Liquid composition storage method and product
A technology of liquid composition and preservation method, which is applied in the preservation of liquid composition and the field of products, can solve the problems of large influence and the like, and achieve the effect of stable storage and transportation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1～11、 comparative example 1～5
[0071] Using 1223xd(Z) (acid component: less than 0.5 ppm, purity: 99%, colorless transparent liquid) as a liquid composition, the above-mentioned immersion test was performed. The results are shown in Table 1.
[0072] [Table 1]
[0073]
[0074] In Table 1, "-" means not determined. As can be seen from Table 1, in Comparative Examples 1 to 5, weight loss and coloration were clearly observed in the test pieces. Therefore, in Comparative Examples 1-5, the measurement of "acid content" and "purity" was not performed. The same applies to Comparative Examples 6 to 10 shown in Table 2.
[0075] In Table 1, the materials shown below were used for various test pieces. The same is true in Table 2.
[0076] Perfluoroalkoxyalkane: "AF2400" manufactured by The Chemours Company
[0077] Polyetheretherketone: "PK-450" manufactured by Nippon Polypenco Limited
[0078] High-density polyethylene: "EL-N-AN" manufactured by Shin-Kobe Electric Machinery Co., Ltd.
[0079] Low-density...
Embodiment 12～22、 comparative example 6～10
[0091] A mixed composition of 1223xd(Z) and 1223za (mixed composition of 90% by mass of 1223xd(Z) and 10% by mass of 1223za, acid component: less than 0.5ppm, purity: 99%, colorless and transparent liquid) as the liquid Compositions were subjected to the immersion test described above. The results are shown in Table 2.
[0092] [Table 2]
[0093]
Embodiment 23～26
[0095] Using 1223xd(Z) (acid component: less than 0.5 ppm, purity: 99%, colorless transparent liquid) as a liquid composition, the above-mentioned immersion test was performed. The results are shown in Table 3.
[0096] [table 3]
[0097]
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |