Pine smoke Huizhou ink and preparation method thereof

A technology of pine smoke and Hui ink, applied in the field of pine smoke and Hui ink and its preparation, can solve the problems of easy condensation of ink, low adhesion, and behavior difference, and achieve the effect of smooth writing and no decrease in adhesion

Pending Publication Date: 2022-04-26
黄山市歙县徽韵工艺品厂(普通合伙)
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0022] 2. Sol
But the adhesion is low, the ink color is shallow, and the ink block is easy to fade and break; if too much glue is added, it will cause poor writing and the ink is easy to condense
[0067] Nanomaterials have certain uniqueness. When the material scale is small to a certain extent, quantum mechanics must be used instead of traditional mechanics to describe its behavior. When the powder particle size is reduced from 10 microns to 10 nanometers, its particle size Although the change is 1000 times, when converted into volume, it will be 10 to the 9th power, so there will be obvious differences in the behavior of the two

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pine smoke Huizhou ink and preparation method thereof
  • Pine smoke Huizhou ink and preparation method thereof
  • Pine smoke Huizhou ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0159] The preparation of embodiment 1 pine smoke ink (unit: g)

[0160] prescription:

[0161] Raw materials Dosage loose smoke 100g sodium cholate 10g ice flakes 10g bone glue 125g

[0162] .

[0163] It is further prepared into pine smoke ink through the following steps:

[0164] 1) Take the prescribed amount of borneol, crush it, pass through a 1200-mesh sieve, and set aside;

[0165] 2) Mix the clear smoke obtained by washing the prescribed amount of smoke with the prescribed amount of sodium cholate, and add 20 times the volume of purified water according to the total mass;

[0166] 3) Set the pressure of the homogenizer to 80 bar, and circulate 15 times to obtain a suspension of nano-scale pine smoke;

[0167] 4) Vacuum drying to obtain a nanoscale pine smoke mixture;

[0168] 5) Take an appropriate amount of purified water, heat to 50°C, add bone glue, and stir slowly until a viscous glue is formed;

[0169] 6) Take the nan...

Embodiment 2

[0172] The preparation of embodiment 2 pine smoke ink (unit: g)

[0173] prescription:

[0174] Raw materials Dosage loose smoke 100g sodium cholate 10g ice flakes 10g Kraft glue 125g

[0175] .

[0176] It is further prepared into pine smoke ink through the following steps:

[0177] 1) Take the prescribed amount of borneol, crush it, pass through a 1200-mesh sieve, and set aside;

[0178] 2) Mix the clear smoke obtained by washing the prescribed amount of smoke with the prescribed amount of sodium cholate, and add 20 times the volume of purified water according to the total mass;

[0179] 3) Set the pressure of the homogenizer to 80 bar, and circulate 15 times to obtain a suspension of nano-scale pine smoke;

[0180] 4) Vacuum drying to obtain a nanoscale pine smoke mixture;

[0181] 5) Take an appropriate amount of purified water, heat it to 50°C, add kraft glue, and stir slowly until a viscous glue is formed;

[0182] 6) Take th...

Embodiment 3 Embodiment 1 and 2

[0185] Example 3 Example 1 and 2 Detection of Songyan Hui ink properties

[0186] By the method described in test 5-7, detect the degree of ink development, viscosity and diffusivity of the Songyan Hui ink obtained in Examples 1 and 2, and detect other Important parameters, the results are shown in the table below.

[0187]

[0188] .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to pine soot Huizhou ink and a preparation method thereof. According to the preparation method, a nano preparation process is introduced into the preparation of the Huizhou ink for the first time, sodium cholate in a specific proportion is added into the pine smoke, a nano-scale pine smoke mixture is prepared by a high-pressure homogenization process, and the pine smoke Huizhou ink is further prepared. The pine smoke Huizhou ink prepared by the technology can neglect the influence of the proportion of added glue to a certain extent. Even if a large proportion of glue is added, the writing is also smooth, and the adhesive force is not reduced under the condition that a low proportion of glue is added. The process is suitable for industrial production.

Description

technical field [0001] The invention belongs to the technical field of Hui ink, and in particular relates to a pine smoke Hui ink and a preparation method thereof. Background technique [0002] The invention of ink is a major contribution made by our ancestors to Chinese culture and even world civilization. Hui ink has distinctive features, unique techniques, a wide variety of genres, and rich scientific and technological connotations, occupying an important position in the history of Chinese ink making. The Hui ink products made with traditional techniques have many advantages. Some are "hard as jade, and their lines are like rhinoceros. It doesn't take a penny to write dozens of pieces." But the fragrance never fades", and some "light can be learned, sharpness can be cut, and the virtue is better than jade, and it is meticulous. The carving work and the ingenuity of the style are all beautiful." [0003] Judging from the existing historical data, the production of Hui in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/16C09D11/17
CPCC09D11/16C09D11/17
Inventor 项颂项德胜
Owner 黄山市歙县徽韵工艺品厂(普通合伙)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com