Preparation method of fiber mesh-compounded diatom ooze coating

A technology of diatom mud coating and fiber screen, which is applied in antifouling/underwater coatings, coatings, paints containing biocide, etc., can solve the problems of inconvenient construction and low strength, and achieve reduced molding time and heat conduction The effect of good sex and good bactericidal effect

Inactive Publication Date: 2021-01-26
佘丽辉
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a method for preparing a fiber screen composite diatom mud coating, mainly to solve the problems that the existing coatings are inconvenient for construction, low in strength and cannot meet people's requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of fiber mesh-compounded diatom ooze coating
  • Preparation method of fiber mesh-compounded diatom ooze coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] refer to Figure 1-2 , a kind of preparation method of fiber screen composite diatom mud coating, comprises the following steps:

[0035] S1: Prepare raw materials, fiber screen, 25-35 parts of deionized water, 15-25 parts of diatomaceous earth, 2-8 parts of humectant, 15-25 parts of pure benzene deodorant emulsion, 10-18 parts of filler, quartz powder 2-6 parts, 0.5-1 part of dispersant, 0.5-1 part of defoamer, 0.2-1 part of nano-diamond particles, 0.2-0.8 part of leveling agent, 0.3-0.6 part of thickener, 2-5 parts of antifreeze , 3-7 parts of photocatalyst, 2-5 parts of antifungal agent; the main material of the present invention is diatomite, which has the characteristics of large porosity, strong absorption, stable chemical properties, heat resistance, etc., and can provide coatings with Excellent surface properties, compatibilization, thickening and improved adhesion. Diatomite coating also has the function of eliminating odor and keeping the room clean. Nano-dia...

Embodiment 2

[0048] refer to Figure 1-2 , a kind of preparation method of fiber screen composite diatom mud coating, comprises the following steps:

[0049] S1: Prepare raw materials, fiber screen, 28-40 parts of deionized water, 18-25 parts of diatomaceous earth, 2-8 parts of humectant, 17-25 parts of pure benzene deodorant emulsion, 13-18 parts of filler, quartz powder 3-6 parts, 0.5-1 part of dispersant, 0.5-1 part of defoamer, 0.5-1 part of nano-diamond particles, 0.2-0.8 part of leveling agent, 0.3-0.6 part of thickener, 2-4 parts of antifreeze , 3-7 parts of photocatalyst, 2-5 parts of antifungal agent; the main material of the present invention is diatomite, which has the characteristics of large porosity, strong absorption, stable chemical properties, heat resistance, etc., and can provide coatings with Excellent surface properties, compatibilization, thickening and improved adhesion. Diatomite coating also has the function of eliminating odor and keeping the room clean. Nano-dia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of diatom ooze coatings, and discloses a preparation method of a fiber mesh-compounded diatom ooze coating. The preparation method comprises the followingstep: S1, preparing raw materials including a fiber mesh, 25-35 parts of deionized water, 15-25 parts of diatomite, 2-8 parts of a humectant, 15-25 parts of an odor-free pure benzene emulsion, 10-18 parts of a filler, 2-6 parts of quartz powder and 0.5-1 part of a dispersant. The invention further provides a construction method of the fiber mesh-compounded diatom ooze coating. The construction method comprises the following steps: S1, cleaning a wall surface, namely cleaning the wall surface to be constructed by using a tool; and S2, fixing the fiber mesh. According to the invention, the overall structural strength of a diatom ooze coating composite layer is improved, and the diatom ooze coating is distributed in meshes of the fiber mesh and bonded and compounded to the fiber mesh and a wall surface base layer, so the flexibility of the diatom ooze coating composite layer is improved, construction is convenient, formaldehyde, benzene and other organic matters can be effectively decomposed, and a good air purification effect is achieved.

Description

technical field [0001] The invention relates to the technical field of diatom mud coatings, in particular to a preparation method of fiber screen composite diatom mud coatings. Background technique [0002] Diatom mud is a kind of inorganic gelling substance as the main bonding material, diatom material as the main functional filler, the preparation of dry powder interior wall decoration coating material, has the functions of eliminating formaldehyde, purifying air, adjusting humidity, releasing negative oxygen ions, fire and flame retardant, wall self-cleaning, sterilization and deodorization and other functions. It is used to replace wallpaper and latex paint. It is suitable for interior wall decoration in villas, apartments, hotels, homes, hospitals, etc. Therefore, diatom mud coating is a new type of environmentally friendly coating. Diatom mud has the functions of eliminating formaldehyde and releasing negative oxygen ions. , calling it "breathable environmentally frie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D7/61C09D7/63C09D7/65C09D5/14E04F13/02E04F13/04
CPCC09D1/00C09D5/14C09D7/61C09D7/63C09D7/65E04F13/02E04F13/047
Inventor 佘丽辉曾文杰曹李
Owner 佘丽辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com