Stainless steel spray wax solvent and preparation method thereof

A technology of stainless steel and wax removal water, which is applied in the field of chemical cleaners, can solve the problems of easy sticking of a layer of wax ash on the surface of the workpiece, short use time of wax removal water, and darkening of the surface of the workpiece, etc., to achieve a thorough wax removal effect at low temperature , increase production capacity, clean oil removal effect

Inactive Publication Date: 2020-04-17
GUANGDONG REDSUNSTAR IND
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this kind of wax removal water has low foam, it is not good for cleaning stubborn wax scales, and as the volume of wax scales in the bath liquid continues to increase, a layer of wax ash tends to stick to the surface of the workpiece, resulting in darkening of the surface of the workpiece , so that the use of wax removal water is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel spray wax solvent and preparation method thereof
  • Stainless steel spray wax solvent and preparation method thereof
  • Stainless steel spray wax solvent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A kind of stainless steel spray dewaxing water, is made up of the component of following weight:

[0050]

[0051] A preparation method for stainless steel spray wax removal water, comprising the following steps: 1) mixing 2-octenyl succinic anhydride, isomeric decanol polyoxyethylene ether and n-butylamine, stirring at a stirring speed of 60rpm for 30min to obtain a mixed Solution 1; 2) Add octyldiethanolamine to the obtained mixed solution 1, and stir for 30 minutes to obtain mixed solution 2; 3) Add water-soluble starch to water, and stir at a stirring speed of 60 rpm for 20 minutes to obtain mixed solution 3; 4) Mix the obtained solution Liquid three was added to the obtained mixed liquid two, and stirred at a stirring speed of 60 rpm for 30 minutes to obtain stainless steel spray wax removal water.

[0052] Test the cleaning effect of the prepared stainless steel spray wax removal water. The test method is to spray the wax removal water with 5% of the above stai...

Embodiment 2

[0054] A kind of stainless steel spray dewaxing water, is made up of the component of following weight:

[0055]

[0056]

[0057] A preparation method for stainless steel spray wax removal water, comprising the following steps: 1) mixing 2-octenyl succinic anhydride, isomeric decanol polyoxyethylene ether and n-butylamine, stirring at a stirring speed of 65rpm for 25min to obtain a mixed Solution 1; 2) Add octyldiethanolamine to the obtained mixed solution 1, and stir for 20 minutes to obtain mixed solution 2; 3) Add water-soluble starch to water, stir at a stirring speed of 65 rpm for 20 minutes to obtain mixed solution 3; 4) Mix the obtained Liquid three was added to the obtained mixed liquid two, and stirred at a stirring speed of 65 rpm for 25 minutes to obtain stainless steel spray wax removal water.

[0058] Referring to the cleaning effect test method of Example 1, the test results are shown in Table 1.

Embodiment 3

[0060] A kind of stainless steel spray dewaxing water, is made up of the component of following weight:

[0061]

[0062] A preparation method for stainless steel spray wax removal water, comprising the following steps: 1) mixing 2-octenyl succinic anhydride, isomeric decanol polyoxyethylene ether and n-butylamine, stirring at a stirring speed of 80rpm for 10min to obtain a mixed Solution 1; 2) Add octyldiethanolamine to the obtained mixed solution 1, and stir for 10 minutes to obtain mixed solution 2; 3) Add water-soluble starch to water, and stir for 15 minutes at a stirring speed of 80 rpm to obtain mixed solution 3; 4) Mix the obtained solution Liquid three was added to the obtained mixed liquid two, and stirred at a stirring speed of 80 rpm for 10 minutes to obtain stainless steel spray wax removal water.

[0063] Referring to the cleaning effect test method of Example 1, the test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

At present, the normal use temperature of a conventional wax solvent is far higher than the temperature maintained by an automatic spray line wax removal tank, so that the wax removal effect is not fully exerted, and the economic benefit is affected. The invention discloses a stainless steel spray wax solvent which is suitable for spraying under a low-temperature condition and has good wax removaleffect. The stainless steel spray wax solvent comprises, by weight, 15-35 parts of a wax dissolving agent, 5-20 parts of a saponifier, 5-20 parts of an alcohol amine solvent, 5-20 parts of a surfactant, 0.2-5 parts of water-soluble starch and 30-65 parts of water. Compared with the prior art, different raw materials, proportioning and manufacturing processes are adopted, and the wax dissolving agent with strong permeability and the surfactant are combined, so that the wax solvent has excellent wax removal effect while keeping low foam, the low-temperature wax removal effect is thorough, the use period is longer, the working efficiency is effectively improved, and the productivity is improved.

Description

technical field [0001] The invention belongs to the technical field of chemical cleaners, and relates to a wax removal water used for cleaning the wax residue on the surface of metal products after polishing, in particular to a stainless steel low-temperature spray wax removal water and a preparation method thereof. Background technique [0002] Today, in the metalworking industry, polishing is indispensable. However, most manufacturers need to use solid polishing wax or liquid wax for polishing. After grinding and polishing, a large amount of wax scale will remain on the metal surface, especially the residual polishing wax firmly attached to the metal surface and depressions. After being melted at high temperature during the grinding process, it adheres more firmly to the surface of the workpiece. Wax removal is the first process of pre-treatment of metal electroplating parts. The speed and thoroughness of wax removal are of great significance to the production of electrop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/24C23G5/036C23G5/06
CPCC23G1/24C23G5/036C23G5/06
Inventor 陈腾飞
Owner GUANGDONG REDSUNSTAR IND
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com