thickness is 15mm, the rolling reduction per pass is 0.3-0.5mm, and the plate thickness is finally rolled...

Example Embodiment

[0040] Embodiment Three

[0041] First of all, the present embodiment adopts the following equipment: Hot-rolling and cold-rolling multi-purpose rolling mill, tubular vacuum annealing furnace. The specific operation of preparing a kind of industrial pure titanium with heterogeneous layered structure in this embodiment is as follows:

[0042] (1) The commercially pure titanium plate used in this example has a thickness of 10mm, and its composition (wt.%) is as follows: 0.15O, 0.01N, 0.01C, 0.03Fe, and the rest is Ti and unavoidable impurities.

[0043] (2) The above-mentioned commercially pure titanium plate was kept in a tube-type vacuum annealing furnace at 750° C. for 2 hours to obtain a homogenized structure with an average grain size of 70 μm.

[0044] (3) The industrial pure titanium plate after homogenization annealing is cold-rolled at room temperature, the initial thickness is 10mm, the rolling reduction per pass is 0.3-0.5mm, and the final plate thickness is rolled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of non-homogeneous layered-structure commercial pure titanium, and belongs to the field of commercial pure titanium manufacturing. The method comprises thesteps that homogenized annealing treatment is conducted on the commercial pure titanium with the thickness of 10-15 mm to obtain homogeneous tissues with the average grain size of 70 microns; 80-90%of cold rolling treatment is conducted on the commercial pure titanium to form traditional belt-shaped coll-rolling tissues; incomplete recrystallization annealing cold rolling treatment is conductedon the commercial pure titanium at the temperature of 450-500 DEG C for 5-60 min to finally prepare the non-homogeneous layered-structure commercial pure titanium. Mechanical experiment results show that the commercial pure titanium with the structure has the buckling strength of 550-660 MPa and the tensile strength of 630-750 MPa, particularly the uniform elongation can be greater than or equal to 4%, and the elongation at break can be greater or equal to 15%. The non-homogeneous layered-structure commercial pure titanium has the advantages that the problem of lower commercial pure titanium strength is solved, the non-homogeneous layered-structure commercial pure titanium can be allowed to have better extendability and plasticity, and the strength and plasticity matching performance of the non-homogeneous layered-structure commercial pure titanium is improved to make industrial application production convenient.

Description

technical field [0001] The invention relates to the field of preparation of industrially pure titanium, in particular to a method for preparing industrially pure titanium with a heterogeneous layered structure. Background technique [0002] Due to its high strength and excellent corrosion resistance, titanium and its alloys have the highest specific strength among many metals. Its specific strength is 3.5 times that of stainless steel, 1.3 times that of aluminum alloy matrix, and 1.7 times that of magnesium alloy. The development and development of titanium alloys and the application of titanium in civil industries will increase exponentially, especially in civil fields such as shipbuilding, automobile manufacturing, chemical industry, electronics, marine development, biomedicine, seawater desalination, geothermal power generation, sewage discharge and anticorrosion. Applications. Compared with titanium alloys, pure titanium does not contain Al, V and other harmful elements...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22F1/18C22F1/02
Inventor 雍鹏凌李玉胜黄照文李建生何燕
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap