Nylon/polyphenylene sulfide alloy material and preparation method thereof

A technology of polyphenylene sulfide and alloy materials, which is applied in the field of nylon modification, can solve the problems that the addition ratio affects the mechanical properties of materials, the cost of laser marking agents is expensive, and easy to produce color stains, etc., to achieve good laser marking effects, excellent The effect of laser marking performance and good mechanical properties

Active Publication Date: 2019-06-07
KINGFA SCI & TECH CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of this technology is that it is simple to implement, but the disadvantage is that the cost of laser marking agents is often very expensive, and the inappropriate addition ratio will affect the mechanical properties of the material. At the same time, many laser marking agents contain heavy metal components, which not only pollute the environment, but also easily produce color pollution. , is not conducive to the realization of color matching

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nylon/polyphenylene sulfide alloy material and preparation method thereof
  • Nylon/polyphenylene sulfide alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-8 and comparative example 1-3

[0047] Weigh PA66 resin, PA6 resin, PPS, glass fiber, antioxidant and lubricant according to the formula dosage of comparative examples 1~3 and specific examples 1~8 described in Table 1, and put the above-mentioned components into mixing Mix in the machine until it is uniform to obtain a premix; then put the obtained premix into a twin-screw extruder for melting and mixing, and extrude and granulate to obtain a PA66 / PPS alloy material; the screw of the twin-screw extruder The aspect ratio is 40~48:1, the barrel temperature is 270~300℃, and the screw speed is 300~450rpm. The performance test of the alloy material is carried out, and the test results are shown in Table 2:

[0048] Table 1 The amount of components used in Comparative Examples 1-3 and Examples 1-8 (parts by weight)

[0049]

[0050] Table 2 Performance test results

[0051]

[0052] From Examples 1-8 and Comparative Examples 1 and 3, it can be seen that adding 1-10 parts of PPS can significantly improve t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a nylon/polyphenylene sulfide alloy material and a preparation method thereof. The nylon/polyphenylene sulfide alloy material comprises following components in parts by weight:35 to 80 parts of nylon, 1 to 10 parts of polyphenylene sulfide, and 20 to 50 parts of glass fibers. By adding a certain amount of polyphenylene sulfide resin into nylon resin, and then the mixture is reinforced by glass fibers to prepare the nylon/polyphenylene sulfide alloy material. Compared with a common laser labeling agent modified enhanced nylon material, the provided nylon/polyphenylene sulfide alloy material has a good mechanical property and an excellent laser labeling performance, does not contain any heavy metal, is environmentally friendly and pollution free, and is beneficial for color matching. The alloy material is resistant to fading in a high temperature high humidity environment, and also has a good laser labeling effect, and moreover, the application range is enlarged.

Description

technical field [0001] The invention belongs to the technical field of nylon modification, and in particular relates to a nylon / polyphenylene sulfide alloy material and a preparation method thereof. Background technique [0002] Polyamide resin has excellent comprehensive properties such as excellent mechanical properties, excellent barrier properties, heat resistance, wear resistance, and chemical corrosion resistance, and is widely used in the fields of machinery manufacturing, electric tools, electronic appliances, and transportation. Especially in the electronic and electrical industry, many parts are marked by laser marking, which requires nylon materials to have good laser marking performance. Nylon materials are generally difficult to mark. To obtain a better laser marking effect, laser marking agents must be added. [0003] Patent CN201810350929 discloses a modified nylon that can be laser marked. By adding a laser marking agent, the nylon has a good laser marking e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L77/02C08L81/02C08K7/14C08K5/20C08K5/101
Inventor 郭唐华冯德才丁超郑一泉许鸿基黄险波叶南飚
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap