A high-performance trapezoidal aluminum alloy material and its production method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An aluminum alloy material and aluminum alloy technology, applied in metal processing equipment, manufacturing tools, mechanical cleaning, etc., can solve the problems of reducing the strength and service life of the hub, uneven composition and performance, and coarse grains of the finished product. Uniform and delicate, less impurities, uniform composition effect
Active Publication Date: 2021-05-11
河南中孚技术中心有限公司
View PDF11 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] At present, the cast aluminum alloy products used in the wheel hub industry have defects such as many pinholes, uneven composition and performance, and internal looseness. The unstable quality cannot meet the qualified industry standards, resulting in coarse grains, pinholes, and many impurities in the finished product. Defects, which greatly reduce the strength and service life of the hub
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0047] Example 1: A high-performance trapezoidal aluminum alloy material, its composition by weight percentage is: silicon Si 7.4%, iron Fe≤0.12%, copper Cu 0.42, magnesium Mg 0.4%, titanium Ti 0.1%, total impurity content < 0.02%, the balance is aluminum.
[0048] The production method of above-mentioned high-performance trapezoidal aluminum alloy material, its steps are as follows:
[0049]A. First add the cold material of the same composition, the addition amount is 15-20% of the furnace capacity, and then add the electrolytic aluminum liquid ingredients, Fe≤0.07% and Si≤0.04% in the electrolytic aluminum liquid, turn on the electromagnetic stirring and heat up at the same time, let the cold material melt To achieve a mixed melt with uniform composition;
[0050] B. When the temperature reaches above 750°C, sprinkle a certain amount of slagging agent, turn on the electromagnetic stirring for 30 to 40 minutes, and then perform slag removal on the surface of the aluminum liq...
Embodiment 2
[0070] Embodiment 2: The production method of this embodiment is basically the same as that of Embodiment 1, and the similarities will not be repeated. The difference is: a high-performance trapezoidal aluminum alloy material, and its composition is by weight percentage: silicon Si 7.5% , iron Fe ≤0.12%, copper Cu 0.46, magnesium Mg 0.45%, titanium Ti 0.15%, total impurity content <0.02%, and the balance is aluminum.
Embodiment 3
[0071] Embodiment 3: The production method of this embodiment is basically the same as that of Embodiment 1, and the similarities will not be repeated. The difference is: a high-performance trapezoidal aluminum alloy material, and its composition is by weight percentage: silicon Si 7.4~ 7.5%, iron Fe ≤0.12%, copper Cu 0.42-0.46, magnesium Mg 0.4-0.45%, titanium Ti 0.1-0.15%, total impurity content <0.02%, and the balance is aluminum.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-performance trapezoidal aluminum alloy material, the composition of which is: silicon Si 7.4-7.5%, iron Fe≤0.12%, copper Cu0.42-0.46, magnesium Mg0.4-0.45%, titanium Ti0. 1-0.15%, the total impurity content is <0.02%, and the balance is aluminum. The production method is as follows: add cold material with the same composition, the ratio is 15-20% of the capacity of the melting furnace, then add the electrolytic aluminum liquid ingredients, through electromagnetic stirring treatment to achieve uniform composition of the aluminum liquid, add alloy materials in turn, through refining, degassing box, The pure aluminum solution is obtained from the filter box, and the horizontal casting is achieved through the balance adjustment. The adjustment amount of the aluminum liquid matches the speed of the casting machine, and the cooling method, cooling water flow and pressure are reasonably distributed, forming a process from liquid to crystallization in the cooling area of the crystallizer. The best condition, to ensure the grain size of the trapezoidal aluminum alloy. The product of the invention has uniform composition, high strength, fine grain size, first-class pinhole degree, low hydrogen content and few impurities, and comprehensively improves the mechanical properties of the alloy product.
Description
[0001] 1. Technical field: [0002] The invention relates to a composition of a high-performance trapezoidal aluminum alloy material and a production method thereof, which are widely used in the production of materials for automobile hubs, through refining, degassing, filtering, horizontal casting and Candinius-Propez The advanced cooling process of the casting unit can effectively improve the strength and performance stability of the product, so that the product has the advantages of bright surface, fine grain size, first-class pinhole degree, and low hydrogen content. [0003] 2. Background technology: [0004] At present, the cast aluminum alloy products used in the wheel hub industry have defects such as many pinholes, uneven composition and performance, and internal looseness. The unstable quality cannot meet the qualified industry standards, resulting in coarse grains, pinholes, and many impurities in the finished product. Defects greatly reduce the strength and service l...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more