Li-doped p-Zn1-xMgxO crystal film and method for preparing same

A technology of p-zn1-xmgxo and crystal, which is applied in the field of Li-doped p-Zn1-xMgxO crystal film and its preparation, can solve the problem of low repeatability and stability of p-type conductance, deep acceptor energy level, Low solid solubility and other problems, to achieve the effect of shallow acceptor energy level, high solid solubility, good stability and repeatability

Inactive Publication Date: 2008-07-30
ZHEJIANG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still some problems in the doping of group V elements: such as low solid solubility of acceptors, deep acceptor energy levels, and low repeatability and stability of p-type conductance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Li-doped p-Zn1-xMgxO crystal film and method for preparing same
  • Li-doped p-Zn1-xMgxO crystal film and method for preparing same
  • Li-doped p-Zn1-xMgxO crystal film and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Combine the following figure 1 , The present invention will be further illustrated through examples. Growing p-Zn on glass substrate 1-x Mg x O crystal film, the specific steps are as follows:

[0018] 1) Sintering of ceramic targets, weighing high-purity ZnO, MgO and Li with a purity of >99.99% 2 CO 3 Powder so that the molar ratio of MgO to ZnO is 1:9, Li 2 CO 3 The molar content of is 0.4%. Put the weighed ZnO, MgO and Li 2 CO 3 The powder is mixed and poured into a ball mill tank equipped with agate balls, and ball milled on a ball mill for 20 hours. The purpose is to mix the raw materials uniformly and refine them to a certain extent, so as to facilitate the molding and sintering of the ceramic target. Then the raw materials are separated and dried, and pre-sintered at 800 ℃ to make Li 2 CO 3 Decomposed into Li 2 O and CO 2 , And CO 2 discharge. The pre-fired powder is ball-milled again, dried, then added with a binder for grinding, and pressed into shape. Put the for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a Li doping p-Zn1-xMgxO transistor film, which is characterized by the following: molar content x of MgO is between 0 and 20 percent and y molar content of Li is between 0 and 2 percent; the carrier density of Li doping p-Zn1-xMgxO transistor film is 1015-1019cm-3; the film adopts pulse laser sedimenting method; the target material is ceramic target sintered by high-pure ZnO, MgO and Li2CO3 powder, wherein the MgO molar content x is between 0 and 20 percent; the Li2CO3 molar content y is between 0 and 1 percent, whose pressure is 0.1-50 Pa with growing temperature at 400-700 deg.c under high-oxygen environment; the doping density can be adjusted through controlling Li content in the target material.

Description

Technical field [0001] The present invention relates to Li-doped p-Zn 1-x Mg x O crystal film and its preparation method. Background technique [0002] Hexagonal Zn produced by adding proper amount of MgO to ZnO 1-x Mg x O crystal film has the same crystal structure as ZnO and similar lattice constant, but its band gap is larger than that of ZnO, and the band can be tailored according to the molar content of Mg. Therefore, Zn 1-x Mg x O film is the best barrier layer material for ZnO. In order to improve the light-emitting performance of optoelectronic devices, devices generally adopt p-n junctions, heterojunctions, superlattices and quantum well structures. If stable growth and controllable p-type Zn can be achieved 1-x Mg x O crystal film, not only can be greatly improved with p-Zn 1-x Mg x The luminous efficiency of ZnO-based light-emitting diodes with O / n-ZnO heterogeneous p-n junction as the basic structure opens up the possibility of application of ZnO-based laser diodes. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B23/00H01L33/00
Inventor 叶志镇张银珠黄海辉曾昱嘉
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com