Ultra-pressure sintered dense solid knife from polycrystalline integrated cubic boron nitride and production thereof

A cubic boron nitride and ultra-high pressure technology, which is applied in the field of improved material cutting tools and its manufacturing, can solve the problems of shortened service life, coating film damage, coating film peeling, etc., to prevent cracks and overcome easy wear , good bonding performance

Inactive Publication Date: 2006-05-31
刘书锋
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, disclosed ZL01142529 and ZL01142530; However, this coating film is often peeled off, and the coating film is also often damaged, resulting in shortened service life during work

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-pressure sintered dense solid knife from polycrystalline integrated cubic boron nitride and production thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Material formula 1: 75% by weight of polycrystalline cubic boron nitride fine powder, 15% by weight of cobalt aluminum alloy fine powder, and 10% by weight of ceramic fine powder additive.

[0023] Material formula 2: 85% by weight of polycrystalline cubic boron nitride fine powder, 10% by weight of cobalt aluminum alloy fine powder, and 5% by weight of ceramic fine powder additive.

[0024] Material formula 3: 80% by weight of polycrystalline cubic boron nitride fine powder, 12% by weight of cobalt aluminum alloy fine powder, and 8% by weight of ceramic fine powder additive.

[0025] The above micropowder:

[0026] (1) In the cobalt aluminum alloy micropowder, cobalt accounts for 2% by weight, and aluminum accounts for 98% by weight; TiC accounts for 3% by weight in the ceramic micropowder additive, AlO accounts for 10% by weight, TiN accounts for 30% by weight, and AlB accounts for 57% by weight.

[0027] (2) In the cobalt aluminum alloy micropowder, cobalt accounts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A ultrahigh sintered dense cutter with integrated polycrystalline cubic boron nitride and its production are disclosed. The material consists of polycrystalline cubic boron nitride 75í½85wt%, ó¾ó§ and ó¾A family metal alloy 10í½15wt% and ceramic additive 5í½10wt%. The process is carried out by placing the cutter raw materials into mould, placing the mould into super-high pressure synthetic colloid, forming into super-high pressure assemble block, pressurizing the cutter materials to 6í½8.5Gpa, and heating to 1300í½1800íÒC for 60í½90 seconds. It has high cutting parameter and excellent cutting effect.

Description

technical field [0001] The invention relates to a cutting tool of improved material and a manufacturing method thereof, which adopts a compact cutting tool which contains polycrystalline cubic boron nitride such as cubic boron nitride, metal alloy powder and ceramic additives as raw materials and is sintered under ultra-high pressure. Background technique [0002] Cubic boron nitride has a hardness and thermal conductivity close to that of diamond and has excellent performance with lower reaction ability with ferrous metals than diamond. Therefore, from the perspective of improving work efficiency and reducing installation costs, people process difficult-to-cut ferrous metal , Use this tool instead of abrasive or processing tools and cemented carbide or cermet tools. [0003] Cubic boron nitride sintered compacts used to prepare cutting tools are sintered compacts containing cubic boron nitride particles and binders, which can generally be powdered into the following two typ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/5831C04B35/645
Inventor 刘书锋
Owner 刘书锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com