Method of replacing lime with limestone for slagging and producing steel in oxygen top blown converter

A technology of oxygen top blowing and converter steelmaking, applied in the manufacture of converters, etc., can solve problems such as physical heat waste, achieve the effects of reducing storage costs, reducing usage, improving heat utilization and production efficiency

Inactive Publication Date: 2011-01-19
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen that, compared with reheating and raising the temperature in the oxygen top-blown converter, a large amount of physical heat that the calcined lime has is wasted in vain.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1, test is carried out in 25 tons of oxygen top-blown converters. After adding 25 tons of molten iron, blow the gun with oxygen for 0.5 minutes and then start adding limestone and fluorite in batches. Limestone is added in batches of 1.2 tons every 1 minute for a total of 6 times, and fluorite is added every 2 minutes. for 3 joins. About 3 minutes after all the slagging agent is added, the carbon flame is lit up and enters the decarburization period. After blowing oxygen for 12 minutes, the furnace was inverted to take samples and measure the temperature. The composition was qualified and the temperature was 1670°C, and then the steel was tapped.

Embodiment 2

[0020] Embodiment 2, test is carried out in 25 tons of oxygen top-blown converters. First add 600 kg of lime, and then add 2 tons of scrap steel. Then add 23 tons of molten iron, blow the gun with oxygen for 2 minutes to raise the temperature, and then start to add limestone and fluorite in batches. There are 1.45 tons of limestone in each batch of slagging agent, and add once every 1.5 minutes, a total of 4 times. About 2 minutes after all the slagging agent is added, the carbon flame is lit up and enters the decarburization period. Oxygen blowing for 11 minutes, the furnace was reversed to take samples and measure the temperature. The composition was qualified, and the temperature was 1660°C, and then the steel was tapped, which showed that adding limestone to make slag did not affect the normal smelting.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to the field of steel production, and relates to a method of replacing lime with limestone for slagging and producing steel in an oxygen top blown converter. The invention is characterized in that the limestone is directly added during slagging in the steel production process. The added batch number is increased and the amount of each batch of material is reduced. Namely the lime is added by 1-3 times for slagging formerly, and when the limestone is added for slagging, the limestone is added by 4-8 times. The adding amount of each time, calculated according to the CaO therein, is 1 / 2-1 / 3 of lime added formerly and is for preventing the condensing and incrusting at the metal surface in the furnace in the early period of converting. The adding amount of limestone, calculated according to CaO therein, accounts for 30%-100% of adding amount of lime in the batch. The method of the invention has the main advantages of elimination of lime calcining procedure or reduction of production scale, reduction of cost required for operating the calcining device and reducing the discharged pollution, prevention of heat waste caused by cooling the lime after calcining,low sulfur content in the lime generated in the oxygen top blown converter, and benefit for restraining resulfurization of melted iron in the steel production process.

Description

technical field [0001] The invention belongs to the field of converter steelmaking and relates to a method for making slagging steel with limestone instead of lime in an oxygen top-blown converter. Background technique [0002] Oxygen top-blown converter steelmaking is a process of forced oxygen supply, rapid oxidation to remove impurity elements in molten iron, and heating molten steel to increase temperature by element oxidation heat. Lime slag needs to be added in the furnace to remove impurity element phosphorus in molten iron. [0003] Lime is a product obtained by calcination of limestone. In production, the limestone is generally heated to above 1200°C. The calcination process is carried out for several hours, during which the limestone (calcium carbonate) decomposes and releases CO 2 And become lime (calcium oxide). Lime carries a large amount of physical heat after it is fired, and it must be cooled to a temperature suitable for transportation before it can be tran...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/36
Inventor 李宏曲英
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com