Cotton and hemp composite cellulose pulp and method for producing same

A technology of composite cellulose and manufacturing method, applied in the direction of cellulose/protein conjugated artificial filament, spinning solution preparation, etc., which can solve the problems of new pulp production, cellulose content, whiteness, and viscosity that cannot be adapted to composite cellulose , ash, iron content and filterability cannot meet the technical requirements of composite viscose fiber pulp, etc., to achieve natural excellent coloring, shorten processing time, and good filter performance

Inactive Publication Date: 2007-12-19
YIBIN GRACE
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process is only suitable for the preparation of a single viscose fiber pulp from a single raw material, and cannot adapt to the production of new composite cellulose pulp. Meet the technical requirements of composite viscose pulp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The novel composite cellulose pulp of the present invention is made of cotton linter and hemp composite, and its weight percentage is: 1%: 99%.

[0039] The novel composite cellulose pulp of the present invention is composed of cotton fiber and hemp fiber, and the weight percentage of each component in its finished product is:

[0040] Cotton Fiber 1%

[0041] Hemp 99%

Embodiment 2

[0043] The novel composite cellulose pulp of the present invention is made of cotton linter and hemp composite, and its weight percentage is: 99%: 1%.

[0044] The novel composite cellulose pulp of the present invention is composed of cotton fiber and hemp fiber, and the weight percentage of each component in its finished product is:

[0045] Cotton 99%

[0046] Hemp fiber 1%

Embodiment 3

[0048]Composite cellulose novel pulp is characterized in that: it is made by combining cotton and hemp according to the following weight ratio, cotton: hemp=50%:50%

[0049] The novel composite cellulose pulp of the present invention is composed of cotton fiber and hemp fiber, and the weight percentage of each component in its finished product is:

[0050] Cotton 50%

[0051] Hemp 50%

[0052] Technical index described in the present invention is:

[0053] Ash≤0.19%

[0054] Moisture 10.0±0.5%

[0055] Iron content≤28ppm

[0056] Fat waxy≤0.25%

[0057] Chlorine-containing substances≤0.25%

[0058] Pectin pentosan≤0.25%

[0059] Lignin≤1.6%

[0060] A cellulose ≥ 92%

[0061] Viscosity≥8.0mpa.s

[0062] Whiteness≥63%

[0063] Fixed volume weight 700~900g / m 3

[0064] Alkaline absorption value 300-770%

[0065] Swelling degree 100-300%

[0066] The manufacturing method comprises the following steps: seasoning, washing, washing, beating and thawing, mixing, impuri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a new composite fiber pulp and making method, which adopts the following random two or more combination as raw material: cotton velvet, hemp, wood, bamboo. The preparing method comprises the following steps: adjusting material; washing material; washing; beating; fluffing; blending; removing impurities; washing; preparing acid; preparing chlorine; bleaching; proceeding acid disposal; removing impurities; washing; filtering. The invention integrates the superiority of cotton and bamboo fiber material, which satisfies different needs of pulp.

Description

technical field [0001] The invention relates to a novel composite cellulose pulp used in the textile field and produced by using natural cotton and hemp raw materials and a manufacturing method thereof. Background technique [0002] With the continuous improvement of living standards, people's requirements for clothing have shifted from meeting the needs of warm and beautiful clothing to the pursuit of comfort, environmental protection and health. All are to adopt single cotton pulp, wood pulp, bamboo pulp, hemp pulp to manufacture viscose fiber at present. [0003] However, the viscose fibers produced from single raw materials such as cotton pulp and hemp pulp have monotonous performance and lack of individuality. The performance is different and has its own characteristics, such as skin affinity, fiber stiffness, antibacterial and antibacterial functions, Fiber softness, deodorization, air permeability, coloring, resilience, moisture absorption and release, etc. Therefore...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01D1/02
Inventor 冯涛
Owner YIBIN GRACE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap