Special water-based antirust liquid for aluminum and preparation method of special water-based antirust liquid

A kind of anti-rust liquid, water-based technology, applied in the direction of anti-corrosion coatings, coatings, polyester coatings, etc., can solve the problems of on-site production efficiency, hard to remove white spots, etc., achieve excellent alkali corrosion inhibition performance, and ensure film formation continuity , the effect of reducing the cost of use

Active Publication Date: 2021-07-09
沈阳防锈包装材料有限责任公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

White spots are difficult to remove, and usually can only be removed by grinding, which undoubtedly has a great impact on on-site production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special water-based antirust liquid for aluminum and preparation method of special water-based antirust liquid
  • Special water-based antirust liquid for aluminum and preparation method of special water-based antirust liquid

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] A kind of preparation method of water-based aluminum antirust solution provided by the invention comprises the following steps:

[0031] (1) Add 25-45 parts of deionized water and 0.01-5 parts of dispersant in sequence in the reaction kettle, stir for 10-15 minutes until the solution is clear and transparent, and obtain the first mixed solution;

[0032] (2) After adding 0.01-10 parts of alkaline agent and 0.01-5 parts of fatty acid into the first mixed liquid, heat the reactor to 70°C-80°C, stir for 20-30min, until the solution is clear and transparent, stop heating, Obtain the second mixed solution;

[0033] (3) Add 25-45 parts of deionized water to the second mixed liquid, then cool down the liquid in the reactor to 40-50°C, then add 0.01-10 parts of film-forming agent and 0.01-5 parts of aluminum corrosion inhibitor in sequence , at 40-50°C, stir for 30-40min until the solution is clear and transparent to obtain the third mixed solution;

[0034] (4) When the temp...

Embodiment 1

[0037] A water-based antirust solution for aluminum, consisting of the following components in parts by weight:

[0038] 3 parts of fatty alcohol polyoxyethylene ether, 2 parts of triethanolamine, 2 parts of monoethanolamine, 4 parts of tall oil, 5 parts of oleic acid ester, 5 parts of silane, 0.2 part of silicone polyether, 78.8 parts of deionized water.

[0039] A preparation method of water-based aluminum antirust liquid, comprising the steps of:

[0040] (1) Add 39.4 parts of deionized water and 3 parts of fatty acid polyoxyethylene ether into the reaction kettle in sequence, and stir for 15 minutes until the solution is clear and transparent to obtain the first mixed solution;

[0041] (2) After adding 2 parts of triethanolamine, 2 parts of monoethanolamine and 4 parts of tall oil into the first mixed solution, heat the reactor to 75°C and stir for 25 minutes until the solution is clear and transparent, then stop heating to obtain the second mixed solution;

[0042](3) ...

Embodiment 2

[0046] A water-based antirust solution for aluminum, consisting of the following components in parts by weight:

[0047] 5 parts of organic polyurethane, 8 parts of isopropanolamine, 5 parts of isononanoic acid, 3 parts of polyester, 2 parts of phosphate ester, 0.1 part of silicone polyether, 76.9 parts of deionized water.

[0048] A kind of preparation method of water-based aluminum antirust solution provided by the invention comprises the following steps:

[0049] (1) Add 38.45 parts of deionized water and 5 parts of organic polyurethane in sequence in the reaction kettle, and stir for 10-15 minutes until the solution is clear and transparent to obtain the first mixed solution;

[0050] (2) After adding 8 parts of isopropanolamine and 5 parts of isononanoic acid into the first mixed solution, heat the reactor to 80°C and stir for 30 minutes until the solution is clear and transparent, then stop heating to obtain the second mixed solution;

[0051] (3) Add 38.45 parts of dei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special water-based antirust liquid for aluminum and a preparation method of the of special water-based antirust liquid. The special water-based antirust liquid for aluminum is composed of the following components in parts by weight: 0.01-5 parts of a dispersing agent, 0.01-10 parts of an alkaline agent, 0.01-5 parts of fatty acid, 0.01-10 parts of a film-forming agent, 0.01-5 parts of an aluminum corrosion inhibitor, 0.01-0.2 part of a defoaming agent and 50-90 parts of deionized water. The special water-based antirust liquid for aluminum provided by the invention not only has excellent alkali corrosion inhibition performance on aluminum materials, but also can ensure that no white hair corrosion phenomenon is generated in the subsequent storage process, does not contain nitrite, chromate, heavy metal and other harmful substances, is safe and environment-friendly, and meets the RoSH 2.0 instruction.

Description

technical field [0001] The invention belongs to the field of antirust technology, and in particular relates to a water-based aluminum special antirust liquid and a preparation method thereof. Background technique [0002] Water-based antirust fluid is widely used in automobile, machining, hardware and other industries, among which, the automobile industry uses the most considerable amount. From the perspective of the automobile industry, water-based anti-rust liquid is used for anti-rust transfer between processes to provide temporary anti-rust protection for auto parts. With the development of "automobile lightweight" in the automotive industry, aluminum materials are gradually replacing ferrous metals. Aluminum auto parts often have problems such as blackening or white spots during production and inter-process storage, which are mainly caused by the corrosion of aluminum. [0003] Two forms of corrosion often occur in aluminum workpieces in the automotive industry during...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/08C09D167/00C09D175/04C09D7/65
CPCC09D5/08C09D175/04C09D7/65C08L67/00C08L71/00C08K5/521
Inventor 郑英斌常羽坤邓亚男周红霍惠李永利李崇
Owner 沈阳防锈包装材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com