Pearlized silver toner and method for preparing PMMA/ABS alloy by using same
A silver-white, pearlescent technology, applied in the direction of pigment paste, etc., can solve the problem of needing painting on the surface of PMMA/ABS alloy, and achieve the effect of saving energy
Active Publication Date: 2012-05-30
SHENZHEN WOTE ADVANCED MATERIALS
View PDF1 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] The object of the present invention is to provide a kind of pearl luster silver-white toner, aims at solving the problem that the PMMA / ABS alloy surface of prior art needs to spray paint when coloring
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] When preparing pearlescent silver-white toner, the ratio of each component is as follows: titanium dioxide: 1%; ultramarine blue: 0.1%; flashing pearl: 43%; illusion pearl green: 5%; 5%; pearl silver: 40%; diffuser: 5.9%.
Embodiment 2
[0023] When preparing pearlescent silver-white toner, the ratio of each component is as follows: titanium dioxide: 2%; ultramarine blue: 0.2%; flashing pearl: 38%; magic pearl green: 7.5%; magic pearl blue 7.5%; Pearl Silver: 40%; Diffuser: 4.8%.
Embodiment 3
[0025] When preparing pearlescent silver-white toner, the ratio of each component is as follows: titanium dioxide: 4%; ultramarine blue: 0.4%; flashing pearl: 30%; magic pearl green: 16%; magic pearl blue 16%; Pearl Silver: 30%; Diffuser: 3.6%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| melt flow index | aaaaa | aaaaa |
Login to View More
Abstract
The invention is suitable for the technical field of thermoplastic resin alloys by high polymer material technology, and provides a pearlized silver toner and a method for preparing a PMMA / ABS alloy by using the same. The pearlized silver toner contains the following components in percentage by weight: 1 to 8 percent of titanium dioxide, 0.1 to 1 percent of ultramarine, 20 to 45 percent of glitter pearl, 5 to 25 percent of multicolor pearlescent green, 5 to 25 percent of multicolor pearlescent blue, 20 to 45 percent of silver pearl, and 1 to 6 percent of dispersing agent. In the invention, firstly, the pearlized silver toner is prepared, and secondly, the pearlized silver PMMA / ABS alloy is prepared by using the prepared pearlized silver toner; the surface of the alloy is free from paint spraying and coloring; and the alloy is formed only at a time, and has the advantages of energy conservation, never fading, environmental protection and the like.
Description
technical field [0001] The invention belongs to the technical field of thermoplastic resin alloys in polymer material technology, and in particular relates to a pearlescent silver-white toner and a method for preparing PMMA / ABS alloy by using the same. Background technique [0002] The development trend of the home appliance industry in recent years is multi-functional, high-grade, intelligent, energy-saving and pollution-free. The application of plastics in home appliances is also increasing day by day, and has become the fastest growing material in the field of home appliances. Home appliance manufacturers are increasingly aware that reducing raw material costs and creating new value are effective ways to ensure the competitiveness of home appliance companies. Generally speaking, the plastic casing of existing home appliances needs to be sprayed and colored, which can not only protect the surface of the parts, improve the weather resistance of the plastic substrate, but a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09D17/00C08L33/12C08L55/02C08J3/20C08K13/02C08K3/22
Inventor 谢迎洪汪平武韦联生何征
Owner SHENZHEN WOTE ADVANCED MATERIALS