Rubber powder compound modified hyperviscous asphalt for noise-reducing and water draining pavement

A compound modification and asphalt-sticking technology, which is applied in building components, building insulation materials, construction, etc., can solve the problems of less than 50% of waste tires being harmlessly utilized, poor impact and scattering performance of the road surface, and viscous toughness of asphalt binders. Insufficient and other problems, achieve significant engineering application value, improve water damage resistance, elongation at break and high splitting tensile strength

Pending Publication Date: 2019-06-28
GUANGXI TRANSPORTATION SCI & TECH GRP CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, according to the current domestic application of noise reduction and drainage pavement, the main problems are: (1) high-viscosity particles are expensive, resulting in a substantial increase in material costs; (2) insufficient viscosity and toughness of asphalt binder, resulting in the anti-impact scattering performance of the pavement Poor, peeling, potholes and other diseases are common after opening to traffic, which affect the performance of the road surface
However, at present, the harmless utilization rate of waste tires is less than 50%. Some of them are used for retreading, producing reclaimed rubber and rubber powder, as fuel, etc.; Secondary pollution, but also caused a serious waste of rubber resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber powder compound modified hyperviscous asphalt for noise-reducing and water draining pavement
  • Rubber powder compound modified hyperviscous asphalt for noise-reducing and water draining pavement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The rubber powder composite modified high-viscosity asphalt for noise reduction and drainage pavement of the present invention is composed of the following raw materials: 100 kg of road petroleum asphalt, 5 kg of activated rubber powder, 2 kg of SBS, 0.1 kg of sulfur, and 0.5 kg of trans polyoctene rubber;

[0031] Preheat the petroleum road asphalt to 170°C and maintain this temperature, add trans polyoctene rubber, stir and shear at a speed of 4000rpm for 60min, then add SBS and activated rubber powder with a particle size of 80 mesh, continue stirring and shearing for 30min, Then add sulfur and stir and shear at a speed of 500rpm for 30 minutes, and then develop the material at 170°C for 150 minutes to obtain rubber powder composite modified high-viscosity asphalt for noise reduction and drainage pavement.

Embodiment 2

[0033] The rubber powder composite modified high-viscosity asphalt for noise reduction and drainage pavement of the present invention is composed of the following raw materials: 100 kg of road petroleum asphalt, 9 kg of activated rubber powder, 4 kg of SEBS, 0.2 kg of sulfur, and 0.7 kg of trans polyoctene rubber;

[0034] Preheat the petroleum road asphalt to 176°C and maintain this temperature, add trans-polyoctene rubber, stir and shear at a speed of 4200rpm for 52min, then add SEBS and activated rubber powder with a particle size of 100 mesh, continue to stir and shear for 26min, Add sulfur and stir and shear at a speed of 600rpm for 24 minutes, and then develop the material at 180°C for 132 minutes to obtain rubber powder composite modified high-viscosity asphalt for noise reduction and drainage pavement.

Embodiment 3

[0036] The rubber powder composite modified high-viscosity asphalt for noise reduction and drainage pavement of the present invention is composed of the following raw materials: 100 kg of road petroleum asphalt, 10 kg of activated rubber powder, 5 kg of SEPS, 0.25 kg of sulfur, and 0.8 kg of trans polyoctene rubber;

[0037]Preheat the petroleum road asphalt to 178°C and maintain this temperature, add trans polyoctene rubber, stir and shear at a speed of 4300rpm for 48min, then add SEPS and activated rubber powder with a particle size of 110 mesh, continue to stir and shear for 24min, Add sulfur and stir and shear at a speed of 650rpm for 21 minutes, and then develop the material at 180°C for 125 minutes to obtain rubber powder composite modified high-viscosity asphalt for noise reduction and drainage pavement.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses rubber powder compound modified hyperviscous asphalt for a noise-reducing and water draining pavement. The asphalt is prepared from pavement petroleum asphalt, activated rubberpowder, a styrene thermoplastic elastomer, a stabilizer and a tackifier. The preparation method comprises the following steps: adding the tackifier into the preheated pavement petroleum asphalt to besheared for 30-60 min; then adding the activated rubber powder and the styrene thermoplastic elastomer to be further sheared; then adding the stabilizer to be sheared for 10-30 min; and developing the material for 60-150 min to obtain the rubber powder compound modified hyperviscous asphalt for the noise-reducing and water draining pavement. The modified hyperviscous asphalt provided by the invention is high in dynamic viscosity, high in softening point, relatively good in sticky toughness and relatively small in flyoff loss and leakage loss, detection results such as needle penetration, ductility and dynamic viscosity can reach a code requirement, and the water damage preventing performance and high temperature anti-rut performance can be improved obviously. The rubber powder compound modified hyperviscous asphalt also has the advantages of being high in low temperature anti-crack ability, long in service life, low in cost and the like, is high in cost performance, and has remarkableengineering application value.

Description

technical field [0001] The invention relates to the field of pavement materials for road engineering, in particular to a rubber powder compound modified high-viscosity asphalt for noise reduction and drainage pavement and a preparation method thereof. Background technique [0002] In recent years, the phenomenon of "waterlogging in light rain and waterlogging in heavy rain" has often appeared in major cities in my country, and it is imminent to effectively solve the problems of urban flood disasters and water pollution. At present, sponge city construction is an important way to solve problems such as comprehensive utilization of rainwater and surface water resources, urban drainage and flood control, and ecological environment protection in urban development, and to achieve low-impact development. development is of great significance. Among them, drainage pavement is the main component of road construction in sponge city. [0003] The noise-reducing drainage pavement in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L19/00C08L53/02C08L23/20C08K3/06
Inventor 陈杰谭华郑明德廉向东刘斌清熊剑平吴绪浩朱政敏禤炜安何俊辉王彬
Owner GUANGXI TRANSPORTATION SCI & TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products