Low-temperature high-toughness nodular cast iron for large thick-wall wind power casting and preparation method of low-temperature high-toughness nodular cast iron

A technology of ductile iron and thick-walled castings, which is applied in the field of metallurgy, can solve the problems of unfavorable casting cost control, etc., and achieve the effects of reducing cross-section sensitivity, pure material, and stable metallographic structure

Pending Publication Date: 2020-12-15
宁波日星铸业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Bao Yulong added 1.0-1.5% nickel to ensure the low-temperature impact performance of the material in "A Preparation Method for Low-temperature and Corrosion-resistant Ductile Iron for Wind Power". This control method can indeed achieve low-temperature impact indicators, but nickel is a precious metal, and the price At 120,000-170,000 per ton, it is very unfavorable for casting cost control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature high-toughness nodular cast iron for large thick-wall wind power casting and preparation method of low-temperature high-toughness nodular cast iron
  • Low-temperature high-toughness nodular cast iron for large thick-wall wind power casting and preparation method of low-temperature high-toughness nodular cast iron
  • Low-temperature high-toughness nodular cast iron for large thick-wall wind power casting and preparation method of low-temperature high-toughness nodular cast iron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The preparation process of the low-temperature high-toughness ductile iron for large thick-walled wind power castings in this embodiment is as follows:

[0053] (1) Raw materials are configured according to the following weight percentages: 80% pig iron, 20% scrap steel, 8% coke, 3% limestone, and 0.9% ferrosilicon. Add pig iron, scrap steel, coke, limestone, and ferrosilicon to the cupola at one time for smelting It is molten iron, and the tapping temperature is controlled at 1500°C.

[0054] Among them, the components of pig iron include: C4.60%, Si0.40%, Mn0.1%, P0.013%, S0.020%, As0.0003%, Pb0.0002%, Sn0.0003 %, Sb0.0004%, Zn0.0002%, Cr0.0041%, Ni0.0030%, Cu0.0030%, V0.010%, Ti0.012%, Mo0.0008%, B≤0.0007% (meet pig iron Components by weight percentage C≥4.00%, Si0.30-0.60%, Mn≤0.1%, P≤0.020%, S≤0.025%, As≤0.0008%, Pb≤0.0005%, Sn≤0.0005%, Sb≤ 0.0006%, Zn≤0.0003%, Cr≤0.0050%, Ni≤0.0060%, Cu≤0.0050%, V≤0.010%, Ti≤0.015%, Mo≤0.0010%, B≤0.0010%),

[0055] Scrap steel ...

Embodiment 2

[0075] In this embodiment, the preparation process of low-temperature high-toughness ductile iron for large thick-walled wind power castings is as follows:

[0076] (1) Raw materials are configured according to the following weight percentages: 85% pig iron, 15% scrap steel, 9% coke, 2.5% limestone, and 1.2% ferrosilicon. Add pig iron, scrap steel, coke, limestone, and ferrosilicon to the cupola at one time for smelting It is molten iron, and the tapping temperature is controlled at 1500°C.

[0077] Among them, the components of pig iron include: C4.60%, Si0.40%, Mn0.1%, P0.013%, S0.020%, As0.0003%, Pb0.0002%, Sn0.0003 %, Sb0.0004%, Zn0.0002%, Cr0.0041%, Ni0.0030%, Cu0.0030%, V0.010%, Ti0.012%, Mo0.0008%, B≤0.0007% (meet pig iron Components by weight percentage C≥4.00%, Si0.30-0.60%, Mn≤0.1%, P≤0.020%, S≤0.025%, As≤0.0008%, Pb≤0.0005%, Sn≤0.0005%, Sb≤ 0.0006%, Zn≤0.0003%, Cr≤0.0050%, Ni≤0.0060%, Cu≤0.0050%, V≤0.010%, Ti≤0.015%, Mo≤0.0010%, B≤0.0010%),

[0078] Scrap steel i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention relates to low-temperature high-toughness nodular cast iron for a large thick-wall wind power casting and a preparation method of the low-temperature high-toughness nodular cast iron, and belongs to the technical field of metallurgy. The low-temperature high-toughness nodular cast iron for the large thick-wall wind power casting comprises the following components in percent by weight: 3.65-3.75% of C, 1.95-2.05% of Si, 0.15-0.25% of Mn, less than or equal to 0.025% of P, 0.005-0.015% of S, 0.035-0.047% of Mg, 0.002-0.006% of RE, 0.003-0.007% of Sb and the balance of Fe. Accordingto the low-temperature high-toughness nodular cast iron, expensive metal elements are not additionally added on the basis of QT400-18AL type cast iron, and on the premise that the strength of the cast iron is guaranteed, the low-temperature high-toughness nodular cast iron has good low-temperature high-toughness performance when applied to the large thick-wall casting.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and relates to a low-temperature high-toughness ductile iron for large thick-walled wind power castings and a preparation method thereof. Background technique [0002] Ductile iron is widely used in wind turbines. According to incomplete statistics, the installed capacity of wind power in the world exceeded 3000GW from 2014 to 2019. With the development of the wind power market, the total installed capacity of wind power is still growing. The installed capacity of wind turbines can be divided into onshore wind turbines and offshore wind turbines according to the area. Generally, the impact requirements of offshore wind turbines on castings are -20°C without notch impact, while onshore wind turbines require -40°C to -20°C without gap impact; for wind power Units with ductile iron castings that are used in low temperature environments all the year round need to use QT350-22AL hubs and bases with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C37/10C22C37/04C22C33/10C21C1/10
CPCC21C1/10C21C1/105C22C33/10C22C37/04C22C37/10Y02P10/20
Inventor 杨麟王惠兵赵益锋王益利
Owner 宁波日星铸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap