Highly-stable composite die base material

A composite mold, stable technology, applied in the field of composite mold base materials, can solve the problems of complex shape, hard base, mold scrapping, etc., and achieve the effect of good stability, high cost performance and low cost

Inactive Publication Date: 2020-01-03
徐州吉瑞合金铸造有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The mold is a precision tool with a complex shape and bears the swelling force of the billet. It has high requirements for structural strength, stiffness, surface hardness, surface roughness and machining accuracy. The development level of mold production is one of the important symbols of the level of mechanical manufacturing. In the actual use of the mold, usually the direct operation of the molding machine directly acts on the upper mold of the mold, and the work is completed by heating, pressurizing, and passing water through the molding machine. However, in the existing technology, most of the bases for placing the mold can only It plays the role of supporting the mold, so when the mold is heated and pressurized, it is easy to cause the mold to move sideways, and the base is too hard. When the upper and lower molds are misoperated and placed incorrectly, the mold is easily scrapped.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] A more stable composite mold base material, the raw materials in the formula are composed by weight percentage: 0.5% modified rubber particles, 10% unsaturated polyester resin, 1% sand, 1% processing aid, 1% flame retardant Agent, 5% foaming agent, 10% stabilizer, 30% lightly burnt powder, at this time can avoid the side shift, but the error of the upper and lower molds will still lead to the scrapping of the mold.

Embodiment 2

[0009] A more stable composite mold base material, the raw materials in the formula are composed by weight percentage: 6% modified rubber particles, 35% unsaturated polyester resin, 10% sand, 3% processing aids, 2.5% flame retardant Agent, 20% foaming agent, 20% stabilizer, 60% lightly burnt powder, at this time can avoid the situation that the mold is scrapped due to the error of the upper and lower molds, but at this time, there may be sideways movement due to the heating and pressing process.

Embodiment 3

[0011] A more stable composite mold base material, the raw materials in the formula are composed by weight percentage: 4% modified rubber particles, 23% unsaturated polyester resin, 5% sand, 1.5% processing aid, 1.25% flame retardant Agent, 13% foaming agent, 15% stabilizer, 45% lightly burnt powder, at this time has excellent stability, can avoid the sideways movement of the mold caused by heating and pressing, and the hardness of the base is relatively low , There will be no upper and lower mold operation errors that directly lead to mold scrapping.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a highly-stable composite die base material. The material contains an additive and a carrier, and the formula of the material comprises 0.5-6 wt% of modified rubber particles,10-35 wt% of unsaturated polyester resin, 1-10 wt% of sands, 0-3 wt% of a processing aid, 0-2.5 wt% of a flame retardant, 5-20 wt% of a foaming agent, 10-20 wt% of a stabilizer and 30-60 wt% of lightburnt magnesium powder. The product prepared through the method has the advantages of excellent stability, avoiding of lateral displacement of a die in the heating and pressurizing process, low basehardness, avoiding of die scrap directly caused by misoperation of die loading and unloading, low cost and high cost performance.

Description

technical field [0001] The invention discloses a more stable composite mold base material. Background technique [0002] The mold is a precision tool with a complex shape and bears the swelling force of the billet. It has high requirements for structural strength, stiffness, surface hardness, surface roughness and machining accuracy. The development level of mold production is one of the important symbols of the level of mechanical manufacturing. In the actual use of the mold, usually the direct operation of the molding machine directly acts on the upper mold of the mold, and the work is completed by heating, pressurizing, and passing water through the molding machine. However, in the existing technology, most of the bases for placing the mold can only It plays the role of supporting the mold, so when the mold is heated and pressurized, it is easy to cause the mold to move sideways, and the base is too hard. When the upper and lower molds are misoperated and placed incorrect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/06C08L21/00C08L15/00C08K3/36C08K3/26C08K3/22C08J9/04
CPCC08J9/0061C08J9/0066C08J9/04C08J2367/06C08J2415/00C08J2421/00
Inventor 卢建波
Owner 徐州吉瑞合金铸造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products