Laminating film and decorating molding body used thereof
A technology for laminating films and coating layers, applied in the fields of crafts for producing decorative surface effects, decorative art, and devices for coating liquids on surfaces, etc., which can solve the problem of difficult appearance design and difficult processability at the same time and appearance design, reduce processability and other issues, achieve excellent appearance design, reduce the difficulty of process management, and reduce the effect of coating site
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
manufacture example
[0155]
[0156] Add acrylic resin (B1), urethane oligomer (B2), and polyfunctional monomer (B3) to a container equipped with a stirrer, and add polymerization initiator (B4), ultraviolet absorber (UVA), Light stabilizer (HALS), and finally add the solvent according to the weight ratio of toluene / ethyl acetate / isopropanol=80 / 5 / 15. Stir for 30 minutes to obtain a clear coating solution.
[0157]
[0158] Acrylic resin (C1) and polyurethane resin (C2) are added to a container equipped with a mixer, and flake aluminum powder and surface conditioner are added while stirring. Finally, toluene solvent is added and stirred for 30 minutes to obtain a colored coating solution. In addition, to obtain a metallic luster laminate film, in addition to the above-mentioned flaky aluminum powder, an orientation control material (C4) is added at the same time.
[0159]
[0160] Use a coater to coat the clear coating on the protective film. After drying, the clear coating layer (B) has a thickness...
Embodiment 1-3
[0216] [Example 1-3; Metallic style laminated film]
[0217] Using [a] the protective film layer (A), [b] the clear coating solution, and [c] the coloring coating solution shown in Table 1, a laminated film was produced according to the above procedure, and at the same time, a decorative molded body was produced using the laminated film, Perform each of the above evaluations. The results are shown in Table 3. In addition, the IV value, SV value, and FF value of the coating film used for evaluation containing the flaky aluminum powder contained in the colored coating solution are shown in Table 19.
[0218] In Table 3 and the following Tables 5, 8, and 11, for IV values exceeding 400 and FF values exceeding 2.0 that cannot be measured with the above-mentioned ALCOPE (アルコ-プ) LMR-200 meter, "<" Indicates that the measuring range of the meter is exceeded.
[0219] In addition, in this example and the examples and comparative examples shown below, detailed descriptions of the mater...
Embodiment 4、5
[0222] [Examples 4 and 5; metal-style laminated film]
[0223] Using [a] the protective film layer (A), [b] the clear coating solution, and [c] the coloring coating solution shown in Table 4, a laminated film was produced according to the above procedure, and at the same time, a decorative molded body was produced using the laminated film, Perform each of the above evaluations. The results are shown in Table 5. In addition, the IV value, SV value, and FF value of the coating film used for evaluation containing the flaky aluminum powder contained in the colored coating solution are shown in Table 19.
PUM
| Property | Measurement | Unit |
|---|---|---|