Light-colored C5C9 copolymer resin catalyst

A copolymer resin and catalyst technology, which is applied in the field of light-colored C5C9 copolymer resin catalysts, can solve the problems of high energy consumption for cooling ice machines, large catalyst consumption, and high F ion content, and achieve product quality improvement, effective product quality, and good dispersion performance Effect

Pending Publication Date: 2021-04-13
PUYANG XINYU PETROCHEM IND
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved by the present invention is to provide a kind of light color C 5 C 9 Copolymerization resin catalyst to solve the technical problems in the prior art that the cold polymerization process requires high energy consumption of ice machine cooling, low production yield, large amount of catalyst, and high content of F ions in wastewater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: A light color C 5 C 9 Copolymerization resin catalyst: including the following raw materials in mass percentage: ALCL 3 20%, BF 3 Diethyl ether complex 50%, 1,2-dichloroethane 20%, diisopropyl ether 10%.

[0030] a light color C 5 / C 9 The preparation method of copolymer resin comprises the steps:

[0031] (1) Polymerization reaction: the C 5 / C 9 Mixed Raw and Light C 5 C 9 The copolymer resin catalyst is mixed in a certain proportion and added to the copolymerization reactor to generate a polymerization product under the action of the catalyst; C 5 / C 9 Mixed raw materials: The mass ratio of composite catalyst is 100:1.5; Reactor temperature: 40-45°C, Reactor pressure: 0.20-0.25MPA, Reactor feed rate: 10-10.5t / h; Reaction residence time: 3.5h ;

[0032] (2) Terminate the polymerization reaction: fully mix the product obtained in step (1) with dilute lye and add it into the termination reaction device to terminate the polymerization reaction, and...

Embodiment 2

[0043] Embodiment 2: the difference with embodiment 1 is:

[0044] a light color C 5 C 9 Copolymerization resin catalyst: including the following raw materials in mass percentage: ALCL 3 25%, BF 3 Diethyl ether complex 45%, 1,2-dichloroethane 23%, diisopropyl ether 7%.

[0045] In this polymerization reaction, by volume, 30% C 5 C 9 Copolymerization resin catalyst with 70% C 5 C 9 The composite catalyst is prepared by extracting the mixed raw materials after polymerization.

[0046] Among them, the light color C 5 C 9 The preparation method of copolymerization resin catalyst comprises the steps: BF 3 Diethyl ether complex, start the preparation kettle to stir, then add fusion agent A, fusion agent B in turn, stir for 0.5h and then use N 2 air insufflation into ALCL 3 The catalyst was prepared by continuing to stir for 1.0h.

[0047] Applied to C by the catalyst of the present invention 5 C 9 On the copolymer resin, its performance index is:

[0048] ①BF 3 The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a light-colored C5C9 copolymer resin catalyst which comprises the following raw materials in percentage by mass: 10-35% of ALCL3, 25-55% of a BF3 diethyl ether complex, 10-25% of a fusion agent A and 5-10% of a fusion agent B. The invention aims to solve the technical problems of high energy consumption, low production yield, high catalyst consumption and high F ion content in wastewater due to the fact that a cold polymerization process in the prior art needs an ice machine for cooling.

Description

technical field [0001] The invention relates to the technical field of resin synthesis, in particular to a light-colored C 5 C 9 Copolymerization catalyst. Background technique [0002] In recent years, with the increase of demand for ethylene, domestic ethylene production facilities are developing towards large-scale development, and many sets of ethylene facilities have been added in various places in my country. For this reason, ethylene by-product C 5 and C 9 Distillate raw materials increase accordingly, for C 5 、C 9 and C 5 C 9 Copolymer resin production provides sufficient raw material resources. C 5 、C 9 and C 5 C 9 The copolymer resin market is still strong in recent years, and the resin production industry is facing huge advantages and opportunities. However, most domestic enterprises can only produce low-end C 9 and C 5 C 9 Copolymer resin, and 60-70% of it is still produced by thermal polymerization process. This kind of resin has deep color, many ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F240/00C08F4/14C08F4/00
CPCC08F240/00C08F4/14C08F4/00
Inventor 贺纪刚李争奎王仁伟赵明磊高鹏裴存章魏自海
Owner PUYANG XINYU PETROCHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap