A kind of invisible appliance and preparation method thereof

An invisible appliance and invisible orthodontic technology, applied in the field of stomatology, can solve the problems of preventing and controlling enamel demineralization in orthodontic patients, and the invisible appliance can not achieve bacteriostasis at the same time, so as to meet clinical needs, promote enamel mineralization, and achieve effective results. long lasting effect

Active Publication Date: 2022-07-22
南方医科大学口腔医院
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problem that existing invisible aligners cannot realize antibacterial and prevent orthodontic patients' enamel demineralization at the same time, the present invention aims to provide an invisible aligner and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of invisible appliance and preparation method thereof
  • A kind of invisible appliance and preparation method thereof
  • A kind of invisible appliance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Embodiment 1 A kind of invisible appliance

[0049] 1. Raw materials

[0050] This embodiment provides an invisible appliance, the invisible orthodontic base material is thermoplastic polyurethane, and the dosage of each component of the coating material is: sodium fluoride 0.35g, PEG 0.5g, chitosan 1g, nano-titanium dioxide 1g; The particle size of the nano-titania is 10 nm.

[0051] 2. Preparation method

[0052] The preparation process is as figure 1 shown.

[0053] (1) Preparation of coating

[0054] S1. Dissolve chitosan in 20g / L acetic acid aqueous solution, filter to obtain 20g / L chitosan solution; prepare 30g / L PEG aqueous solution, add sodium fluoride and mix to obtain fluorine-loaded PEG aqueous solution;

[0055] S2. Mix the chitosan / acetic acid aqueous solution in step S1 with the fluorine-loaded PEG aqueous solution to obtain a chitosan / fluorine-loaded PEG homogeneous mixed solution;

[0056] S3. adding nano titanium dioxide to the homogeneous mixed s...

Embodiment 2

[0061] Embodiment 2 A kind of invisible appliance

[0062] 1. Raw materials

[0063] This embodiment provides an invisible appliance, the invisible orthodontic base material is thermoplastic polyurethane, and the dosage of each component of the coating material is: calcium fluoride 0.35g, PEG 0.35g, chitosan 2g, nano-titanium dioxide 1g; The particle size of the nano-titania is 10 nm.

[0064] 2. Preparation method

[0065] Same as Example 1.

Embodiment 3

[0066] Embodiment 3 A kind of invisible appliance

[0067] 1. Raw materials

[0068] This embodiment provides an invisible appliance, the invisible orthodontic base material is thermoplastic polyurethane, and the dosage of each component of the coating material is: 0.35 g of stannous fluoride, 0.35 g of PEG, 1 g of chitosan, and 1 g of nano-titanium dioxide; The particle size of nano titanium dioxide is 10nm.

[0069] 2. Preparation method

[0070] Same as Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention provides an invisible appliance and a preparation method thereof. The invisible appliance is obtained by introducing a coating material into the surface of an invisible orthodontic substrate through an ultrasonic-assisted technology; the coating material includes fluorine salt, PEG, chitosan Sugar and nano-titanium dioxide, the preparation of coating material adopts PEG-loaded fluorine to obtain stable and long-lasting slow-release fluorine effect, so that it has the property of promoting enamel mineralization; PEG can also improve the dispersion of nano-titanium dioxide particles in suspension, improve the Nano-titanium dioxide has uniform dispersion, good biocompatibility, stable chemical properties, and remarkable bacteriostatic effect. Its combination with chitosan can significantly enhance bacteriostatic properties. The obtained invisible appliance has excellent mechanical properties, long-term bacteriostatic, Features that promote enamel mineralization.

Description

technical field [0001] The invention relates to the technical field of stomatology, in particular, to an invisible appliance and a preparation method thereof. Background technique [0002] Due to the advantages of self-removal and wearing, easy cleaning, aesthetics, comfort, and convenience, invisible appliances have been increasingly favored by patients with malocclusion in recent years. However, with the expansion of the patient group wearing invisible appliances, the complications brought about by invisible appliances have gradually emerged, among which the most common ones are demineralization of tooth enamel and caries. Invisible appliances are in close contact with the tooth surface during wearing, the saliva and air flow rates on the tooth surface are reduced, and the scouring ability of dental plaque is weakened. In addition, the easily formed anaerobic interface changes bacterial metabolism and microecology, which eventually causes Demineralization of tooth enamel....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61C7/00A61C7/08A61L31/10A61L31/08A61L31/14A61L31/16
CPCA61C7/00A61C7/08A61L31/10A61L31/088A61L31/14A61L31/16A61L2300/102A61L2300/404C08L5/08C08L71/02
Inventor 张超王健蓉何龙文代丹妮陈堉铭邵龙泉
Owner 南方医科大学口腔医院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap