C50 high-strength resin concrete and preparation process thereof

A resin concrete, high-strength technology, applied in the field of high-strength concrete, can solve the problems of difficulty in mixing, poor cohesion, poor workability of concrete, etc., and achieve the effects of high mixing ease, improved interface state, and high mechanical properties.

Active Publication Date: 2022-04-22
HUACHUANG ARCHITECTURAL DESIGN CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For the above-mentioned high-strength phenolic resin concrete, the inventor believes that after more phenolic resin is added, the cohesion of each raw material is poor when mixed, and it is not easy to stir. poor workability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • C50 high-strength resin concrete and preparation process thereof
  • C50 high-strength resin concrete and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The C50 high-strength resin concrete in this embodiment is made of the following raw materials: 220kg of cement, 90kg of mineral powder, 70kg of fly ash, 5kg of silica fume, 720kg of sand, 950kg of coarse aggregate, 7kg of admixture, 165kg of water, compound Resin 100kg, curing agent 8kg. The composite resin is composed of liquid phenolic resin and solid phenolic resin in a mass ratio of 15:7.

[0043] Among them, the cement is ordinary Portland cement with the label 50.5. The specific surface area of ​​mineral powder is 400㎡ / kg. Fly ash is a first-class fly ash. The specific surface area of ​​silica fume is 22000㎡ / kg. The admixture is a high-efficiency polycarboxylate water reducer with a water reducing rate of 25%. The fineness modulus of the sand is 2.5. The curing agent is NL curing agent. The liquid phenolic resin is 2127 phenolic resin with a solid content of 50%. The solid phenolic resin is 2123 phenolic resin powder with an average particle size of 100 μm...

Embodiment 2

[0048] The C50 high-strength resin concrete in this embodiment is made of the following raw materials: 250kg of cement, 120kg of mineral powder, 90kg of fly ash, 15kg of silica fume, 780kg of sand, 1000kg of coarse aggregate, 10kg of admixture, 180kg of water, compound Resin 120kg, curing agent 15kg. The composite resin is composed of liquid phenolic resin and solid phenolic resin in a mass ratio of 15:7.

[0049]Among them, the cement is ordinary Portland cement with the label 50.5. The specific surface area of ​​mineral powder is 400㎡ / kg. Fly ash is a first-class fly ash. The specific surface area of ​​silica fume is 22000㎡ / kg. The admixture is a high-efficiency polycarboxylate water reducer with a water reducing rate of 25%. The fineness modulus of the sand is 2.5. The curing agent is NL curing agent. The liquid phenolic resin is 2127 phenolic resin with a solid content of 50%. The solid phenolic resin is 2123 phenolic resin powder with an average particle size of 10...

Embodiment 3

[0054] The C50 high-strength resin concrete in this embodiment is made of the following raw materials: 250kg of cement, 110kg of mineral powder, 80kg of fly ash, 12kg of silica fume, 750kg of sand, 980kg of coarse aggregate, 8kg of admixture, 170kg of water, compound Resin 110kg, curing agent 12kg. The composite resin is composed of liquid phenolic resin and solid phenolic resin in a mass ratio of 15:7.

[0055] Among them, the cement is ordinary Portland cement with the label 50.5. The specific surface area of ​​mineral powder is 400㎡ / kg. Fly ash is a first-class fly ash. The specific surface area of ​​silica fume is 22000㎡ / kg. The admixture is a high-efficiency polycarboxylate water reducer with a water reducing rate of 25%. The fineness modulus of the sand is 2.5. The curing agent is NL curing agent. The liquid phenolic resin is 2127 phenolic resin with a solid content of 50%. The solid phenolic resin is 2123 phenolic resin powder with an average particle size of 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of high-strength concrete, and particularly discloses C50 high-strength resin concrete and a preparation process thereof. The C50 high-strength resin concrete is mainly prepared from the following raw materials in parts by weight: 220 to 250 parts of cement, 90 to 120 parts of mineral powder, 70 to 90 parts of fly ash, 5 to 15 parts of silica fume, 720 to 780 parts of sand, 950 to 1000 parts of coarse aggregate, 7 to 10 parts of an additive, 165 to 180 parts of water, 100 to 120 parts of composite resin and 8 to 15 parts of a curing agent, the composite resin is composed of liquid phenolic resin and solid phenolic resin according to the mass ratio of (15-26): (7-10). The C50 high-strength resin concrete can be used for building, water conservancy and road and bridge engineering, and has the advantages of high strength and easiness in stirring.

Description

technical field [0001] This application relates to the technical field of high-strength concrete, more specifically, it relates to a C50 high-strength resin concrete and its preparation process. Background technique [0002] Concrete is widely used in housing construction, hydraulic engineering, road construction, bridge construction and other projects. Concrete can be divided into cement concrete, gypsum concrete, water glass concrete, Portland concrete, asphalt concrete, polymer concrete and so on according to the variety of cementitious materials. Among them, polymer concrete is a granular organic-inorganic composite material. It is a concrete composed of organic polymers (such as resins), inorganic cementitious materials and aggregates, which can improve the strength, cohesive force, and chemical corrosion resistance of concrete. performance. [0003] The Chinese patent whose application notification number is CN104261747A discloses a high-strength phenolic resin concr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2201/50C04B2201/52C04B18/08C04B18/141C04B18/146C04B14/06C04B14/02C04B24/302C04B2103/0068Y02W30/91
Inventor 马瑜琦马海群李二鹤
Owner HUACHUANG ARCHITECTURAL DESIGN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap